Effects of hydrodynamic shear during formation of paper sheets with the addition of nanofibrillated cellulose, cationic starch, and cationic retention aid, TAPPI Journal September 2024
ABSTRACT: Laboratory tests were conducted to evaluate effects of hydrodynamic shear levels on papermaking process variables and paper handsheet properties. The furnish was from 100% recycled copy paper, to which was added nanofibrillated cellulose (NFC) at the 5% level following its optional pretreatment with cationic starch. A cationic copolymer of acrylamide (cPAM) was used as the retention aid. Different levels of hydrodynamic shear were applied both after mixing the NFC with the cationic starch (pre-shearing) or after all the furnish components had been combined (final shearing). The presence or absence of pre-shearing was found to have little effect on the measured outcomes. By contrast, increasing final shear hurt filler retention and made the resulting paper more uniform. However, the final shear level did not have a significant effect on the tensile strength of the resulting handsheets. Medium-charge density cationic starch, used in pretreating the NFC, consistently gave greater strength in comparison to a high-charge cationic starch. The significance of these findings is that though the relatively high hydrodynamic shear levels associated with modern paper machines can have some beneficial effects, they do not necessarily overcome all challenges associated with wet-end addition of nanocellulose in combination with other additives.
Journal articles
Magazine articles
Control of continuous digester kappa number using generalized model predictive control, TAPPI Journal September 2024
ABSTRACT: Kappa number variability at the digester impacts pulp yield, physical strength properties, and lignin content for downstream delignification processing. Regulation of the digester kappa number is therefore of great importance to the pulp and paper industry. In this work, an industrial application of model-based predictive control (MPC), based on generalized prediction control, was developed for kappa number feedback control and applied to a dual vessel continuous digester located in Western Canada. The problem was complicated by the need to apply heat at multiple locations in the cook. In this study, the problem was reduced from a multiple to a single input system by identifying three potential single variable permutations for temperature adjustment. In the end, a coordinated approach to the heaters was adopted. The process was perturbed and modeled as a simple first order plus dead time model and implemented in generalized predictive control (GPC). The GPC was then configured to be equivalent to Dahlin’s controller, which reduced tuning parameterization to a single closed loop time constant. The controller was then tuned based on robustness towards a worst-case dead time mismatch of 50%. The control held the mean value of the kappa number close to the setpoint, and a 40% reduction in the kappa number’s standard deviation was achieved. Different kappa number trials were run, and the average fiberline yield for each period was evaluated. Trial results suggested yield gains of 0.3%•0.5% were possible for each 1 kappa number target increase.
Journal articles
Magazine articles
Flocculation of fiber suspensions studied by Rheo-OCT, TAPPI Journal September 2024
ABSTRACT: When dealing with papermaking fiber suspensions, particle flocculation takes place even before the paper web is formed. The particle flocculation depends on several aspects, including particle mass concentration (consistency), particle collisions, electrochemical interactions promoted by chemical additives, etc. Due to its importance, fiber suspension flocculation has been studied for a long time in papermaking, and several methods have been developed for this purpose. The traditional techniques include, for example, focused beam reflectance microscopy (FBRM) and high-speed video imaging (HSVI). Recently, a new optical method, optical coherence tomography (OCT), has emerged for flocculation analysis. The advantages of OCT are the possibility to study opaque suspensions, its micron-llevel resolution, and its high data acquisition speed. The OCT measurements can be combined with rheological (Rheo) measurements, allowing simultaneous measurement of both the time evolution of the floc size and the suspension viscosity. In this work, we used this approach, Rheo-OCT, to study the flocculation of suspensions of various papermaking furnishes. We analyzed the time evolution of the floc size and the fiber suspension viscosity when the studied papermaking suspensions were treated with highly refined furnish (HRF) — a furnish that contained a significant amount of micofibrillated cellulose (MFC)-type fibrils — and/or chemical additives. Such studies can lead to a better understanding of the impact of flocculation on the produced paper web in terms of qualities like formation, drainage potential, and strength behavior.
