Cationic emulsions of maleic anhydride derivatives of oleic and abietic acid for hydrophobic sizing of paper, TAPPI Journal 2020
ABSTRACT: Ordinary rosin sizing agents are mixtures of resin acids that include abietic acid and related compounds obtained from softwoods such as pine. Fatty acids, which are another byproduct of the kraft pulping of soft-wood species, also may have hydrophobic effects, but their use as sizing agents has seldom been considered. In the current study, abietic acid and oleic acid, in the absence of other components, were first modified by reaction with maleic acid anhydride. Then, the maleated derivatives (maleated oleic acid [MOA] and maleated abietic acid [MAA]), which were emulsified with cationic starch at the 1:1 and 3:2 ratio, respectively, were added to fiber furnish containing aluminum sulfate (papermaker’s alum). The prepared sheets were dried with a rotating drum on one side at 100°C at low pressure to cure the sizing agents. The chemical, optical strength, and absorption properties were measured. The presence of the sizing material was confirmed using time of flight secondary ion mass spectrometry (ToF-SIMS), and the retention of the sizing agent on fibers was supported by evidence of hydrocarbons on the paper surface. In addition to achieving sufficient water resistance features with MAA, a lesser hydrophobic character was obtained when using MOA. Compared to commercial applications, relatively large amounts of sizing agent were used to obtain a sufficient sizing degree. The MOA required 5% addition to achieve a similar sizing degree as MAA at the 2% level. The sizing treatments also resulted in substantial increases in tensile index value. Since cationic starch was used in the formulation of the sizing agents, the increase in tensile index may have been due to the influence of cationic starch. Contributions to paper strength from a combination of ionic complexation and mutual association of hydrophobic groups is also proposed. Depending on the amount of sizing agent, the yellowness increased, especially when sizing with MOA.
Journal articles
Magazine articles
Upscaling of foam forming technology for pilot scale, TAPPI JOURNAL August 2019
ABSTRACT: The need for production cost savings and changes in the global paper and board industry during recent years have been constants. Changes in the global paper and board industry during past years have increased the need for more cost-efficient processes and production technologies. It is known that in paper and board production, foam typically leads to problems in the process rather than improvements in production efficiency. Foam forming technology, where foam is used as a carrier phase and a flowing medium, exploits the properties of dispersive foam. In this study, the possibility of applying foam forming technology to paper applications was investigated using a pilot scale paper forming environment modified for foam forming from conventional water forming. According to the results, the shape of jet-to-wire ratios was the same in both forming methods, but in the case of foam forming, the achieved scale of jet-to-wire ratio and MD/CD-ratio were wider and not behaving sensitively to shear changes in the forming section as a water forming process would. This kind of behavior would be beneficial when upscaling foam technology to the production scale. The dryness results after the forming section indicated the improvement in dewatering, especially when foam density was at the lowest level (i.e., air content was at the highest level). In addition, the dryness results after the pressing section indicated a faster increase in the dryness level as a function of foam density, with all density levels compared to the corresponding water formed sheets. According to the study, the bonding level of water- and foam-laid structures were at the same level when the highest wet pressing value was applied. The results of the study show that the strength loss often associated with foam forming can be compensat-ed for successfully through wet pressing.
Journal articles
Magazine articles
Print quality of flexographic printed paperboard related to coating composition and structure, TAPPI Journal January 2018
Print quality of flexographic printed paperboard related to coating composition and structure, TAPPI Journal January 2018
Journal articles
Magazine articles
Lignin-based resins for kraft paper applications, TAPPI Journal November 2019
ABSTRACT: We investigated miscanthus (MS) and willow (W) lignin-furfural based resins as potential reinforce-ment agents on softwood and hardwood kraft paper. These resins might be sustainable alternatives to the commercial phenolformaldehyde (PF) resins. Phenol is a petrochemical product and formaldehyde has been classified as a carcinogen by the U.S. Environmental Protection Agency. The lignin used in this study was derived from hot water extraction (160ºC, 2 h) of MS and W biomass, and may be considered sulfur-free. These biorefinery lignins were characterized for their chemical composition and inherent properties via wet chemistry and instrumental techniques. The resin blends (MS-resin and W-resin) were characterized for their molecular weight, thermal behavior, and mechanical properties. Mechanical properties were measured by the resin’s ability to reinforce softwood and hard-wood kraft papers. The effect of adding hexamethylenetetramine (HMTA), a curing agent, to the resin was also examined. Mixtures of PF and lignin-based resins were investigated to further explore ways to reduce use of non-renewables, phenol, and carcinogenic formaldehyde. The results show that lignin-based resins have the potential to replace PF resins in kraft paper applications. For softwood paper, the highest strength was achieved using W-resin, without HMTA (2.5 times greater than PF with HMTA). For hardwood paper, MS-resin with HMTA gave the highest strength (2.3 times higher than PF with HMTA). The lignin-based resins, without HMTA, also yielded mechanical properties comparable to PF with HMTA.
