Furnishing autohydrolyzed poplar weakly alkaline P-RC APMP to make lightweight coated base paper, TAPPI Journal February 2022
ABSTRACT: This work investigated the effects of autohydrolysis pretreatment severity on poplar (Populus tomentosa Carr.) woodchips used to make a type of high-yield pulp (HYP) known as preconditioning followed by refiner chemical treatment, alkaline peroxide mechanical pulp (P-RC APMP). It also investigated the ratios for partially replacing sodium hydroxide (NaOH) with magnesium oxide (MgO) in the high-consistency (HC) retention stage of the P-RC APMP process on the obtained HYP’s properties. The results show that the pretreatment severity of autohydrolysis at combined hydrolysis factor (CHF) = 10.77 and the 50 wt% ratio for partially substituting NaOH with MgO were the optimum conditions for making light-weight coated (LWC) base paper. Compared to the conventional P-RC APMP, the optimized P-RC APMP had similar bulk and higher tensile, burst, and tear indices, as well as opacity, but a slightly lower ISO brightness. When the optimized P-RC APMP and commercial softwood bleached sulfate pulp (SBKP) were blended to make LWC base paper, the most favorable pulp furnish was comprised of 50% optimized P-RC APMP and 50% commercial SBKP. The obtained LWC base paper handsheet had better bulk, and its other properties could also meet the require-ments of LWC base paper.
Journal articles
Magazine articles
A true green cover for industrial waste landfills, TAPPI Journal April 2024
ABSTRACT: Greenhouse gas (GHG) emissions in the United States totaled 5,981 million metric tons of carbon dioxide equivalent (MMT CO2eq) in 2020. Of that, GHG emissions by the pulp and paper sector amounted to 35 MMT CO2eq direct emissions and those by industrial waste landfills summed to 7.4 MMT CO2eq direct emissions. Loss of GHG sinks due to change in land use further contributes to the net GHG emissions. Industrial waste landfills are typically required to comply with certain federal and state regulations, including meeting requirements for final cover systems. Conventional final cover systems have included use of soil covers and/or soil-geosynthetic composite covers. An engineered turf cover provides for an excellent “green” alternative final cover system for industrial waste landfills.This paper discusses various sustainability aspects pertaining to use of an engineered turf final cover, including: (i)significantly low carbon footprint associated with the construction of an engineered turf alternative final coverwhen compared to closure using a traditional or prescriptive cover system; (ii) saving valuable soil and land resourc-es; (iii) saving water resources by reduction in its use during and after construction; (iv) reducing impacts associated with borrow areas; and (v) reducing overall carbon footprint. Further, when using an engineered turf cover, opportunities exist for beneficial reuse of land, including development of solar energy. A brief discussion on the potential fordevelopment of solar energy is included.
Journal articles
Magazine articles
Surface modification of TiO2 with MPS and its effects on the wettability and physical properties of Kawayan Kiling (Bambusa vulgaris Schrad ex. Wendl) handsheets, TAPPI Jouranl April 2024
ABSTRACT: The need for hydrophobic papers has steadily increased over past years. These papers are often sought after as packaging materials and have high demand in the food industry and medicine. In this study, various concentrations of surface-modified TiO2-MPS were added to Kawayan Kiling (B. vulgaris) pulp at the wet-end section of handsheet formation. Surface-modified TiO2-MPS was made from nano-titanium (IV) oxide using 3-(trimethoxysilyl)propyl methacrylate as a coupling agent. The wettability of handsheets and physical properties were tested using various standard methods. Results reveal that the handsheets without surface-modified TiO2-MPS had the lowest water contact angle (WCA), while the handsheet with 12.34% (w/w) surface-modified TiO2-MPS had the highest WCA. At 17% (w/w) surfacemodified TiO2-MPS, the WCA rapidly declined. Handsheets with surface-modified TiO2-MPS have a rougher surface compared to the handsheets without chemicals and handsheets with unmodified TiO2. This roughness made the handsheet hydrophobic. The handsheet with 12.34% (w/w) unmodified TiO2 has a smoother surface than the control handsheet. Energy-dispersive X-ray spectroscopy (EDS) analysis shows that the handsheet with 12.34% (w/w) unmodified TiO2 contained titanium, while the handsheet with 12.34% (w/w) surface-modified TiO2-MPS contained both titanium and silicon. Generally, the physical properties of handsheets improved with surface-modified TiO2- MPS, especially grammage, bulk thickness, tensile index, and water absorptiveness, which showed statistically significant differences across treatments. The tear index did not differ between treatments.
