Preparation of regenerated cellulose from rice straw lignocellulosic waste and its use for reinforced paper products, TAPPI Journal July 2021
ABSTRACT: Rice straw waste is a lignocellulosic waste produced by farmers in large quantities. In this study, regenerated cellulose (RC) from rice straw was prepared by dissolving rice straw holocellulose (HC) in NaOH/Urea/Thio-urea/Water solution by the freeze-thawing process. The crystallinity index of RC was calculated at 31%, which is out of the crystallinity range of 39%•69% that has been previously suggested.The study indicated that the RC is amorphous with a low degree of polymerization (638) and higher hydroxyl group content as compared to HC. The fiber length of RC was found to be 26.7% shorter; however, the width of RC was 21.2% higher as compared to HC. Reduced kinked fiber content was observed in the fraction of RC (18.3%) as compared with HC (39.1%), and a higher curl index of fiber was observed more so in HC (10.5%) than RC (5.6%). Because of the regeneration process, the fiber length was reduced and a fines element content of about 96% was observed in RC compared to the initial fines content of HC (56.9%). Irrespective of the high fines element content of RC, the composite paper of rice straw bleached pulp and RC fibers was developed with an increase in the tensile index from 41.4 N.m/g to 71.2 N.m/g and an increase in the burst index from 4.7 kPa.m2/g to 5.3 kPa.m2/g with the addition of 5% and 15% RC, respectively. However, enhanced tear index of paper was observed up to 5% and then it declined upon further addition of RC. The study revealed that regenerated cellulose can be used as a strength additive to overcome the shortcomings of low mechanical properties in paper products.
Journal articles
Magazine articles
A guide to eliminating baggy webs, TAPPI Journal June 2021
ABSTRACT: Slack or baggy webs can cause misregistration, wrinkles, and breaks in printing and converting operations. Bagginess appears as non-uniform tautness in the cross direction (CD) of a paper web. The underlying cause is uneven CD tension profiles, for which there are few remedies once the paper is made. Precision measurements of CD tension profiles combined with trials on commercial paper machines have shown that uniform CD distribution of moisture, basis weight, and caliper profiles at the reel are key to avoiding bagginess. However, the most important but infrequently measured factor is the CD moisture profile entering the dryer section. Wetter areas entering the dryers are permanently elongated more than dry areas, leading to greater slackness in the finished paper. In storage, wound-in tension can amplify baggy streaks in paper near the surface of a roll and adjacent to the core. Unwrapped or poorly wrapped rolls exposed to low humidity environments may have baggy centers caused by moisture loss from the roll edges.All of the factors that impact bagginess have been incorporated in a mathematical model that was used to interpret the observations from commercial trials and can be used as a guide to solve future problems.
Journal articles
Magazine articles
Totally chlorine-free peracetic acid pulping for nanocellulose isolation from hemp and poplar, TAPPI Journal August 2023
ABSTRACT: Nanocellulose is a promising and sustainable feedstock for developing advanced and functional materials. However, the characteristics of nanocellulose, such as crystallinity, surface energy, and aspect ratio, can vary depending on biomass source and pretreatment methods, leading to variable performance of the nanocellulose-based materials. In this study, cellulose nanocrystals (CNCs) were isolated from hemp and poplar using totally chlorine free (TCF) peracetic acid and sodium chlorite delignification and bleaching pretreatments to probe the influences of biomass source and treatment methods on the isolation and characteristics of CNCs. Our results showed that hemp and poplar were almost completely delignified by peracetic acid treatment, whereas sodium chlorite treatment left 5%•6% lignin in the pulp. The yields of CNCs from raw hemp and poplar biomass ranged from 9.8% to 21.9% and 10.9% to 28.3%, respectively, depending on the treatment methods. The dimensions of CNCs from TCF-treated biomass generally maintained a larger width and aspect ratio than those from sodium chlorite-treated biomass. The poplar-derived CNCs exhibited slightly higher crystallinity of 53%•58% than hemp-derived CNCs of 49%•54%. The zeta potential of the CNCs, ranging from -20.1 mV to -31.1 mV, ensured a well-dispersed aqueous solution. The surface energy (dispersive energy of 40•80 mJ/m2 and specific energy of 2•10 mJ/m2), water interaction, and thermal stability of the CNCs were comparable, regardless of the biomass source and pretreatment methods. Our finding suggests that the TCF technique with peracetic acid treatment is a promising delignification and bleaching approach to obtain cellulose-rich pulps from herbaceous and hardwood biomass for nanocellulose isolation.
