A guide to eliminating baggy webs, TAPPI Journal June 2021
ABSTRACT: Slack or baggy webs can cause misregistration, wrinkles, and breaks in printing and converting operations. Bagginess appears as non-uniform tautness in the cross direction (CD) of a paper web. The underlying cause is uneven CD tension profiles, for which there are few remedies once the paper is made. Precision measurements of CD tension profiles combined with trials on commercial paper machines have shown that uniform CD distribution of moisture, basis weight, and caliper profiles at the reel are key to avoiding bagginess. However, the most important but infrequently measured factor is the CD moisture profile entering the dryer section. Wetter areas entering the dryers are permanently elongated more than dry areas, leading to greater slackness in the finished paper. In storage, wound-in tension can amplify baggy streaks in paper near the surface of a roll and adjacent to the core. Unwrapped or poorly wrapped rolls exposed to low humidity environments may have baggy centers caused by moisture loss from the roll edges.All of the factors that impact bagginess have been incorporated in a mathematical model that was used to interpret the observations from commercial trials and can be used as a guide to solve future problems.
Journal articles
Magazine articles
Understanding extensibility of paper: Role of fiber elongation and fiber bonding, TAPPI Journal March 2020
ABSTRACT: The tensile tests of individual bleached softwood kraft pulp fibers and sheets, as well as the micro-mechanical simulation of the fiber network, suggest that only a part of the elongation potential of individual fibers is utilized in the elongation of the sheet. The stress-strain curves of two actual individual pulp fibers and one mimicked classic stress-strain behavior of fiber were applied to a micromechanical simulation of random fiber networks. Both the experimental results and the micromechanical simulations indicated that fiber bonding has an important role not only in determining the strength but also the elongation of fiber networks. Additionally, the results indicate that the shape of the stress-strain curve of individual pulp fibers may have a significant influence on the shape of the stress-strain curve of a paper sheet. A large increase in elongation and strength of paper can be reached only by strengthening fiber-fiber bonding, as demonstrated by the experimental handsheets containing starch and cellulose microfibrils and by the micromechanical simulations. The key conclusion related to this investigation was that simulated uniform inter-fiber bond strength does not influence the shape of the stress-strain curve of the fiber network until the bonds fail, whereas the number of bonds has an influence on the activation of the fiber network and on the shape of the whole stress-strain curve.
Journal articles
Magazine articles
In-process detection of fiber cutting in low consistency ref
In-process detection of fiber cutting in low consistency refining based on measurement of forces on refiner bars, TAPPI JOURNAL April 2017
Journal articles
Commissioning Brownstock Washing Controls for an Evaporator Limited Mill
An automated shower water control system has been implemented to reduce the volume and vari-ability of weak black liquor being sent from the pulp mill to the evaporators. The washing controls attempt to bal-ance the need for consistent and low soda carryover to the bleach plant with consistently high weak black liquor solids being sent to the evaporators. The washer controls were implemented on two bleachable grade hardwood lines (one with oxygen delignification, one without oxygen delignification) and one pine line. Implementation of the con-trol program resulted in an increase in black liquor solids of 0.6 percentage points for the hardwood lines. Significant foam reduction was realized on the pine line since the pine black liquor solids were able to be consistently maintained just below the soap separation point. Low black liquor solids excursions to the evaporators were eliminated. Bleach plant carryover was stabilized and no negative impact on chemical consumption was noticed when control-ling weak black liquor solids to recovery.
Journal articles
Magazine articles
Mechanical modification of softwood pulp fibers using a novel lightweight vertical bar plate, TAPPI Journal April 2021
ABSTRACT: Refiner plates made using sand casting have a draft angle, which results in a trapezoidal bar shape. These trapezoidal bar plates have a limited throughput compared to the vertical bar plates, and eventually the edges of the bars become dull, resulting in longer time to reach the target freeness and shorter service life. The new light-weight refiner plate with a bar insertion method into a plate base was developed by selecting an aluminium-based alloy as the plate base material and a stainless steel alloy with high wear resistance as the bar material. The light-weight plate with sharp bar edges was very effective in reducing refining energy by reaching the target freeness faster than the sand-cast bar plate. Finally, the lightweight sharp bar plate, which weighed only about half the weight of the cast bar plate, was expected to significantly contribute to easy replacement, improved paper quality, and larger throughput without excessive loss of fiber length.
