Quantification of vegetable oil in recycled paper, TAPPI JOURNAL September 2020
ABSTRACT: Vegetable soybean oil is commonly used in cooking foods that are packaged in takeaway paper-board containers. Vegetable oil is hydrophobic, and in sufficiently high concentration, could interfere with interfiber bonding and result in paper strength loss. In order to quantify the effect of oil on the resulting paperboard strength, it is necessary to quantify the oil content in paper. A lab method was evaluated to determine the soybean oil content in paper. Handsheets were made with pulps previously treated with different proportions of vegetable oil. Pyrolysis gas chromatography-mass spectrometry (pyGCMS) was used to quantify the amount of oil left in the handsheets. The results revealed a strong correlation between the amount of oil applied to the initial pulp and the amount of oil left in the handsheets.In addition, the effect of vegetable oils on paper strength may be affected by the cooking process. Vegetable oil is known to degrade over time in the presence of oxygen, light, and temperature. The vegetable oil was put in an oven to imitate the oil lifecycle during a typical pizza cooking process. The cooked oil was then left at room temperature and not protected from air (oxygen) or from normal daylight. The heated, then cooled, oil was stored over a period of 13 weeks. During this time, samples of the aged oil were tested as part of a time-based degradation study of the cooked and cooled oil.
Journal articles
Magazine articles
Celebrating 100 Issues of Paper360°, Paper360º September/October 2020
Celebrating 100 Issues of Paper360°, Paper360º September/October 2020
Journal articles
Magazine articles
Chemical addition to wet webs using foam application, TAPPI Journal January 2023
ABSTRACT: In papermaking, the conventional way to add chemicals to the web is to dose them into the fiber stock and form the paper afterwards. However, in many cases, adding chemicals directly to the stock is challenging. For example, strength aids tend to increase flocculation in the stock, which limits the addition amounts of those aids. The need for better performance of paper (and paperboard) products has given rise to the need for functionalization of paper. Adding such functional chemicals to the stock is usually rather inefficient. Hence, novel methods are needed to add chemicals to the paper bulk. One such method is dosing chemicals to the wet web via foam application. In this study, we built a laboratory-scale sheetfed dynamic foam application device and utilized it to study addition of starch to wet bleached chemithermomechanical pulp (BCTMP) paper handsheets. The impact of parameters such as vacuum level, the amount of added chemical, and the viscosity of the foaming liquid on the penetration of starch into the wet web was explored. Starch penetration into wet webs was measured via iodine-potassium iodide staining, followed by image analysis. According to our results, controlling the viscosity of the foaming liquid gives the best possibility to control the penetration.
Journal articles
Magazine articles
Z-direction chemical analysis for new application methods, TAPPI Journal January 2023
ABSTRACT: In conventional wet-end chemical addition during paper production, chemical distribution through the z-direction of the sheet is usually not considered an important characteristic. With a nontraditional chemical dosing approach, such as foam-assisted additive addition, the chemistry can appear at different concentrations throughout the sheet, typically in a z-direction gradient. To fully understand the strength properties of the sheet, it is helpful to view or quantify the chemical distribution through the sheet in the z-direction. One qualitative method uses a dye technique along with confocal laser scanning microscopy to generate an image where the relative chemical concentration can be observed. A quantitative method involves compiling nitrogen analyses of layered subsections of the sheet into a composite graph of relative chemical concentration vs. the z-direction of the sheet. Chemical distribution analysis can be paired with traditional z-direction strength tests, such as Scott bond and z-direction tensile, to help one understand and improve the chemical addition process and its effects.
Journal articles
Permeability simulation for filled paper based on three-dimensional structural model developed by X-ray computed tomography scanning, TAPPI Journal March 2026
ABSTRACT: In this study, an in-depth exploration of filled paper was conducted to understand its structural and permeability characteristics. Cotton linter pulp and precipitated calcium carbonate (PCC) filler were utilized to prepare pure fiber paper, and PCC1 and PCC2 filled papers with different filler particle sizes. Then, the pore structure parameters of paper samples were characterized by mercury intrusion porosimetry, and the X-ray computed tomography (X-CT) scanning was carried out. Subsequently, the 3D microstructures were established based on the X-CT slice images, and the filler characteristic parameters and filler 3D distribution were quantitatively analyzed. Finally, permeation simulations in the thickness and horizontal directions were performed. The findings indicate that filling changes the paper porosity, and the pore tortuosity varies with direction. The estimated pore•throat radius distribution shows specific patterns for different papers. The fillers have different distribution characteristics in the paper samples. Moreover, the paper permeability differs with direction, with smallsized filler having a significant impact on fluid penetration in the thickness direction. Overall, this study provides an effective method for investigating internal paper filler and its distribution, which contributes to the understanding of paper structure•performance relationships.