Journal articles
Magazine articles
SCC susceptibility of chromized type 409 stainless steel in alkaline chloride solutions at ambient temperature and pressure, TAPPI Journal August 2023
ABSTRACT: Biomass hydrothermal liquefaction (HTL) is operated in a harsh reaction medium that contains hot pressurized water, inorganic acidic or basic catalyst, and inorganic/organic corrosive components released during the conversion. Candidate alloys for this application require suitable resistance to both corrosion and stress corrosion cracking (SCC) to withstand the HTL process conditions (250°C•374°C and 4•22 MPa). Ferritic iron-chromium (Fe-Cr) steels are more prone to corrosion but less susceptible to SCC compared to austenitic iron-chromium-nickel (Fe-Cr-Ni) steels. Chromizing can significantly reduce corrosion of Type 409 stainless steel (Fe-11Cr) in a simulated aqueous HTL solution. The objective of this study is to determine the SCC susceptibility of chromized Type 409 stainless steel, relative to the bare (non-chromized) case. The slow strain rate testing (SSRT) technique was used for this purpose. For simplicity of experimentation, SSRT was conducted using simulated HTL water containing 800 ppm potassium chloride (KCl), 1 M potassium carbonate (K2CO3), and 10 wt% acetic acid at ambient temperature and pressure. Complementary potentiodynamic polarization measurements and surface analysis by X-ray photoelectron spectros-copy (XPS) were also made to help interpret the SSRT results. The SSRT results show no significant difference in SCC susceptibility, regardless of the starting surface. Thus, chromizing, while significantly reducing the corrosion of Type 409 stainless steel, does not adversely affect SCC susceptibility, at least under the conditions tested.
Journal articles
Magazine articles
A true green cover for industrial waste landfills, TAPPI Journal April 2024
ABSTRACT: Greenhouse gas (GHG) emissions in the United States totaled 5,981 million metric tons of carbon dioxide equivalent (MMT CO2eq) in 2020. Of that, GHG emissions by the pulp and paper sector amounted to 35 MMT CO2eq direct emissions and those by industrial waste landfills summed to 7.4 MMT CO2eq direct emissions. Loss of GHG sinks due to change in land use further contributes to the net GHG emissions. Industrial waste landfills are typically required to comply with certain federal and state regulations, including meeting requirements for final cover systems. Conventional final cover systems have included use of soil covers and/or soil-geosynthetic composite covers. An engineered turf cover provides for an excellent “green” alternative final cover system for industrial waste landfills.This paper discusses various sustainability aspects pertaining to use of an engineered turf final cover, including: (i)significantly low carbon footprint associated with the construction of an engineered turf alternative final coverwhen compared to closure using a traditional or prescriptive cover system; (ii) saving valuable soil and land resourc-es; (iii) saving water resources by reduction in its use during and after construction; (iv) reducing impacts associated with borrow areas; and (v) reducing overall carbon footprint. Further, when using an engineered turf cover, opportunities exist for beneficial reuse of land, including development of solar energy. A brief discussion on the potential fordevelopment of solar energy is included.