Journal articles
Magazine articles
Sulfur makeup in an unbleached kraft pulp mill, TAPPI Journal August 2024
ABSTRACT: Sodium sesquisulfate or “sesqui” (Na3H(SO4)2) is a by-product of chlorine dioxide production at kraft pulp mills. It is typically used for sodium and sulfur makeup in the liquor loop. Mondi Hinton Inc. (MHI) in Hinton, AB, Canada, was converting from bleached to unbleached kraft pulp production and was thus losing this source of makeup. The only option that was readily available as a substitute was sodium hydrosulfide (NaHS), which was cost prohibitive. Other options such as sodium sulfate (Na2SO4), emulsified sulfur, sulfuric acid (H2SO4), and sodium bisulfite (NaHSO3) were compared. The mill concluded that pelletized sulfur plus sodium hydroxide or “caustic soda” (NaOH) was the best option. Laboratory-scale experiments showed that pelletized sulfur dissolved in white liquor (WL). A mill-scale trial revealed that pelletized sulfur added to a causticizer had no adverse impacts on the downstream pressure filters or kiln operation. The sulfur reacted to produce polysulfide upstream of the WL storage tank, giving the liquor an orange hue. This polysulfide appeared to partially degrade into thiosulfate before being fed to the digester. The heavy black liquor (HBL) sulfur:sodium (S:Na) ratio did not change significantly, even though the sulfur/soda addition location was upstream of the original one. In addition, other properties such as liquor heating value and elemental analysis did not significantly change. Due to polysulfide/thiosulfate concentration in the white liquor, it was determined that the carbon steel equipment was at risk for corrosion. During the annual turnaround that occurred eight months after the addition of sulfur was started, the wash zone of the digester showed no signs of thinning/damage. The mill has been running exclusively with pelletized sulfur for 22 months (as of August 2024), realizing significant cost savings compared to the use of NaHS or other sulfur/soda addition options.
Journal articles
Magazine articles
Next generation dry strength additives: Leveraging on-site synthesis to develop high performance glyoxalated polyacrylamides, TAPPI Journal January 2024
ABSTRACT: Although glyoxalated polyacrylamides (gPAMs) have been described since the 1950s, the freedom to design new materials based on this chemistry has been limited by practical concerns; namely, a balance between solution concentration and material characteristics must be met to make the economics of gPAM strength additives work for the paper industry. For traditional “delivered” gPAMs, only a very narrow range of polyacrylamide molecular weights and compositions could be considered for glyoxalation. However, the development and successful implementation of automated reactor equipment that allows for the synthesis of gPAMs from glyoxal and polyacrylamide copolymers at the mill, known as “on-site” glyoxalation, obviates the shipping and stability concerns that have traditionally held back gPAM development. As such, on-site generators represent a platform that enables the glyoxalation of materials that would otherwise not have been suitable for use in a traditionally delivered gPAM product. These on-site generators therefore open new avenues for polymer design to allow for the creation of the next generation of strength additives. By leveraging the synthetic freedom of the on-site generators, a suite of high performance gPAMs has been designed, yielding materials that provide both exceptional strength and drainage performance in poor quality furnishes.
Journal articles
Magazine articles
Effects of different soda loss measurement techniques on brownstock quality, TAPPI Journal July 2024
ABSTRACT: The efficiency of the kraft recovery plant, bleaching process, and paper machine are affected when black liquor carryover from the brownstock washers is not controlled well. Measuring soda loss within a mill can vary from using conductivity, either in-situ or with a lab sample of black liquor filtrate squeezed from the last stage washer, to measuring absolute sodium content with a lab sodium specific ion probe or spectrophotometer. While measuring conductivity has value in tracking trends in black liquor losses, it is not an acceptable method in reporting losses in absolute units, typically in lb/ton of pulp. This is further complicated when trying to benchmark soda loss performance across a fleet of mills with multiple washer lines. Not only do the testing methods vary, but the amount of bound soda on high kappa pulps can be significant. This variability creates inconsistent results, and studies are needed to understand the effect of different testing methods on the pulp quality. In this study, soda loss is expressed as sodium sulfate (Na2SO4). Four different methods to measure soda content in pulp off commercial brownstock washers were studied: full digestion (FD), washing soaking overnight and washing (WSW), soaking in boiling water and stirring 10-min (SW-10), and squeeze-no wash (Sq). Total, washable, and bound sodium sulfate calculations were determined for each soda content measuring technique using inductively coupled plasma-optical emission spectroscopy (ICP-OES). Results showed bound and washable sodium sulfate amounts significantly depend on which soda measurement technique was used. In addition, the soda results were correlated with the pulp kappa numbers. As the kappa number increases, bound soda increases, regardless of the soda measurement method used. Impacts of high sodium sulfate in brownstock are also discussed.