Journal articles
Magazine articles
Study on the effect of aluminum diethyl phosphinate in synergy with ammonium polyphosphate on the flame retardancy of cellulose paper, TAPPI Journal April 2025
ABSTRACT: This paper involved the synergistic incorporation of ammonium polyphosphate (APP) and diethyl aluminum phosphinate (AlPi) as flame-retardant fillers for producing flame-retardant paper. The research revealed that APPs were square particles with a smooth surface, and their solubility was 0.29 g/100 mL at 20°C, which increased to 4.12 g/100 mL at 60°C. The surfaces of AlPis were rough and irregular. The solubility of AlPi was 0.023 g/100 mL at 20°C, and the solubility remained stable when the temperature increased. The addition of AlPi had a minor influence on the pulp beating degree. The tensile strength of kraft/APP/AlPi decreased with the increase of the AlPi addition. For a paper with 20 wt% APP and 0 wt% AlPi, the limiting oxygen index (LOI) value was 27.2%, and it burned completely at the eighth second during vertical combustion. When the AlPi additive content increased to 20 wt%, its LOI value increased to 32.2%, and the vertical combustion self-extinguished as soon as the flame was removed. Scanning electron microscopy (SEM) showed that the char residue of the kraft/APP/AlPi had a more complete fiber network structure than that of kraft/APP. The Raman spectroscopy indicated that the area ratio of the D (amorphous phase; disordered graphite vibration) band to the G (crystal phase; graphite carbon vibration) band (ID/ IG) ratio of kraft/APP/AlPi was lower than that of kraft/APP, meaning that the graphitization degree of the char residue of kraft/APP/AlPi was higher than that of kraft/APP, which indicated the kraft/APP/AlPi had better flame retardancy.
Journal articles
In-situ process monitoring in deep-drawing of paper using partially transparent tools, TAPPI Journal August 2025
ABSTRACT: The production of three-dimensionally formed packaging from paper by deep drawing usually leads to the occurrence of wrinkles, which result from the high tangential compressive stresses in the flange area and the limited flowability of the material. Wrinkles, although mostly tolerated in industry, end in both a reduced visual appearance and a reduction in usability for packaging, as with, for example, when gas-tightness is required. Previous research efforts have been limited to determining the wrinkle distribution after completion of forming and removal of the formed part. Consequently, the possibility of understanding the sequence of formation of individual wrinkles in the inhomogeneous material is lost. To remedy this situation, a method for local in-situ process monitoring is presented. Using a transparent die and an industrial camera, the flange area can be observed during the forming process. An image processing algorithm is applied to analyze the local development of the deep drawing process from the continuously recorded image data. The method described can be used to analyze the draw-in behavior and wrinkle formation locally and continuously over the drawing depth. The blank holder force influences the draw-in and the wrinkle pattern both locally and throughout the drawing process. A more precise understanding of the wrinkle formation will allow for more efficient process control in the future.
Journal articles
Magazine articles
Upscaling of foam forming technology for pilot scale, TAPPI JOURNAL August 2019
ABSTRACT: The need for production cost savings and changes in the global paper and board industry during recent years have been constants. Changes in the global paper and board industry during past years have increased the need for more cost-efficient processes and production technologies. It is known that in paper and board production, foam typically leads to problems in the process rather than improvements in production efficiency. Foam forming technology, where foam is used as a carrier phase and a flowing medium, exploits the properties of dispersive foam. In this study, the possibility of applying foam forming technology to paper applications was investigated using a pilot scale paper forming environment modified for foam forming from conventional water forming. According to the results, the shape of jet-to-wire ratios was the same in both forming methods, but in the case of foam forming, the achieved scale of jet-to-wire ratio and MD/CD-ratio were wider and not behaving sensitively to shear changes in the forming section as a water forming process would. This kind of behavior would be beneficial when upscaling foam technology to the production scale. The dryness results after the forming section indicated the improvement in dewatering, especially when foam density was at the lowest level (i.e., air content was at the highest level). In addition, the dryness results after the pressing section indicated a faster increase in the dryness level as a function of foam density, with all density levels compared to the corresponding water formed sheets. According to the study, the bonding level of water- and foam-laid structures were at the same level when the highest wet pressing value was applied. The results of the study show that the strength loss often associated with foam forming can be compensat-ed for successfully through wet pressing.
Journal articles
Magazine articles
Viscoelastic web curl due to storage in wound rolls, TAPPI Journal July 2020
ABSTRACT: Winding is often the final operation in a roll-to-roll manufacturing process. Web materials, i.e., materials that are thin compared to their length, are wound into rolls because this form is the only practical means to store them. The resulting bending strains and associated stresses are large for thick webs and laminates. As many webs are viscoelastic on some time scale, bending stresses lead to creep and inhomogeneous changes in length. When the web material is unwound and cut into discrete samples, a residual curvature remains. This curvature, called curl, is the inability for the web to lie flat at no tension. Curl is an undesirable web defect that causes loss of productivity in a subsequent web process. This paper describes the development and implementation of modeling and experimental tools to explore and mitigate curl in homogenous webs. Two theoretical and numerical methods that allow the prediction of curl in a web are developed: a winding software based on bending recovery theory, and the implementation of dynamic simula-tions of winding. One experimental method is developed that directly measures the curl online by taking advantage of the anticlastic bending resulting from the curl. These methods are demonstrated for a low-density polyethylene web.