Journal articles
Magazine articles
Surface modification of TiO2 with MPS and its effects on the wettability and physical properties of Kawayan Kiling (Bambusa vulgaris Schrad ex. Wendl) handsheets, TAPPI Jouranl April 2024
ABSTRACT: The need for hydrophobic papers has steadily increased over past years. These papers are often sought after as packaging materials and have high demand in the food industry and medicine. In this study, various concentrations of surface-modified TiO2-MPS were added to Kawayan Kiling (B. vulgaris) pulp at the wet-end section of handsheet formation. Surface-modified TiO2-MPS was made from nano-titanium (IV) oxide using 3-(trimethoxysilyl)propyl methacrylate as a coupling agent. The wettability of handsheets and physical properties were tested using various standard methods. Results reveal that the handsheets without surface-modified TiO2-MPS had the lowest water contact angle (WCA), while the handsheet with 12.34% (w/w) surface-modified TiO2-MPS had the highest WCA. At 17% (w/w) surfacemodified TiO2-MPS, the WCA rapidly declined. Handsheets with surface-modified TiO2-MPS have a rougher surface compared to the handsheets without chemicals and handsheets with unmodified TiO2. This roughness made the handsheet hydrophobic. The handsheet with 12.34% (w/w) unmodified TiO2 has a smoother surface than the control handsheet. Energy-dispersive X-ray spectroscopy (EDS) analysis shows that the handsheet with 12.34% (w/w) unmodified TiO2 contained titanium, while the handsheet with 12.34% (w/w) surface-modified TiO2-MPS contained both titanium and silicon. Generally, the physical properties of handsheets improved with surface-modified TiO2- MPS, especially grammage, bulk thickness, tensile index, and water absorptiveness, which showed statistically significant differences across treatments. The tear index did not differ between treatments.
Journal articles
Magazine articles
Sulfur makeup in an unbleached kraft pulp mill, TAPPI Journal August 2024
ABSTRACT: Sodium sesquisulfate or “sesqui” (Na3H(SO4)2) is a by-product of chlorine dioxide production at kraft pulp mills. It is typically used for sodium and sulfur makeup in the liquor loop. Mondi Hinton Inc. (MHI) in Hinton, AB, Canada, was converting from bleached to unbleached kraft pulp production and was thus losing this source of makeup. The only option that was readily available as a substitute was sodium hydrosulfide (NaHS), which was cost prohibitive. Other options such as sodium sulfate (Na2SO4), emulsified sulfur, sulfuric acid (H2SO4), and sodium bisulfite (NaHSO3) were compared. The mill concluded that pelletized sulfur plus sodium hydroxide or “caustic soda” (NaOH) was the best option. Laboratory-scale experiments showed that pelletized sulfur dissolved in white liquor (WL). A mill-scale trial revealed that pelletized sulfur added to a causticizer had no adverse impacts on the downstream pressure filters or kiln operation. The sulfur reacted to produce polysulfide upstream of the WL storage tank, giving the liquor an orange hue. This polysulfide appeared to partially degrade into thiosulfate before being fed to the digester. The heavy black liquor (HBL) sulfur:sodium (S:Na) ratio did not change significantly, even though the sulfur/soda addition location was upstream of the original one. In addition, other properties such as liquor heating value and elemental analysis did not significantly change. Due to polysulfide/thiosulfate concentration in the white liquor, it was determined that the carbon steel equipment was at risk for corrosion. During the annual turnaround that occurred eight months after the addition of sulfur was started, the wash zone of the digester showed no signs of thinning/damage. The mill has been running exclusively with pelletized sulfur for 22 months (as of August 2024), realizing significant cost savings compared to the use of NaHS or other sulfur/soda addition options.
