The use of hollow sphere pigments as strength additives in paper and paperboard coatings—Part 2: Optimization in paperboard formulations for opacity and strength, TAPPI Journal November 2020
ABSTRACT: This report aims to summarize the efforts in testing the properties of coatings for paperboard utilizing hollow sphere pigments (HSPs). HSPs are known to effectively scatter light and replace titanium dioxide (TiO2) in architectural coating formulations. The effect of the particle size and void fraction was evaluated, along with many coating parameters, including level of addition, binder chemistry, and blends of two HSPs. The small HSPs that have optimized voids for scattering light showed equivalent strength to the TiO2-containing control. The strength data was surprising, particularly the improvement in strength for coatings containing large particle size HSPs. Because of this increase in strength, four parts of binder could be removed, which allowed for higher brightness while not compromising other properties, including hot melt glueability. These trends held true using different binder chemistries (styrene acrylic, vinyl acrylic, and styrene butadiene). Upon refining the formulations further, blends of two HSPs showed further benefit.
Journal articles
Estimating dose and interaction of X-rays with cellulose-based fibrous materials using micro-computed tomography, TAPPI Journal March 2026
ABSTRACT: Micro-computed tomography (ìCT) has a reputation as a nondestructive analysis method. Unfortunately, this leads to the common misconception that radiation damage of the sample does not play a role. With the increased use of ìCT in laboratory-based machines, more and more cellulose-based materials are studied. In this paper, we show with three examples that radiation damage is important in dry and wet paper and in viscose fibers. In an attempt to quantify radiation damage, we came up with a workflow that enables researchers to predict the X-ray dose within a laboratory-based ìCT machine. This gives researchers the possibility to quantitatively judge the influence of radiation damage on each measured sample. While one cannot extend the measured doses from one machine to another, one can still apply the work flow presented in this study to any ìCT setup. In this way, it is possible to minimize radiation damage by choosing the best parameters in a ìCT for obtaining perfect data with no or little radiation damage.
Journal articles
Magazine articles
New opportunities in the paper and nonwovens industries with foam-assisted web forming and chemical application, TAPPI Journal January 2023
ABSTRACT: Foam-assisted web forming and chemical application technologies have great potential to improve manufacturing efficiency and product quality in the paper and nonwovens industries. In this study, the benefits of foam forming and foam-assisted application of chemicals were demonstrated in a pilot machine trial. Uniform high-bulk webs of unrefined bleached softwood kraft pulp (BSKP) and viscose fibers were manufactured by foam forming. It was shown that foam formed low-grammage and high-bulk viscose fiber webs can be strengthened by foam-assisted application of latex onto the wet web. Correspondingly, foam-assisted application of carboxymethyl cellulose (CMC) and anionic polyacrylamide (A-PAM) improved the strength of the foam formed low-grammage and high-bulk BSKP web. Overall, the pilot machine results indicated that material cost savings could be achieved and a high-performance product could be manufactured with foam-based technologies.
Journal articles
Magazine articles
Water chemistry challenges in pulping and papermaking • fundamentals and practical insights: Part 2: Conductivity, charge, and hardness, TAPPI Journal June 2023
ABSTRACT: Although water is essential to the papermaking process, papermakers often overlook its importance and focus on fibers, fillers, and chemical additives. A better understanding of water properties and chemical interactions associated with water at the wet end leads to a sound foundation for high-quality paper production and smooth operation. Water is an excellent solvent for ionic substances, both organic and inorganic. These substances contribute to system conductivity, charge, and hardness and significantly impact the papermaking process. Part 1 of this paper, published in TAPPI J. 21(6): 313(2022), discussed fundamental water properties, water chemistry, and the impact of pH on pulping and papermaking operations. In this paper, we review definitions, sources, and the typical symptoms of the effect of conductivity, charge, and hardness on the productivity of the papermaking process. Sources of conductivity, charge, and hardness impacting these factors, measurement methods, and available correction strategies for their control are also discussed.
