Cationic emulsions of maleic anhydride derivatives of oleic and abietic acid for hydrophobic sizing of paper, TAPPI Journal 2020
ABSTRACT: Ordinary rosin sizing agents are mixtures of resin acids that include abietic acid and related compounds obtained from softwoods such as pine. Fatty acids, which are another byproduct of the kraft pulping of soft-wood species, also may have hydrophobic effects, but their use as sizing agents has seldom been considered. In the current study, abietic acid and oleic acid, in the absence of other components, were first modified by reaction with maleic acid anhydride. Then, the maleated derivatives (maleated oleic acid [MOA] and maleated abietic acid [MAA]), which were emulsified with cationic starch at the 1:1 and 3:2 ratio, respectively, were added to fiber furnish containing aluminum sulfate (papermaker’s alum). The prepared sheets were dried with a rotating drum on one side at 100°C at low pressure to cure the sizing agents. The chemical, optical strength, and absorption properties were measured. The presence of the sizing material was confirmed using time of flight secondary ion mass spectrometry (ToF-SIMS), and the retention of the sizing agent on fibers was supported by evidence of hydrocarbons on the paper surface. In addition to achieving sufficient water resistance features with MAA, a lesser hydrophobic character was obtained when using MOA. Compared to commercial applications, relatively large amounts of sizing agent were used to obtain a sufficient sizing degree. The MOA required 5% addition to achieve a similar sizing degree as MAA at the 2% level. The sizing treatments also resulted in substantial increases in tensile index value. Since cationic starch was used in the formulation of the sizing agents, the increase in tensile index may have been due to the influence of cationic starch. Contributions to paper strength from a combination of ionic complexation and mutual association of hydrophobic groups is also proposed. Depending on the amount of sizing agent, the yellowness increased, especially when sizing with MOA.
Journal articles
Magazine articles
Development of a fast brightness testing method for mechanical pulp based on microwave oven drying, TAPPI Journal June 2020
ABSTRACT: Brightness is an important quality parameter for pulp products, and it is important to have reliable measurement of pulp brightness in a timely manner for process control and/or quality control purposes. In these circumstances, a quick testing method for pulp brightness is highly desirable.A rapid handsheet brightness testing method for lignin-rich mechanical pulp has been developed, which is based on the use of tap water to make handsheets and microwave ovens to rapidly dry the handsheet. Microwave oven fast drying decreased the handsheet brightness of mechanical pulp by 5•6 points due to the lignin-originated discol-oration reactions. The spray of ascorbic acid and ethylenediaminetetraacetic acid (EDTA) solutions to the handsheet can effectively inhibit these lignin discoloration reactions.With 0.2% ascorbic acid and 0.2% EDTA spraying on the wet pulp handsheet, the brightness of the handsheet from a peroxide-bleached stone groundwood pulp after the microwave oven fast drying method was similar to that obtained from the same pulp but following TAPPI Standard Test Method T 272 sp-12 “Forming handsheets for reflectance testing of pulp (sheet machine procedure)”. The effect of handsheet dryness on the handsheet brightness was also studied, and the results showed that the brightness reading was almost constant in the dryness range of 70% to 90%. The method developed is a reliable, fast brightness testing method for lignin-rich pulp that is of practical interest in industrial operations.
Journal articles
Magazine articles
Integrated study of flue gas flow and superheating process in a recovery boiler using computational fluid dynamics and 1D-process modeling, TAPPI Journal June 2020
ABSTRACT: Superheaters are the last heat exchangers on the steam side in recovery boilers. They are typically made of expensive materials due to the high steam temperature and risks associated with ash-induced corrosion. Therefore, detailed knowledge about the steam properties and material temperature distribution is essential for improving the energy efficiency, cost efficiency, and safety of recovery boilers. In this work, for the first time, a comprehensive one-dimensional (1D) process model (1D-PM) for a superheated steam cycle is developed and linked with a full-scale three-dimensional (3D) computational fluid dynamics (CFD) model of the superheater region flue gas flow. The results indicate that: (1) the geometries of headers and superheater platens affect platen-wise steam mass flow rate distribution (3%•7%); and (2) the CFD solution of the 3D flue gas flow field and platen heat flux distribution coupled with the 1D-PM affect the platen-wise steam superheating temperature (45%•122%) and material temperature distribution (1%•6%). Moreover, it is also found that the commonly-used uniform heat flux distribution approach for the superheating process is not accurate, as it does not consider the effect of flue gas flow field in the superheater region. These new observations clearly demonstrate the value of the present integrated CFD/1D-PM modeling approach.