Journal articles
Magazine articles
The role of hornification in the deterioration mechanism of physical properties of unrefined eucalyptus fibers during paper recycling, TAPPI Journal February 2024
ABSTRACT: Physical properties of cellulosic paper deteriorate significantly during paper recycling, which hinders the sustainable development of the paper industry. This work investigates the property deterioration mechanism and the role of hornification in the recycling process of unrefined eucalyptus fibers. The results showed that during the recycling process, the hornification gradually deepened, the fiber width gradually decreased, and the physical properties of the paper also gradually decreased. After five cycles of reuse, the relative bonding area decreased by 17.6%, while the relative bonding force decreased by 1.8%. Further results indicated that the physical property deterioration of the paper was closely related to the decrease of fiber bonding area. The fiber bonding area decreased linearly with the reduction of re-swollen fiber width during paper recycling. Re-swollen fiber width was closely related to the hornification. Hornification mainly reduces the bonding area of unrefined eucalyptus fiber rather than the bonding force. The work elucidates the role of hornification in the recycling process of unrefined eucalyptus fibers and the deterioration mechanism of paper physical properties, which will be helpful to control the property deterioration of paper and achieve a longer life cycle.
Journal articles
Magazine articles
Enhancing tissue wet pressing performance and dry end material efficiency for cost savings, TAPPI Journal May 2024
ABSTRACT: The steadily growing global tissue paper demand lays a foundation for new technologies targeting tissue production optimization, as well as improved material and time efficiency. Tissue making is an especially energy-intensive field of paper industry, creating unique demands for performance in wet pressing and drying processes to cut energy usage. Intelligent roll solutions offer new tools for tissue making to achieve these goals. These tools aim at improving press nip, moisture, and tension profiles; reeling nip and parent roll hardness profiles; rewinder runnability; and end product web handling characteristics in converting. Intelligent rolls can be utilized in all the main processes and positions on tissue production lines. With these tools, production cost reductions and energy savings can be obtained by optimizing the press nip-to-Yankee cylinder contact, avoiding moisture profile errors requiring overdrying with the Yankee hood and reducing reeling/winding broke under low nip load conditions typical to tissue windups. The intelligent roll system consists of a helically mounted force or temperature sensors, roll covers, measurement electronics, digital radio transmission, and a receiver system connected to a user interface or the mill automation system. What distinguishes these implementations is that no layout changes or added external measurement devices are required, helping to fit into compact tissue machine environments, regardless of the equipment type • traditional, hybrid, or through-air drying (TAD) concept. In tissue processing equipment, the optimal positions for these rolls are press nip rollers, reeling cylinders, rewinder or converting line paper lead rolls, or rewinder winding drums. In addition to these, temperature profile measurements are utilized, with the main application being the sheet temperature profile detection after Yankee drying for moisture profile and drying process optimization.
Journal articles
Magazine articles
In-situ green synthesis and adsorption on methylene blue of copper-based metal organic framework/cellulose/chitosan (CCTSA/HKUST-1) composite aerogel, TAPPI Journal October 2024
ABSTRACT: In order to explore the application of metal-organic frameworks (MOFs) in environmental and water treatment fields, a new composite aerogel of HKUST-1/cellulose/chitosan (CCTSA/HKUST-1) with better hydrostability was synthesized by an in-situ synthesis method combining covalent cross-linking and solvothermal methods as an efficient adsorbent for methylene blue (MB). The composite aerogel (CCTSA) obtained by covalent cross-linking of cellulose (CE) and chitosan (CTS) exhibited excellent stability under strong acid and solvent-thermal conditions. With the increase of CTS content, it was beneficial to the in-situ synthesis of HKUST-1, as well as to increase the mass loading rate of HKUST-1 to 37.06%, while the Brunauer-Emmett-Teller (BET) specific surface area of CCTSA/HKUST-1 composite aerogel reached 945.123 m2·g-1, which was much higher than that of the CCTSA composite aerogel (14.489 m2·g-1). The CCTSA/ HKUST-1 composite aerogel exhibited excellent adsorption capacity (537.6 mg·g-1) on MB solution, and cyclic adsorption could be achieved. This study proposes a concept of valorization of alkaline peroxide mechanical pulping (APMP) waste liquor to hemicellulose-based hydrogel. This hemicellulose-based hydrogel exhibits a sensitive temperature/pH dual response. Hemicellulose-based hydrogels swell or shrink through the change of hydrogen bond/electrostatic repulsion/charge screening. They also show good water absorption and water retention properties.