Pre-damping effects on water absorption and drying dynamics in flexographic printing, TAPPI Journal November 2025
ABSTRACT: Optimizing flexographic printability can involve the ink and the substrate, as well as the printing process. It has been widely reported in the literature that controlling topography of the substrate and its porosity are vital for good flexographic printability, especially when using water-based inks. This study focuses on how pre-damping a surface impacts liquid absorption and improves wet trapping (ink on ink with no intermediate drying) in flexographic printing. A Prüfbau universal print tester was adapted to analyze flexographic wet-on-wet ink printing and trapping using yellow and magenta inks for contrast. Slow drying of the first ink layer (yellow) leads to mottle when the second layer (magenta) is applied. The study explores the “wet sponge” hypothesis: a pre-damped surface should absorb liquid faster. The Lucas- Washburn equation describes long-term absorption, but it does not capture short-term uptake, which instead follows a linear dependence on time.
Journal articles
Water and grease resistance of paperboard coated with long chain cellulose fatty acid esters using electrostatic powder coating, TAPPI Journal April 2026
ABSTRACT: Fiber-based materials used for foodservice, takeaway, and other packaging applications must typically provide water and grease resistance. Simultaneously, there is growing interest towards bio-based and renewable barrier coatings. In this study we applied thermoplastic long chain fatty acid cellulose esters onto paperboard using electrostatic powder coating to create barrier properties of interest. Electrostatic powder coating provides a water-free process to tackle moisture-induced quality issues and to provide an even coating layer. Cellulose octanoate and palmitate esters were produced in pilot scale. These were ground into fine particles using liquid nitrogen and applied onto paperboard sheets using an electrostatic powder gun. The loosely packed coatings were fixed and fused onto the paperboard by hot pressing. We characterized the coated sheets for coating thickness, contact angles with water, water absorption, grease resistance (KIT), and olive oil barrier. Two commercial polyethylene powders were used as references. Our results indicated that the long chain cellulose fatty acid ester coatings were thermoplastic and hydrophobic with contact angles above 100°. Water absorption was similar to the reference coatings. While grease resistance was lower than with the references, the cellulose ester coatings slowed down diffusion of olive oil through the paperboard. Cellulose octanoate ester with a lower melt viscosity already provided smooth coatings after the initial hot pressing step, while in most cases, the second post hot pressing step further improved the barrier properties.
Journal articles
Point load measurements on paperboard packages and bulging, TAPPI Journal March 2026
ABSTRACT: Paperboard packaging is made by processing board materials into sheets or rolls and shaping them through creasing, cutting, folding, and erecting. The conversion process generates residual moments at the folds that cause panel bulging. This study experimentally investigates how the bulging introduced during the converting processes influence the mechanical response of paperboard packages during point load testing within the elastic deformation range. The study shows that panel bulging may significantly affect packaging performance as-perceived strength and stiffness. Bulging, influenced by the board’s basis weight, can affect the package performance even more than packaging stiffness. Point load tests in the elastic region were performed on empty packages (78 mm × 50 mm × 110 mm) with force applied at specific points along their long sides. The packages evaluated in this study were made of two identically processed materials of different grammages. The heavier material showed more pronounced bulging than the lighter one, leading to overlapping force-displacement curves for the packages, and to that, a lower force and stiffness may be measured at a certain indentation depth for the package of heavier material. This complicates material choice according to functional requirements. The results show that a highly bulged package might resemble one with less bulging of another material. According to the results, it is not certain that a higher grammage package shows a higher indentation force and stiffness than a lower grammage package when measured at a certain indentation. This indicates that optimizing the creasing and folding processes can be a way to enhance performance rather than simply increasing board weight. The study underscores the importance of controlling converting parameters, especially creasing and folding behavior. Well-performed creasing and folding gives a low residual momentum, little bulging, and a high stiffness and compression strength at point loading in the elastic region. Proper optimization can improve packaging performance and manual handling user-friendliness.
Journal articles
Magazine articles
Control of continuous digester kappa number using generalized model predictive control, TAPPI Journal September 2024
ABSTRACT: Kappa number variability at the digester impacts pulp yield, physical strength properties, and lignin content for downstream delignification processing. Regulation of the digester kappa number is therefore of great importance to the pulp and paper industry. In this work, an industrial application of model-based predictive control (MPC), based on generalized prediction control, was developed for kappa number feedback control and applied to a dual vessel continuous digester located in Western Canada. The problem was complicated by the need to apply heat at multiple locations in the cook. In this study, the problem was reduced from a multiple to a single input system by identifying three potential single variable permutations for temperature adjustment. In the end, a coordinated approach to the heaters was adopted. The process was perturbed and modeled as a simple first order plus dead time model and implemented in generalized predictive control (GPC). The GPC was then configured to be equivalent to Dahlin’s controller, which reduced tuning parameterization to a single closed loop time constant. The controller was then tuned based on robustness towards a worst-case dead time mismatch of 50%. The control held the mean value of the kappa number close to the setpoint, and a 40% reduction in the kappa number’s standard deviation was achieved. Different kappa number trials were run, and the average fiberline yield for each period was evaluated. Trial results suggested yield gains of 0.3%•0.5% were possible for each 1 kappa number target increase.