Journal articles
Magazine articles
Enhancing tissue wet pressing performance and dry end material efficiency for cost savings, TAPPI Journal May 2024
ABSTRACT: The steadily growing global tissue paper demand lays a foundation for new technologies targeting tissue production optimization, as well as improved material and time efficiency. Tissue making is an especially energy-intensive field of paper industry, creating unique demands for performance in wet pressing and drying processes to cut energy usage. Intelligent roll solutions offer new tools for tissue making to achieve these goals. These tools aim at improving press nip, moisture, and tension profiles; reeling nip and parent roll hardness profiles; rewinder runnability; and end product web handling characteristics in converting. Intelligent rolls can be utilized in all the main processes and positions on tissue production lines. With these tools, production cost reductions and energy savings can be obtained by optimizing the press nip-to-Yankee cylinder contact, avoiding moisture profile errors requiring overdrying with the Yankee hood and reducing reeling/winding broke under low nip load conditions typical to tissue windups. The intelligent roll system consists of a helically mounted force or temperature sensors, roll covers, measurement electronics, digital radio transmission, and a receiver system connected to a user interface or the mill automation system. What distinguishes these implementations is that no layout changes or added external measurement devices are required, helping to fit into compact tissue machine environments, regardless of the equipment type • traditional, hybrid, or through-air drying (TAD) concept. In tissue processing equipment, the optimal positions for these rolls are press nip rollers, reeling cylinders, rewinder or converting line paper lead rolls, or rewinder winding drums. In addition to these, temperature profile measurements are utilized, with the main application being the sheet temperature profile detection after Yankee drying for moisture profile and drying process optimization.
Journal articles
Biphasic 1-butanol/water delignification of miscanthus for manufacturing papermaking pulp, TAPPI Journal August 2026
ABSTRACT: Miscanthus has emerged as a promising nonwoody fiber source for papermaking and fiber molding as the world has sought alternatives to wood-based products. A diverse range of chemistries have been explored at the laboratory scale to turn nonwoody biomass into fibers; however, few have been successful at pilot or commercial scales. An emerging organosolv delignification chemistry that has demonstrated previous technical success is butanol/water, having been shown to produce papers with similar properties to other, more conventional chemistries, but offering the benefit of a built-in sugar and lignin coproduct separation. While a range of fiber lengths were achieved (0.45•0.95 mm), addition of sodium hydroxide (NaOH) to the butanol/water delignification chemistry resulted in fiber lengths comparable to commercially available hardwood pulps (0.7•1.0 mm). Lignin concentration was reduced from 19.1 wt% in the raw miscanthus to under 3.5 wt% for most trials. The lowest lignin concentration (2.5 wt%) was achieved at 180°C for 180 min with 50:50 butanol:water and 2 wt% acetic acid. Yet, the high severity of this condition (and similar ones) resulted in a significant truncation of fiber length, which is detrimental for papermaking applications. The highest quality pulp for papermaking was generated at 180°C for 180 min with 50:50 butanol:water and 10 wt% NaOH. This pulp had one of the longest fiber lengths, the highest brightness, and the highest hemicellulose concentration. Thus, butanol/water delignification, especially with NaOH addition, resulted in the successful production of cellulose-rich pulps that have potential in commercial papermaking and fiber molding applications.
Journal articles
Alternative disposal methods for pulp mill biosludge
ABSTRACT: The chemical pulp production process produces notable amounts of biosludge, mostly in the wastewater treatment system. Biosludge is a problematic waste stream due to its properties, and recently, its amounts have been on the increase. The most used disposal processes are incineration in a bark boiler or a recovery boiler now that landfilling is no longer permitted by legislation in many countries. Incineration of wet sludges with poor drying characteristics decreases the energy efficiency of the process. Biosludge is typically mixed with black liquor in the evaporation plant before feeding to the recovery boiler. Although the recovery boiler is designed to handle challenging fuels, biosludge disposal requires consideration of its behavior during evaporation and accumulation of non-process elements in the recovery cycle. This study discusses the currently used sludge handling methods and presents two novel methods, hydrothermal carbonization and anaerobic digestion, to convert sludge into a usable form. Production of hydrochar or biogas offers new usage possibilities for biosludge and improves the energy efficiency of the mill when the new methods replace incineration. The processes are still developing, and thus their economic feasibility is uncertain; however, depending on the case details, they can be considered promising alternatives to be implemented in the future.
Journal articles
Effects of calcium on sodium salt scaling with the presence of resin acids and fatty acids, TAPPI Journal June 2026
ABSTRACT: Reintroducing tall oil soap or its related products into high dry solids black liquor has been found to reduce sodium salt scaling in falling film evaporators. Aside from resin acids and fatty acids, which are the likely scale inhibitors, calcium is reintroduced into black liquor because of the relatively high calcium content of tall oil soap. One concern is that this increase in calcium content might lead to the formation of additional calcium and sodium scales in evaporators. In this work, we investigated the relationship among trace amounts of calcium, sodium salts, resin acids, and fatty acids in a controlled system using a model salt solution and a benchtop setup. We studied the effects of the calcium carbonate addition and calcium carbonate scales on sodium salt scaling in the presence of resin acids and fatty acids. We found that some calcium carbonate is incorporated in the precipitated sodium crystals, and the suspended sodium crystals become larger and more compact with increasing calcium carbonate concentration. Experiments in the benchtop setup show that precipitating calcium carbonate scale on the heat exchanger does not lead to a higher rate of sodium salt scaling. The solubility of calcium carbonate is not affected by the addition of resin acids and fatty acids. These findings indicate that the reduction in sodium salt scaling through the addition of tall oil soap is primarily related to resin acids and fatty acids, rather than to calcium or to interactions between calcium and mixtures of resin and fatty acids.