Journal articles
Magazine articles
Rheological characteristics of platy kaolin, TAPPI JOURNAL September 2019
ABSTRACT: Platy kaolin can provide significant value in the coating of paper and paperboard. It can be used in multiple applications and can provide benefits such as titanium dioxide (TiO2) extension, smoothness improvement, improved print gloss or ink set rates, calendering intensity reduction, and improved barrier properties. It is not a pigment that can be simply substituted for traditional hydrous kaolin without some adjustment to the coating formulation. These adjustments can be as simple as reducing solids, but may require binder changes as well. The coater setup may need to be adjusted because of the unique rheological behaviors these pigments exhibit.The unique rheological characteristics of platy kaolin are explored here. Measurements of the water retention of platy kaolin containing coatings confirm that water retention is not reduced in comparison to more blocky kaolin pigments, despite the lower coating solids at which they need to be run. This means that the rheological characteristics are the most important in understanding the runnability. An extensive analysis reveals some unique behaviors that need to be understood when utilizing these materials. Viscoelastic measurements indicate that, for this binder system, Tan d is mainly a function of solids. This may explain how weeping is initiated on a blade coater. The degree of shear thinning behaviors is investigated using the Ostwald de-Waele power law. The immobilization point was determined using the Dougherty-Krieger equation and related to the work of Weeks at the University of Maine on blade coater runnability. An indirect measure of particle shape and size synergy is also demonstrated using the Dougherty-Krieger equation parameters.
Journal articles
Magazine articles
Flow characteristics of drag-reducing natural bamboo fiber suspensions with minimal environmental load, TAPPI Journal September 2019
ABSTRACT: The reduction of pipe friction loss by adding drag-reducing agents has attracted attention as an aid to energy conservation. Drag-reducing agents induce drag reduction (DR) effects and should have a minimal environmental load, with natural resource-saving potential. This study demonstrates bamboo fiber as a drag-reducing agent that saves natural resources and has a low environmental load. Using pressure drop measurements, we report DR with suspensions of bamboo fibers with the average diameter of 13.3 µm and aspect ratio of 98.7. The maximum DR obtained in this experiment is 43% at the concentration of 4000 ppm and pipe diameter of 30 mm; DR is affected by the Reynolds number, suspension concentration, and pipe diameter. In addition, the bamboo fibers can be easily removed from the suspensions by filtration. We found that low-environmental-load bamboo fiber has DR effects like those of other fibers; its effects are greater than those of conventional synthetic fibers and wood pulp. Furthermore, it is resistant to mechanical degradation, recoverable, and recyclable. Therefore, DR effects can be selectively obtained by adding the fibers only when DR is needed; the fibers can then be collected when DR is no longer necessary. This method might greatly expand the application range of DR agents. The results demonstrate the usefulness of bamboo fibers as DR additives.
Journal articles
Magazine articles
A novel unit operation to remove hydrophobic contaminants, TAPPI Journal April 2020
ABSTRACT: For mills making paper with recovered fiber, removal of hydrophobic contaminants is essential for trouble-free operation of paper machines. Significant cost savings on paper machine operation can be achieved by reducing deposits, which results in better quality, reduced downtime, increased fiber yield, and reduced energy consumption. Bubble nucleation separation (BNS) is a relatively new process for removing hydrophobic particles. When vacuum is applied to a slurry, dissolved gas bubbles nucleate on hydrophobic particles and drag them to the surface for easy removal. We constructed a 16-L batch unit to evaluate the effect of operating parameters on removal of hydrophobic particles, using statistical design of experiments. These results were used to guide our design of a 16-L continuous unit. We tested this unit on laboratory and mill samples. The removal of 60%•80% of hydrophobic particles was achieved with a low reject rate of < 2%.Following on this success, we built a 200-L pilot unit and tested it in our pilot plant. With promising results there, we installed the pilot unit at a commercial paper recycling mill. Over the course of several mill trials, we showed that it was possible to remove a considerable amount of suspended solids from paper machine white water with less than 2% rejects. Unfortunately, due to the unit only treating 50 L/min and the mill flow being 12000 L/min, we were not able treat a sufficient portion of the white water to know whether a large-scale implementation of BNS would improve paper machine runnability.