Journal articles
Magazine articles
Flocculation of fiber suspensions studied by Rheo-OCT, TAPPI Journal September 2024
ABSTRACT: When dealing with papermaking fiber suspensions, particle flocculation takes place even before the paper web is formed. The particle flocculation depends on several aspects, including particle mass concentration (consistency), particle collisions, electrochemical interactions promoted by chemical additives, etc. Due to its importance, fiber suspension flocculation has been studied for a long time in papermaking, and several methods have been developed for this purpose. The traditional techniques include, for example, focused beam reflectance microscopy (FBRM) and high-speed video imaging (HSVI). Recently, a new optical method, optical coherence tomography (OCT), has emerged for flocculation analysis. The advantages of OCT are the possibility to study opaque suspensions, its micron-llevel resolution, and its high data acquisition speed. The OCT measurements can be combined with rheological (Rheo) measurements, allowing simultaneous measurement of both the time evolution of the floc size and the suspension viscosity. In this work, we used this approach, Rheo-OCT, to study the flocculation of suspensions of various papermaking furnishes. We analyzed the time evolution of the floc size and the fiber suspension viscosity when the studied papermaking suspensions were treated with highly refined furnish (HRF) — a furnish that contained a significant amount of micofibrillated cellulose (MFC)-type fibrils — and/or chemical additives. Such studies can lead to a better understanding of the impact of flocculation on the produced paper web in terms of qualities like formation, drainage potential, and strength behavior.
Journal articles
Magazine articles
Study on the effect of aluminum diethyl phosphinate in synergy with ammonium polyphosphate on the flame retardancy of cellulose paper, TAPPI Journal April 2025
ABSTRACT: This paper involved the synergistic incorporation of ammonium polyphosphate (APP) and diethyl aluminum phosphinate (AlPi) as flame-retardant fillers for producing flame-retardant paper. The research revealed that APPs were square particles with a smooth surface, and their solubility was 0.29 g/100 mL at 20°C, which increased to 4.12 g/100 mL at 60°C. The surfaces of AlPis were rough and irregular. The solubility of AlPi was 0.023 g/100 mL at 20°C, and the solubility remained stable when the temperature increased. The addition of AlPi had a minor influence on the pulp beating degree. The tensile strength of kraft/APP/AlPi decreased with the increase of the AlPi addition. For a paper with 20 wt% APP and 0 wt% AlPi, the limiting oxygen index (LOI) value was 27.2%, and it burned completely at the eighth second during vertical combustion. When the AlPi additive content increased to 20 wt%, its LOI value increased to 32.2%, and the vertical combustion self-extinguished as soon as the flame was removed. Scanning electron microscopy (SEM) showed that the char residue of the kraft/APP/AlPi had a more complete fiber network structure than that of kraft/APP. The Raman spectroscopy indicated that the area ratio of the D (amorphous phase; disordered graphite vibration) band to the G (crystal phase; graphite carbon vibration) band (ID/ IG) ratio of kraft/APP/AlPi was lower than that of kraft/APP, meaning that the graphitization degree of the char residue of kraft/APP/AlPi was higher than that of kraft/APP, which indicated the kraft/APP/AlPi had better flame retardancy.
Journal articles
In-situ process monitoring in deep-drawing of paper using partially transparent tools, TAPPI Journal August 2025
ABSTRACT: The production of three-dimensionally formed packaging from paper by deep drawing usually leads to the occurrence of wrinkles, which result from the high tangential compressive stresses in the flange area and the limited flowability of the material. Wrinkles, although mostly tolerated in industry, end in both a reduced visual appearance and a reduction in usability for packaging, as with, for example, when gas-tightness is required. Previous research efforts have been limited to determining the wrinkle distribution after completion of forming and removal of the formed part. Consequently, the possibility of understanding the sequence of formation of individual wrinkles in the inhomogeneous material is lost. To remedy this situation, a method for local in-situ process monitoring is presented. Using a transparent die and an industrial camera, the flange area can be observed during the forming process. An image processing algorithm is applied to analyze the local development of the deep drawing process from the continuously recorded image data. The method described can be used to analyze the draw-in behavior and wrinkle formation locally and continuously over the drawing depth. The blank holder force influences the draw-in and the wrinkle pattern both locally and throughout the drawing process. A more precise understanding of the wrinkle formation will allow for more efficient process control in the future.