Journal articles
Magazine articles
Quantification of the degree of preference for different tissue products based on a hand-felt tissue test panel, TAPPI Journal May 2023
ABSTRACT: In this study, we successfully established a quantification model to determine the preference (PF) for different tissue products based on the results of a hand-felt tissue testing panel. The panel ascertained that products designed with four-ply tissues provided higher total tensile strength (TTS) and hand-felt surface softness (HSS) than did those of the three-ply, two-ply, and single-ply products.When practically tested with a tissue softness analyzer (TSA), the four-ply tissue product had a softness (TSA-HF) advantage; however, in human panel tests, more than half of the participants could not be sure of the hand-felt bulk softness (HBS) of the four-ply tissue product. This was mainly because when using the four-ply tissue, the hand-held test pad gave an overall perception distinctly different from those of the hand-held two- or three-ply products, which also differed from the flattened state of test pieces used in the instrumental softness tests. Users could distinctly feel that a product was safer (better TTS) and more comfortable (higher hand-held surface softness). Thus, the four-ply tissue product was accorded a higher preference.
Journal articles
Magazine articles
Research on flame-retardant paper prepared by the method of in-pulp addition of ammonium polyphosphate, TAPPI Journal May 2023
ABSTRACT: At present, the production of flame-retardant paper usually uses the impregnation method of phosphorus-nitrogen flame retardants in paper. There are few reports on the application of an in-pulp addition method. In this paper, the solubility of ammonium polyphosphate (APP) and its effect on flame-retardant paper were investigated for use in an in-pulp addition method. It was found that APP particles were square, with an average particle size of 21.88 µm. The particle size decreased significantly after immersion in water at 25°C for 24 h. Furthermore, most of the APPs were dissolved after immersion in water at 90°C for 0.5 h, and the residuals agglomerated and their shape turned into an amorphous form. The APP possessed strong electronegativity and could partially ionize in water. The solubility of APP was 0.18 g/100 mL water at 25°C and increased quickly when the temperature was higher than 30°C. Therefore, APP should be added to the pulp at temperatures below 30°C. The tensile strength of the paper initially increased with the addition of APP, and it reached the maximum value when the APP content was 10% and then gradually decreased. The limiting oxygen index (LOI) value of the paper was 28.7% when the added amount of APP was 30% and cationic polyacrylamide (CPAM) was 0.08%, reaching the flame-retardant level.
Journal articles
Pre-damping effects on water absorption and drying dynamics in flexographic printing, TAPPI Journal November 2025
ABSTRACT: Optimizing flexographic printability can involve the ink and the substrate, as well as the printing process. It has been widely reported in the literature that controlling topography of the substrate and its porosity are vital for good flexographic printability, especially when using water-based inks. This study focuses on how pre-damping a surface impacts liquid absorption and improves wet trapping (ink on ink with no intermediate drying) in flexographic printing. A Prüfbau universal print tester was adapted to analyze flexographic wet-on-wet ink printing and trapping using yellow and magenta inks for contrast. Slow drying of the first ink layer (yellow) leads to mottle when the second layer (magenta) is applied. The study explores the “wet sponge” hypothesis: a pre-damped surface should absorb liquid faster. The Lucas- Washburn equation describes long-term absorption, but it does not capture short-term uptake, which instead follows a linear dependence on time.
Journal articles
Effects of biopolymer coatings on paper permeability and capillarity for paper-based rapid diagnostic test devices, TAPPI Journal September 2025
ABSTRACT: Rapid diagnostic test (RDT) devices are widely used for diagnostics due to their affordability, portability, and user-friendliness. However, conventional assays typically rely on nitrocellulose membranes and plastic casings. These materials raise environmental concerns due to their non-renewable nature, energy-intensive production methods, and poor biodegradability. This study explores the development of fully bio-based RDT substrates using a sustainable alternative: softwoodderived microfibrillated cellulose (MFC), cellulose nanocrystals (CNC), and chitosan as surface modifiers to improve paper properties and enhance RDT sustainability. Cotton filter paper substrates were coated with different biopolymer formulations using a manual blade coater: bleached MFC (BMFC), lignin-containing MFC (LMFC), BMFC combined with CNC, LMFC combined with CNC, and chitosan. Evaluation of the most relevant physical properties concerning RDT performance was conducted, including wetting, water retention value, air permeability, capillary flow rate, and surface morphology. Results showed that biopolymer- based coatings can effectively modify surface properties by reducing pore size and tuning hydrophilicity, while maintaining the renewable and bio-based characteristics of the substrate. The LMFC-coated paper exhibited the best overall performance among all formulations, reducing flow time by 50% (3.00 mm/s vs. 1.5 mm/s) compared to the uncoated paper, yet preserving high water retention. The BMFC+CNC coating also significantly improved flow rate, showing a 36.7% reduction (2.37 mm/s vs. 1.5 mm/s), and enhanced porosity uniformity. In contrast, the flow rate of chitosan-coated paper decreased by over 5,000% (0.027 mm/s), reflecting its strong barrier properties and hydrophobic surface (highest contact angle: 91.4°). These findings suggest that MFC-based coatings are promising ecofriendly alternatives to nitrocellulose, offering optimized capillary transport and structural adaptability. This paves the way for the development of sustainable, high-performance, rapid diagnostic tests.