Journal articles
Effects of in-plane straining on the out-of-plane delamination properties of paperboard, TAPPI Journal March 2026
ABSTRACT: Delamination strength is an essential property for the creasing and folding operations of paperboard into boxes. Due to fixation during creasing, the paperboard suffers in-plane straining. In the present study, we aim to increase our understanding of how in-plane straining affects the delamination properties of paperboard. Samples of paperboard were first strained in in-plane tensile loading, both in the machine-direction and in the cross-direction. Afterward, the paperboard is loaded in the out-of-plane (ZD) direction. Three different grades of commercial paperboard from two major manufacturers were tested in a climate-controlled lab. The results showed similar results for all grades of paperboard, with the delamination strength and the out-of-plane stiffness decreasing virtually linearly with pre-straining. With about 5% plastic in-plane straining, the strength was reduced by about 20% and the stiffness decreased by more than 50% for all grades of paperboard. Normalizing the strength and the stiffness with their values without pre-straining reveals virtually the same relation for all grades of paperboard. If proven to be a general result, this will prove valuable in reducing the demand for experiments.
Journal articles
Influence of base sheet properties on barrier coating performance, TAPPI Journal November 2025
ABSTRACT: Paper packaging offers a sustainable alternative to standard plastic-based materials, particularly for food and beverage applications. With reduced fiber treatment options like fluorochemicals, uncoated base stock often provides little-to-no effective barrier against liquid water, oil/grease, or moisture transmission. Despite the lack of natural barrier performance, base sheet properties can significantly influence the efficiency of applied waterbased barrier coatings. In this study, various base stock properties, such as caliper, porosity, roughness, and ash content, are reported to influence the barrier performance of styrene-acrylic and a copolymer of styrene-butadiene/styrene-acrylate based barrier coatings. These findings will help paper and board producers design better, more cost-effective, purposebuilt substrates for barrier applications in the packaging industry.
Journal articles
A laboratory-scale automated vacuum-assisted device for coating of cellulose nanofibrils onto paper, TAPPI Journal November 2025
ABSTRACT: An automated vacuum-assisted coating system was developed to deposit cellulose nanofibril (CNF) layers onto paper substrates, simulating potential industrial geometries while allowing precise control of web speed (10•20 m/min), vacuum time (up to 30 s), and applicator gap (0.5•0.9 mm). Vacuum assistance makes it possible to obtain coat weights over 5 g/m2 in a single pass and increases solids after coating from less than 10% to over 28%• 30%, reducing drying demand by more than 60%. Coat weights were tuned from 6 to over 11 g/m² by varying suspension solids (0.4•0.6 wt%), line speed, and filtration length (20•40 mm), with strong agreement between experimental data and model predictions. Barrier testing showed Kit test values for double folded samples of 9•12 and Gurley air resistances above 4 × 104 s once coat weights exceeded 7 g/m². Comparable performance was achieved with lower fines content CNF (60%) by increasing coat weight, providing technical flexibility and cost advantages for industrial scale-up.
Journal articles
Magazine articles
Editorial: New coating grades require new tests: Barrier performance inside the package, TAPPI Journal November 2024
The TAPPI Journal special Coating issue is an annual issue that focuses on paper coating and coated papers. It is drawn from presentations at TAPPICon and from other submissions on the topic of paper coating. The TAPPICon 2024 Coating track was rich in high-quality technical content. In fact, the papers were of such significance that Coating members of the TAPPI Journal Editorial Board, which include me, Gregg Reed, and Gregory Welsch, decided that a second paper coating-related special issue would be appropriate for the TAPPI Journal editorial calendar. In addition to the current issue on Barrier Coating Testing, there will be another issue on Coating Fundamentals in early 2025.
Journal articles
Magazine articles
Test method and coating composition impact on measured moisture vapor transmission rate for waterborne coatings on paper, TAPPI Journal November 2024
ABSTRACT: Moisture vapor barrier is one of the necessary performance attributes for paper packages. Two methods are typically employed to assess the moisture vapor transmission rate (MVTR): the gravimetric cup method (ASTM E96) and the MOCON method (ASTM F1249). While those tests have been compared for free standing polymeric films, less is understood about their application in coated paper. Our results show that, despite a general agreement between the two methods, discrepancies exist where test protocols and material properties of coated paper impact the MVTR measurement. The measurement discrepancies can be explained by differences in local moisture concentration. Our study provides new insights on moisture vapor barrier assessment of waterborne coatings on paper and implications for achieving paper packages with improved barrier performance.