Journal articles
Magazine articles
Cationic emulsions of maleic anhydride derivatives of oleic and abietic acid for hydrophobic sizing of paper, TAPPI Journal 2020
ABSTRACT: Ordinary rosin sizing agents are mixtures of resin acids that include abietic acid and related compounds obtained from softwoods such as pine. Fatty acids, which are another byproduct of the kraft pulping of soft-wood species, also may have hydrophobic effects, but their use as sizing agents has seldom been considered. In the current study, abietic acid and oleic acid, in the absence of other components, were first modified by reaction with maleic acid anhydride. Then, the maleated derivatives (maleated oleic acid [MOA] and maleated abietic acid [MAA]), which were emulsified with cationic starch at the 1:1 and 3:2 ratio, respectively, were added to fiber furnish containing aluminum sulfate (papermaker’s alum). The prepared sheets were dried with a rotating drum on one side at 100°C at low pressure to cure the sizing agents. The chemical, optical strength, and absorption properties were measured. The presence of the sizing material was confirmed using time of flight secondary ion mass spectrometry (ToF-SIMS), and the retention of the sizing agent on fibers was supported by evidence of hydrocarbons on the paper surface. In addition to achieving sufficient water resistance features with MAA, a lesser hydrophobic character was obtained when using MOA. Compared to commercial applications, relatively large amounts of sizing agent were used to obtain a sufficient sizing degree. The MOA required 5% addition to achieve a similar sizing degree as MAA at the 2% level. The sizing treatments also resulted in substantial increases in tensile index value. Since cationic starch was used in the formulation of the sizing agents, the increase in tensile index may have been due to the influence of cationic starch. Contributions to paper strength from a combination of ionic complexation and mutual association of hydrophobic groups is also proposed. Depending on the amount of sizing agent, the yellowness increased, especially when sizing with MOA.
Journal articles
Magazine articles
Rheological characteristics of platy kaolin, TAPPI JOURNAL September 2019
ABSTRACT: Platy kaolin can provide significant value in the coating of paper and paperboard. It can be used in multiple applications and can provide benefits such as titanium dioxide (TiO2) extension, smoothness improvement, improved print gloss or ink set rates, calendering intensity reduction, and improved barrier properties. It is not a pigment that can be simply substituted for traditional hydrous kaolin without some adjustment to the coating formulation. These adjustments can be as simple as reducing solids, but may require binder changes as well. The coater setup may need to be adjusted because of the unique rheological behaviors these pigments exhibit.The unique rheological characteristics of platy kaolin are explored here. Measurements of the water retention of platy kaolin containing coatings confirm that water retention is not reduced in comparison to more blocky kaolin pigments, despite the lower coating solids at which they need to be run. This means that the rheological characteristics are the most important in understanding the runnability. An extensive analysis reveals some unique behaviors that need to be understood when utilizing these materials. Viscoelastic measurements indicate that, for this binder system, Tan d is mainly a function of solids. This may explain how weeping is initiated on a blade coater. The degree of shear thinning behaviors is investigated using the Ostwald de-Waele power law. The immobilization point was determined using the Dougherty-Krieger equation and related to the work of Weeks at the University of Maine on blade coater runnability. An indirect measure of particle shape and size synergy is also demonstrated using the Dougherty-Krieger equation parameters.
Journal articles
Magazine articles
Flow characteristics of drag-reducing natural bamboo fiber suspensions with minimal environmental load, TAPPI Journal September 2019
ABSTRACT: The reduction of pipe friction loss by adding drag-reducing agents has attracted attention as an aid to energy conservation. Drag-reducing agents induce drag reduction (DR) effects and should have a minimal environmental load, with natural resource-saving potential. This study demonstrates bamboo fiber as a drag-reducing agent that saves natural resources and has a low environmental load. Using pressure drop measurements, we report DR with suspensions of bamboo fibers with the average diameter of 13.3 µm and aspect ratio of 98.7. The maximum DR obtained in this experiment is 43% at the concentration of 4000 ppm and pipe diameter of 30 mm; DR is affected by the Reynolds number, suspension concentration, and pipe diameter. In addition, the bamboo fibers can be easily removed from the suspensions by filtration. We found that low-environmental-load bamboo fiber has DR effects like those of other fibers; its effects are greater than those of conventional synthetic fibers and wood pulp. Furthermore, it is resistant to mechanical degradation, recoverable, and recyclable. Therefore, DR effects can be selectively obtained by adding the fibers only when DR is needed; the fibers can then be collected when DR is no longer necessary. This method might greatly expand the application range of DR agents. The results demonstrate the usefulness of bamboo fibers as DR additives.