Tetraethyl orthosilicate-containing dispersion coating — water vapor and liquid water barrier properties, TAPPI Journal September 2021
ABSTRACT: An aqueous styrene-butadiene latex dispersion coating containing in-situ processed tetraethyl orthosilicate (TEOS) applied on paperboard demonstrated improved water barrier performance. Coatings containing TEOS equivalent to 0.8% silicon dioxide (SiO2; dry basis) exhibited water vapor performance of < 25 g/m2/day (23°C, 50% relative humidity [RH]) and liquid water barrier performance Cobb 1800 s of < 6 g/m2, when applied as a single-layer 18 g/m2 coating. Cobb 1800 s barrier performance was still good (< 11 g/m2) at coat weights of 7•10 g/m2. The use of filler materials such as kaolin improved the vapor barrier properties of the coating, but this was not critical to the liquid water barrier properties.
Journal articles
Magazine articles
Commercially relevant water vapor barrier properties of high amylose starch acetates: Fact or fiction?, TAPPI Journal September 2021
ABSTRACT: Starches have recently regained attention as ecofriendly barrier materials due to the increased demand for sustainable packaging. They are easily processable by conventional plastics processing equipment and have been utilized for oil and grease barrier applications. While starches have excellent oxygen barrier properties and decent water barrier properties at low relative humidity (RH), they are moisture sensitive, as demonstrated by the deterioration of the barrier properties at higher RH values. Starch esters are chemically modified starches where the hydroxyl group of the starch has been substituted by other moieties such as acetates. This imparts hydrophobicity to starches and has been claimed as a good way of retaining water vapor barrier properties of starches, even at high RH conditions. We studied the water vapor barrier properties of one class of starch esters, i.e., high amylose starch acetates that were assumed to have good water vapor barrier properties. Our investigations found that with a high degree of substitution of hydroxyl groups, the modified starches did indeed show improvements in water vapor response as compared to pure high amylose starch films; however, the barrier properties were orders of magnitude lower than commercially used water vapor barriers like polyethylene. Even though these materials had improved water vapor barrier response, high amylose starch acetates are likely unsuitable as water vapor barriers by themselves, as implied by previous literature studies and patents.
Magazine articles
Good manufacturing practices in recycled paper and paperboard production for use in food packaging, TAPPI JOURNAL, August 1999, Vol. 82(8)
Good manufacturing practices in recycled paper and paperboard production for use in food packaging, TAPPI JOURNAL, August 1999, Vol. 82(8)
Magazine articles
A guide to developing a best management practices (bmp) plan for spent liquor, part II, TAPPI JOURNAL, December 1999, Vol. 82(12)
A guide to developing a best management practices (bmp) plan for spent liquor, part II, TAPPI JOURNAL, December 1999, Vol. 82(12)
Journal articles
Magazine articles
Pilot scale black liquor concentration using pressure driven membrane separation, TAPPI Journal April 2023
ABSTRACT: Black liquor concentration using pressure driven membrane separation has long been proposed as a means of achieving energy savings and breaking production bottlenecks. To date, limitations in membrane performance and stability under black liquor process conditions have prevented those promises from being realized out-side of tightly controlled laboratory settings. In this work, we describe the first successful pilot scale field deployments of a membrane system for black liquor concentration. Using a purpose-built system and commercial sized, spiral wound graphene oxide membrane elements, we have logged nearly 6000 h of runtime across deployments to multiple mill sites. We demonstrate concentration of black liquor from 14% to >20% total solids, while generating permeate water comparable in quality to that of evaporator condensate and an 81% reduction in energy consumption relative to evaporation. At a commercial scale, these results translate to $2 M/year in net energy savings for a typical mill, as well as an opportunity to support production increases or mill expansions. These results represent a significant leap forward in the ability of membrane systems to deliver substantial value via black liquor concentration.
Journal articles
Magazine articles
Evaluation of soap recovery efficiency from black liquor — analytical tools, TAPPI Journal April 2023
ABSTRACT: Soap skimmings (“soap”) are typically recovered from black liquor in kraft mills that process a high percentage of softwood. In many mills, the recovery of soap is inefficient, negatively impacting performance of evaporators and recovery boilers and resulting in loss of potential revenue. A thorough evaluation of soap recovery performance in a kraft mill requires measurement of soap content in black liquor at various sampling locations, especially around the soap skimmer.The standard laboratory method for evaluating soap content in black liquor is a complex, multi-step process that relies on solvent extraction and titration; most mills send these samples to an outside laboratory for this analysis. In this study, 100 black liquor samples, with a wide range of soap concentrations, were tested by the standard solvent extraction method. After additional dilution, each sample was also tested for surface tension with a bubble pressure tensiometer. The results were found to correlate very closely with the solvent extraction tests results. This alternate method, using surface tension measurements of diluted black liquor samples, produces rapid results and can be easily implemented in most kraft mills, which would facilitate much more frequent in-house evaluations of soap recovery performance.