Journal articles
Water and grease resistance of paperboard coated with long chain cellulose fatty acid esters using electrostatic powder coating, TAPPI Journal April 2026
ABSTRACT: Fiber-based materials used for foodservice, takeaway, and other packaging applications must typically provide water and grease resistance. Simultaneously, there is growing interest towards bio-based and renewable barrier coatings. In this study we applied thermoplastic long chain fatty acid cellulose esters onto paperboard using electrostatic powder coating to create barrier properties of interest. Electrostatic powder coating provides a water-free process to tackle moisture-induced quality issues and to provide an even coating layer. Cellulose octanoate and palmitate esters were produced in pilot scale. These were ground into fine particles using liquid nitrogen and applied onto paperboard sheets using an electrostatic powder gun. The loosely packed coatings were fixed and fused onto the paperboard by hot pressing. We characterized the coated sheets for coating thickness, contact angles with water, water absorption, grease resistance (KIT), and olive oil barrier. Two commercial polyethylene powders were used as references. Our results indicated that the long chain cellulose fatty acid ester coatings were thermoplastic and hydrophobic with contact angles above 100°. Water absorption was similar to the reference coatings. While grease resistance was lower than with the references, the cellulose ester coatings slowed down diffusion of olive oil through the paperboard. Cellulose octanoate ester with a lower melt viscosity already provided smooth coatings after the initial hot pressing step, while in most cases, the second post hot pressing step further improved the barrier properties.
Journal articles
Pilot-made, highly extensible paper for dry 3D forming, TAPPI Journal May 2025
Cellulose fiber-based packaging materials must perform well in demanding three dimensional (3D) forming process conditions. On the other hand, the development of manufacturing concepts is required for improved competitiveness of bio-based materials. This study covers some key factors that influence the extensibility of cellulose fiber-based structures and presents a pilot-scale development study of a 3D formable material concept. Bleached softwood kraft (BSK) pulp from a Nordic pulp mill was used in the pilot trials. Cellulose-based webs were formed using water-laid and foam-laid web forming using a pilot paper machine. For the water-laid forming, the BSK pulp was refined by applying a high consistency (HC) phase at over 40% consistency, followed by a low consistency (LC) refining at 4% consistency. The BSK pulp was refined for the foam-laid forming by only applying lowconsistency refining. In the foam-laid web forming, anionic sodium dodecyl sulfate (SDS), two foamable latexes, and polyvinyl alcohol (PVA) were used as foaming agents. The pilot rolls were dried at a separate steam cylinder dryer pilot and compacted in-plane in the machine direction (MD) at a separate pilot machine. Tensile properties of the treated paper webs were measured and evaluated with respect to achieved web shrinkage. The same dimensional contraction brought by shrinkage was almost strained out in tensile testing. The results indicated that the shrinkage that occurred by drying and in-plane compaction depended on the pulp furnish. The water-laid material achieved about 30% elongation, whereas the foam-laid material achieved significantly above 50% elongation. The 3D forming performance of the dry materials was tested using fixed and sliding blank methods. The dry paper sheets performed well enough in 3D forming for application to many consumer package applications according to their extensibility.
Journal articles
Magazine articles
Study on the effect of aluminum diethyl phosphinate in synergy with ammonium polyphosphate on the flame retardancy of cellulose paper, TAPPI Journal April 2025
ABSTRACT: This paper involved the synergistic incorporation of ammonium polyphosphate (APP) and diethyl aluminum phosphinate (AlPi) as flame-retardant fillers for producing flame-retardant paper. The research revealed that APPs were square particles with a smooth surface, and their solubility was 0.29 g/100 mL at 20°C, which increased to 4.12 g/100 mL at 60°C. The surfaces of AlPis were rough and irregular. The solubility of AlPi was 0.023 g/100 mL at 20°C, and the solubility remained stable when the temperature increased. The addition of AlPi had a minor influence on the pulp beating degree. The tensile strength of kraft/APP/AlPi decreased with the increase of the AlPi addition. For a paper with 20 wt% APP and 0 wt% AlPi, the limiting oxygen index (LOI) value was 27.2%, and it burned completely at the eighth second during vertical combustion. When the AlPi additive content increased to 20 wt%, its LOI value increased to 32.2%, and the vertical combustion self-extinguished as soon as the flame was removed. Scanning electron microscopy (SEM) showed that the char residue of the kraft/APP/AlPi had a more complete fiber network structure than that of kraft/APP. The Raman spectroscopy indicated that the area ratio of the D (amorphous phase; disordered graphite vibration) band to the G (crystal phase; graphite carbon vibration) band (ID/ IG) ratio of kraft/APP/AlPi was lower than that of kraft/APP, meaning that the graphitization degree of the char residue of kraft/APP/AlPi was higher than that of kraft/APP, which indicated the kraft/APP/AlPi had better flame retardancy.