Journal articles
Examination of the potential to reduce water application rat
Examination of the potential to reduce water application rates for hardwood pulp logs stored in wet decks, TAPPI JOURNAL August 2016
Journal articles
Alkyl ketene dimer (AKD) sizing of paper under simplified tr
Alkyl ketene dimer (AKD) sizing of paper under simplified treatment conditions, TAPPI JOURNAL August 2016
Journal articles
Magazine articles
A case study review of wood ash land application programs in North America, TAPPI Journal February 2021
ABSTRACT: Several regulatory agencies and universities have published guidelines addressing the use of wood ash as liming material for agricultural land and as a soil amendment and fertilizer. This paper summarizes the experiences collected from several forest products facility-sponsored agricultural application programs across North America. These case studies are characterized in terms of the quality of the wood ash involved in the agricultural application, approval requirements, recommended management practices, agricultural benefits of wood ash, and challenges confronted by ash generators and farmers during storage, handling, and land application of wood ash.Reported benefits associated with land-applying wood ash include increasing the pH of acidic soils, improving soil quality, and increasing crop yields. Farmers apply wood ash on their land because in addition to its liming value, it has been shown to effectively fertilize the soil while maintaining soil pH at a level that is optimal for plant growth. Given the content of calcium, potassium, and magnesium that wood ash supplies to the soil, wood ash also improves soil tilth. Wood ash has also proven to be a cost-effective alternative to agricultural lime, especially in rural areas where access to commercial agricultural lime is limited. Some of the challenges identified in the review of case studies include lengthy application approvals in some jurisdictions; weather-related issues associated with delivery, storage, and application of wood ash; maintaining consistent ash quality; inaccurate assessment of required ash testing; potential increased equipment maintenance; and misconceptions on the part of some farmers and government agencies regarding the effect and efficacy of wood ash on soil quality and crop productivity.
Journal articles
Magazine articles
Key material properties in crease cracking of kraft paper, TAPPI Journal February 2021
ABSTRACT: Crease cracking of paperboard is important to control for the appearance and structural integrity of packages. Crease cracking is affected by creasing operation variables, as well as the physical properties of the paperboard. However, the effects of the physical properties are not clearly known. The objectives of this work were to identify the key material properties that affect crease cracking and to clarify the effects of fiber composition and starch. Laboratory sheets were produced from bleached and refined softwood and hardwood commercial pulp at grammage and thicknesses that match a typical paperboard. To mimic papermaking operations, surface starch was applied via a bench-top size press. The sheets were creased in the lab over a range of penetration depths, and reverse-side cracking was measured. The results showed that less reverse-side cracking was correlated with higher tensile post-peak energy, a lower bending stress, and a lower z-direction (ZD) stiffness. The tensile post-peak energy is a measure of the resistance to crack growth via fiber-bridging. The bending force and the ZD stiffness influence the forces that create cracks. It was observed that decreasing the ratio of hard-wood-to-softwood content and reducing the amount of starch would both decrease crease cracking.
Journal articles
Magazine articles
Application of foamed additives to the surface of wet handsheets, TAPPI Journal January 2021
ABSTRACT: We explored the application of foamed wet-end additives onto wet handsheets to qualify our method of application and to demonstrate the method’s usefulness for prescreening additives and foaming agents for packaging applications.We modified a laboratory drawdown coating machine to allow coating of wet handsheets with foamed additives. Initial sheet solids were adjusted to a target of 8%•25% by vacuum. Foam layer thickness was set mechanically. After application, the foamed additives were drawn into the sheet with vacuum. The additive dosage was adjusted by altering its concentration within the foaming formulation. We evaluated more than 100 foaming agents and 10 strength additives, comparing wet-end and foam-assisted addition with no addition on recycled linerboard and virgin linerboard furnish. Foam-assisted addition typically displayed a much steeper dose-response curve and much higher maximum strength levels than wet-end addition. Our results suggest potential target applications for this technology, such as lightweighting, and improved strength performance in mills with relatively closed water systems, where strength aids added into the wet end are adversely influenced by accumulation of inorganic ions and organic species.