Journal articles
Magazine articles
Web lateral instability caused by nonuniform paper properties, TAPPI Journal January 2022
ABSTRACT: Lateral or cross-machine direction (CD) web movement in printing or converting can cause problems such as misregistration, wrinkles, breaks, and folder issues. The role of paper properties in this problem was studied by measuring lateral web positions on commercial printing presses and on a pilot-scale roll testing facility (RTF). The findings clearly showed that CD profiles of machine direction (MD) tension were a key factor in web stability. Uneven tension profiles cause the web to move towards the low-tension side. Although extremely nonuniform tension profiles are visible as bagginess, more often, tension profiles must be detected by precision devices such as the RTF. Once detected, the profiles may be analyzed to determine the cause of web offset and weaving problems.Causes of tension profiles can originate from nonuniform paper properties. For example, by means of case studies, we show that an uneven moisture profile entering the dryer section can lead to a nonuniform tension profile and lateral web movement. Time-varying changes in basis weight or stiffness may also lead to oscillations in the web’s lateral position. These problems were corrected by identifying the root cause and making appropriate changes. In addition, we developed a mathematical model of lateral stability that explains the underlying mechanisms and can be used to understand and correct causes of lateral web instability.
Journal articles
Magazine articles
Application of ATR-IR measurements to predict the deinking efficiency of UV-cured inks, TAPPI Journal January 2022
ABSTRACT: In recent years, ultraviolet (UV)-curable ink has been developed and widely used in various printing applications. However, using UV-printed products (UV prints) in recovered paper recycling causes end-product dirt specks and quality issues. A new method was developed that can distinguish UV prints from other prints by means of attenuated total reflectance infrared (ATR-IR) spectroscopy. Application of this method could allow more efficient use of UV prints as raw materials for paper recycling.First, a mill trial was performed using UV prints alone as raw materials in a deinked pulp (DIP) process. Second, test prints were made with four types of UV inks: a conventional UV ink and three different highly-sensitive UV inks. Each print sample had four levels of four-color ink coverage patterns (100%, 75%, 50%, and 25%). Next, deinkability of all prints was evaluated by laboratory experiments. Finally, each print was measured using the ATR-IR method, and the relationship between the IR spectra and deinkability was investigated. Mill trial results showed that UV prints caused more than 20 times as many dirt specks as those printed with conventional oil-based ink. There were variations in recycling performance among UV prints taken from bales used for the mill trial. Lab tests clearly revealed that not all UV-printed products lead to dirt specks. In order to clarify the factors that affected deinkability of UV prints, the print samples were investigated by lab experiments. Key findings from lab experiments include: œ The number of dirt specks larger than 250 µm in diameter increased as the ink coverage increased. œ Higher ink coverage area showed stronger intensity of ATR-IR spectral bands associated with inks. These results indicate that deinkability of UV prints could be predicted by analysis of ATR-IR spectra. œ Finally, the method was applied for assessment of recovered paper from commercial printing presses. It was confirmed that this method made it possible to distinguish easily deinkable UV prints from other UV prints. Based on these findings, we concluded that the ATR-IR method is applicable for inspection of incoming recovered paper.
Journal articles
Magazine articles
Investigation of the Cellulose-Water Relationship by the Pressure Plate Method, TAPPI Journal July 2022
ABSTRACT: The swelling and water retention properties of pulp fibers are of basic importance in papermaking.
Journal articles
Magazine articles
Web instability in the open draw and the impact on paper machine efficiency, TAPPI Journal May 2022
ABSTRACT: Paper is most likely to break in the first open draw on a paper machine where it is unsupported, wettest, and weakest. Tension is applied to peel the web from the roll surface, as well as minimize web flutter in the open draw. The average tension is well below the breaking point and is often set by adjusting the speed difference between the press and the next machine element by visually observing the behavior of the web. However, machine direction variations caused by instabilities in the paper machine can cause tension swings that exceed the strength of the web. Measurement of the web’s release point from press rolls on pilot and commercial paper machines was used to identify the cause of tension instabilities. Variations in the speed of the paper machine drives and the work of adhesion from the press roll surface were identified as key factors. Fluctuations of paper moisture, which affects the elastic modulus and strength of the web, appear to be less important.