Journal articles
Pilot-made, highly extensible paper for dry 3D forming, TAPPI Journal May 2025
Cellulose fiber-based packaging materials must perform well in demanding three dimensional (3D) forming process conditions. On the other hand, the development of manufacturing concepts is required for improved competitiveness of bio-based materials. This study covers some key factors that influence the extensibility of cellulose fiber-based structures and presents a pilot-scale development study of a 3D formable material concept. Bleached softwood kraft (BSK) pulp from a Nordic pulp mill was used in the pilot trials. Cellulose-based webs were formed using water-laid and foam-laid web forming using a pilot paper machine. For the water-laid forming, the BSK pulp was refined by applying a high consistency (HC) phase at over 40% consistency, followed by a low consistency (LC) refining at 4% consistency. The BSK pulp was refined for the foam-laid forming by only applying lowconsistency refining. In the foam-laid web forming, anionic sodium dodecyl sulfate (SDS), two foamable latexes, and polyvinyl alcohol (PVA) were used as foaming agents. The pilot rolls were dried at a separate steam cylinder dryer pilot and compacted in-plane in the machine direction (MD) at a separate pilot machine. Tensile properties of the treated paper webs were measured and evaluated with respect to achieved web shrinkage. The same dimensional contraction brought by shrinkage was almost strained out in tensile testing. The results indicated that the shrinkage that occurred by drying and in-plane compaction depended on the pulp furnish. The water-laid material achieved about 30% elongation, whereas the foam-laid material achieved significantly above 50% elongation. The 3D forming performance of the dry materials was tested using fixed and sliding blank methods. The dry paper sheets performed well enough in 3D forming for application to many consumer package applications according to their extensibility.
Journal articles
Magazine articles
Peracetate/singlet oxygen chemistry used in post-bleaching of kraft pulp as a practical oxidant for paper machines, TAPPI Journal May 2021
ABSTRACT: The use of a novel sodium peracetate/singlet oxygen chemistry for brightening bleached kraft pulp shows exciting potential for technical performance, supply logistics, safety, and cost reduction. Potential chemical carryover to the paper machine raises questions about whether peracetate will impact paper machine performance, such as metal corrosion, useful press felt life, and interference with existing biocide programs or paper machine chemistry. Sodium peracetate/singlet oxygen chemistry can be used in high-density storage chests for brightening/whitening and to increase color stability. Any oxidant used directly before the paper machine has the possibility of impacting paper machine operations. Traditional oxidants used in bleaching, such as chlorine dioxide and hydrogen peroxide, are known to cause corrosion on machinery metals and press felts. Hydrogen peroxide residuals can interfere with common biocide programs. Traditional oxidants used in biocide treatments themselves significantly degrade press felt life when the rule-of-thumb concentration thresholds are exceeded. Sodium peracetate is evaluated in this paper for its impact on nylon press felt fiber degradation, metal corrosion, and interference with typical biocide programs.Laboratory results indicate that sodium peracetate/singlet oxygen chemistry is less corrosive than chlorine, bromine, and hydrogen peroxide on press felt nylon fiber and can therefore be used at higher levels than those chemistries to increase brightness without increasing negative downstream impact. Sodium peracetate can also be used with current biocide programs without negative impacts such as consumptive degradation. Higher residuals of peracetate going to the paper machine may be useful as a biocide itself and can complement existing programs, allowing those programs to stay within their safe operating levels and thereby extend press felt useful life.
Journal articles
Magazine articles
Gas dispersion in the oxygen delignification process, TAPPI Journal May 2021
ABSTRACT: There has been very little knowledge about the state of gas dispersion in the oxygen delignification process, even though this has a major impact on the performance of the reactor. This paper presents a new continu-ous inline method for measuring oxygen bubble size distribution in the reactor, as well as results from studies con-ducted in softwood and hardwood lines. This new measurement worked well, and new information about oxygen bubble size, as well as how different reactor conditions affected the distribution, was obtained. For example:œ In the softwood line, the mean volume-weighted bubble size was about 0.1 mm, whereas in the hardwood line, this size was almost 10 times higher. For both lines, there was considerable variation in the measured bubble size over the long term.œ For both lines, an increase in mixer rotation speed caused a discernible decrease in the bubble size, and an increase in oxygen charge caused a discernible increase in the bubble size.œ In the softwood line, no coalescence of the bubbles in the reactor was observed, but in the hardwood line, some coalescence of the larger bubbles occurred.œ In the test conducted in the hardwood line, the use of brownstock washer defoamer caused a discernible increase in oxygen bubble size.œ In the hardwood line, reactor pressure had a noticeable effect on the amount of delignification, which indicated that improving mass transfer of oxygen (e.g., by decreasing the oxygen bubble size, in this case) should also have an increasing effect on the delignification.