Journal articles
Magazine articles
Lignin-based resins for kraft paper applications, TAPPI Journal November 2019
ABSTRACT: We investigated miscanthus (MS) and willow (W) lignin-furfural based resins as potential reinforce-ment agents on softwood and hardwood kraft paper. These resins might be sustainable alternatives to the commercial phenolformaldehyde (PF) resins. Phenol is a petrochemical product and formaldehyde has been classified as a carcinogen by the U.S. Environmental Protection Agency. The lignin used in this study was derived from hot water extraction (160ºC, 2 h) of MS and W biomass, and may be considered sulfur-free. These biorefinery lignins were characterized for their chemical composition and inherent properties via wet chemistry and instrumental techniques. The resin blends (MS-resin and W-resin) were characterized for their molecular weight, thermal behavior, and mechanical properties. Mechanical properties were measured by the resin’s ability to reinforce softwood and hard-wood kraft papers. The effect of adding hexamethylenetetramine (HMTA), a curing agent, to the resin was also examined. Mixtures of PF and lignin-based resins were investigated to further explore ways to reduce use of non-renewables, phenol, and carcinogenic formaldehyde. The results show that lignin-based resins have the potential to replace PF resins in kraft paper applications. For softwood paper, the highest strength was achieved using W-resin, without HMTA (2.5 times greater than PF with HMTA). For hardwood paper, MS-resin with HMTA gave the highest strength (2.3 times higher than PF with HMTA). The lignin-based resins, without HMTA, also yielded mechanical properties comparable to PF with HMTA.
Journal articles
Magazine articles
Viscoelastic web curl due to storage in wound rolls, TAPPI Journal July 2020
ABSTRACT: Winding is often the final operation in a roll-to-roll manufacturing process. Web materials, i.e., materials that are thin compared to their length, are wound into rolls because this form is the only practical means to store them. The resulting bending strains and associated stresses are large for thick webs and laminates. As many webs are viscoelastic on some time scale, bending stresses lead to creep and inhomogeneous changes in length. When the web material is unwound and cut into discrete samples, a residual curvature remains. This curvature, called curl, is the inability for the web to lie flat at no tension. Curl is an undesirable web defect that causes loss of productivity in a subsequent web process. This paper describes the development and implementation of modeling and experimental tools to explore and mitigate curl in homogenous webs. Two theoretical and numerical methods that allow the prediction of curl in a web are developed: a winding software based on bending recovery theory, and the implementation of dynamic simula-tions of winding. One experimental method is developed that directly measures the curl online by taking advantage of the anticlastic bending resulting from the curl. These methods are demonstrated for a low-density polyethylene web.
Journal articles
Magazine articles
Cationic emulsions of maleic anhydride derivatives of oleic and abietic acid for hydrophobic sizing of paper, TAPPI Journal 2020
ABSTRACT: Ordinary rosin sizing agents are mixtures of resin acids that include abietic acid and related compounds obtained from softwoods such as pine. Fatty acids, which are another byproduct of the kraft pulping of soft-wood species, also may have hydrophobic effects, but their use as sizing agents has seldom been considered. In the current study, abietic acid and oleic acid, in the absence of other components, were first modified by reaction with maleic acid anhydride. Then, the maleated derivatives (maleated oleic acid [MOA] and maleated abietic acid [MAA]), which were emulsified with cationic starch at the 1:1 and 3:2 ratio, respectively, were added to fiber furnish containing aluminum sulfate (papermaker’s alum). The prepared sheets were dried with a rotating drum on one side at 100°C at low pressure to cure the sizing agents. The chemical, optical strength, and absorption properties were measured. The presence of the sizing material was confirmed using time of flight secondary ion mass spectrometry (ToF-SIMS), and the retention of the sizing agent on fibers was supported by evidence of hydrocarbons on the paper surface. In addition to achieving sufficient water resistance features with MAA, a lesser hydrophobic character was obtained when using MOA. Compared to commercial applications, relatively large amounts of sizing agent were used to obtain a sufficient sizing degree. The MOA required 5% addition to achieve a similar sizing degree as MAA at the 2% level. The sizing treatments also resulted in substantial increases in tensile index value. Since cationic starch was used in the formulation of the sizing agents, the increase in tensile index may have been due to the influence of cationic starch. Contributions to paper strength from a combination of ionic complexation and mutual association of hydrophobic groups is also proposed. Depending on the amount of sizing agent, the yellowness increased, especially when sizing with MOA.