Journal articles
Magazine articles
Determining operating variables that impact internal fiber bonding using Wedge statistical analysis
ABSTRACT: In this study, Wedge statistical analysis tools were used to collect, collate, clean up, plot, and analyze several years of operational data from a commercial paper machine. The z-direction tensile (ZDT) and Scott Bond tests were chosen as representative of fiber bond strength. After analyzing thousands of operational parameters, the ones with the most significant impact upon ZDT involved starch application method, starch penetration, and the amount of starch applied. Scott bond was found to be significantly impacted by formation and refining. Final calendering of the paper web has also shown an impact on internal fiber bonding.
Journal articles
Magazine articles
Lignin-based resins for kraft paper applications, TAPPI Journal November 2019
ABSTRACT: We investigated miscanthus (MS) and willow (W) lignin-furfural based resins as potential reinforce-ment agents on softwood and hardwood kraft paper. These resins might be sustainable alternatives to the commercial phenolformaldehyde (PF) resins. Phenol is a petrochemical product and formaldehyde has been classified as a carcinogen by the U.S. Environmental Protection Agency. The lignin used in this study was derived from hot water extraction (160ºC, 2 h) of MS and W biomass, and may be considered sulfur-free. These biorefinery lignins were characterized for their chemical composition and inherent properties via wet chemistry and instrumental techniques. The resin blends (MS-resin and W-resin) were characterized for their molecular weight, thermal behavior, and mechanical properties. Mechanical properties were measured by the resin’s ability to reinforce softwood and hard-wood kraft papers. The effect of adding hexamethylenetetramine (HMTA), a curing agent, to the resin was also examined. Mixtures of PF and lignin-based resins were investigated to further explore ways to reduce use of non-renewables, phenol, and carcinogenic formaldehyde. The results show that lignin-based resins have the potential to replace PF resins in kraft paper applications. For softwood paper, the highest strength was achieved using W-resin, without HMTA (2.5 times greater than PF with HMTA). For hardwood paper, MS-resin with HMTA gave the highest strength (2.3 times higher than PF with HMTA). The lignin-based resins, without HMTA, also yielded mechanical properties comparable to PF with HMTA.
Journal articles
Magazine articles
Creating adaptive predictions for packaging-critical quality parameters using advanced analytics and machine learning, TAPPI Journal November 2019
ABSTRACT: Packaging manufacturers are challenged to achieve consistent strength targets and maximize pro-duction while reducing costs through smarter fiber utilization, chemical optimization, energy reduction, and more. With innovative instrumentation readily accessible, mills are collecting vast amounts of data that provide them with ever increasing visibility into their processes. Turning this visibility into actionable insight is key to successfully exceeding customer expectations and reducing costs. Predictive analytics supported by machine learning can provide real-time quality measures that remain robust and accurate in the face of changing machine conditions. These adaptive quality “soft sensors” allow for more informed, on-the-fly process changes; fast change detection; and process control optimization without requiring periodic model tuning.The use of predictive modeling in the paper industry has increased in recent years; however, little attention has been given to packaging finished quality. The use of machine learning to maintain prediction relevancy under ever-changing machine conditions is novel. In this paper, we demonstrate the process of establishing real-time, adaptive quality predictions in an industry focused on reel-to-reel quality control, and we discuss the value created through the availability and use of real-time critical quality.