Journal articles
Point load measurements on paperboard packages and bulging, TAPPI Journal March 2026
ABSTRACT: Paperboard packaging is made by processing board materials into sheets or rolls and shaping them through creasing, cutting, folding, and erecting. The conversion process generates residual moments at the folds that cause panel bulging. This study experimentally investigates how the bulging introduced during the converting processes influence the mechanical response of paperboard packages during point load testing within the elastic deformation range. The study shows that panel bulging may significantly affect packaging performance as-perceived strength and stiffness. Bulging, influenced by the board’s basis weight, can affect the package performance even more than packaging stiffness. Point load tests in the elastic region were performed on empty packages (78 mm × 50 mm × 110 mm) with force applied at specific points along their long sides. The packages evaluated in this study were made of two identically processed materials of different grammages. The heavier material showed more pronounced bulging than the lighter one, leading to overlapping force-displacement curves for the packages, and to that, a lower force and stiffness may be measured at a certain indentation depth for the package of heavier material. This complicates material choice according to functional requirements. The results show that a highly bulged package might resemble one with less bulging of another material. According to the results, it is not certain that a higher grammage package shows a higher indentation force and stiffness than a lower grammage package when measured at a certain indentation. This indicates that optimizing the creasing and folding processes can be a way to enhance performance rather than simply increasing board weight. The study underscores the importance of controlling converting parameters, especially creasing and folding behavior. Well-performed creasing and folding gives a low residual momentum, little bulging, and a high stiffness and compression strength at point loading in the elastic region. Proper optimization can improve packaging performance and manual handling user-friendliness.
Journal articles
Water and grease resistance of paperboard coated with long chain cellulose fatty acid esters using electrostatic powder coating, TAPPI Journal April 2026
ABSTRACT: Fiber-based materials used for foodservice, takeaway, and other packaging applications must typically provide water and grease resistance. Simultaneously, there is growing interest towards bio-based and renewable barrier coatings. In this study we applied thermoplastic long chain fatty acid cellulose esters onto paperboard using electrostatic powder coating to create barrier properties of interest. Electrostatic powder coating provides a water-free process to tackle moisture-induced quality issues and to provide an even coating layer. Cellulose octanoate and palmitate esters were produced in pilot scale. These were ground into fine particles using liquid nitrogen and applied onto paperboard sheets using an electrostatic powder gun. The loosely packed coatings were fixed and fused onto the paperboard by hot pressing. We characterized the coated sheets for coating thickness, contact angles with water, water absorption, grease resistance (KIT), and olive oil barrier. Two commercial polyethylene powders were used as references. Our results indicated that the long chain cellulose fatty acid ester coatings were thermoplastic and hydrophobic with contact angles above 100°. Water absorption was similar to the reference coatings. While grease resistance was lower than with the references, the cellulose ester coatings slowed down diffusion of olive oil through the paperboard. Cellulose octanoate ester with a lower melt viscosity already provided smooth coatings after the initial hot pressing step, while in most cases, the second post hot pressing step further improved the barrier properties.
Journal articles
Magazine articles
Application of fuzzy TOPSIS in the Analyze phase of the DMAIC cycle to aid decision-making, TAPPI Journal April 2020
ABSTRACT: This paper reports the use of multicriteria analysis in the Analyze phase of the DMAIC (Define-Measure-Analyze-Improve-Control) cycle for continuous improvement. The research was carried out in a tissue paper factory located in southern Brazil. A sample of 64 parts of 16 different reels of recycled paper was used. A problem regarding paper quality variability was detected, presenting a scrap index ranging between 9% and 23%, compromising machine productivity and product sales. This motivated the implementation of a structured project supported by the application of the DMAIC cycle. The project team (machine operators, maintenance staff, supervisor, and data analyst) defined the evaluation criteria and determined the control intervals and their equivalence with linguistic variables to support the necessary evaluations for the application of fuzzy TOPSIS (Technique for Order of Preference by Similarity to Ideal Solution). The criteria were C1-Longitudinal Strength (Kgf), C2-Longitudinal Elongation (mm), C3-Cross-strength (kgf), C4-Cross-elongation (mm), C5-Weight (g/m²), and C6-Humidity (%). The results showed that samples with the same ranking had the lowest scrap indexes in the subsequent process. Also, the criterion C5 had a more significant impact on the quality of the product than the other criteria, which was determined from the DMAIC sequence. Improvements related to C5 should be prioritized. The fuzzy TOPSIS method presented is a flexible tool, adapting itself to the solution of the problem and contributing to the decision-making process.