Factors affecting deposit formation in foul condensate stripping systems, TAPPI Journal June 2024
ABSTRACT: In kraft pulp mills, foul condensates are often steam-stripped to produce clean condensate for use as process water. The formation of organic deposits in the stripped condensate is a common problem. A systematic study was conducted to examine the deposit composition and the most likely operating parameters responsible for stripped condensate contamination experienced at a kraft mill in Brazil. Daily averaged data of 170 operating parameters over a 15-month period were analyzed by means of multivariate discriminant analysis and random forest classification analysis. The results showed that the deposit formation is related to high temperature, pressure, and dry solids operations in various evaporator effects. These conditions, combined with the poor demisting efficiency in these effects, may have increased black liquor carryover mist in the vapor. Deposit formation also appeared to be related to increased throughput of the foul condensate stripping system and increased pressure in the stripper. Results of Fourier transform infrared spectroscopy (FTIR) and pyrolysis-gas chromatography mass spectrometry (Py-GCMS) analyses show that the deposit consists of mostly organic matter that likely originated from wood extractives and lignin.
Journal articles
Magazine articles
Effect of high sulfate content on viscosity of recovery boiler molten smelt, TAPPI Journal March 2024
ABSTRACT: A systematic study was conducted to examine the effect of high sulfate content on the freezing temperature of molten smelt and how this may contribute to the formation of viscous jellyroll smelt in recovery boilers. The results show that even for recovery boilers with a smelt reduction as low as 70%, the sulfate content in smelt has no or little effect on smelt freezing temperature, and hence, on molten smelt fluidity. The perceived adverse effect of high sulfate content on smelt fluidity and on jellyroll smelt formation comes from the high sulfate content in deposits that have fallen from the upper furnace. Fallen deposits may or may not form jellyroll smelt, depending on whether or not they can melt and be well-mixed with molten smelt by the time they reach the smelt spouts. It is not the high sulfate content in smelt resulting from the low smelt reduction efficiency that makes molten smelt viscous and forms jellyroll smelt, but rather, it is the incomplete melting of fallen deposits that results in one of the proposed mechanisms for jellyroll smelt formation.
Journal articles
Magazine articles
Assessing variation in package modeling, TAPPI Journal April 2021
ABSTRACT: Predictions from empirical models are affected by variability in the input parameters for the data set used to build the models. For corrugated boxes, the difference between actual and modeled compression strength creates a real cost associated with box production, often resulting in boxes that may need to be over-designed to compensate for a lack of model precision. No work to date has attempted to assess the limitation in these compression estimates due to input parameter testing variability. In this paper we approach that problem, initially for the McKee equation and then conceptually for other box models. For our industry to do a better job at meeting the needs of our corrugated packaging customers, we need to reduce the variation in the tests we all rely on, particularly for evaluating material strength (edge crush test [ECT]) and package compression performance (box compression test [BCT]).
Journal articles
Magazine articles
Spraying starch on the Fourdrinier— An option between wet end starch and the size press, TAPPI Journal January 2021
ABSTRACT: Technology to apply suspensions of starch grains to the wet surface of paper, during the dewatering process, is reviewed. Though the technology is not new, it continues to attract the attention of papermakers as a means to increase bonding strength. Starch grains that are sprayed onto the wet-web of paper can be retained at levels exceeding what can be effectively added to the fiber suspension at the wet end. Unlike adding a starch solution at a size press, no additional drying capacity is required on the paper machine. To be effective, the starch needs to be able to swell and develop bonding during the paper drying process. Paperboard applications with recycled fibers appear to be a good fit. There is potential to increase bonding by processes that favor fuller gelatinization of the starch grains by the time the paper becomes dry.
Journal articles
Magazine articles
Investigation on the recycling of sulfuric acid from pretreatment of cellulose for nanocellulose preparation, TAPPI JOURNAL February 2020
ABSTRACT: Sulfuric acid is often used to pretreat cellulose prior to homogenization and conversion to nanocellulose. It would be economically significant to reuse the acid to close the overall value chain loop. The target of this work was to investigate the effect of recovery and recycling frequency of sulfuric acid from the pretreatments on the pretreatment yield of water-insoluble cellulose solid residue, and to explore the relationship between the nanocellulose size prepared by recovery of acid and number of cycles. The surface properties of the nanocelluloses were measured, including content of sulfate groups, absolute zeta potential, crystallinity, and thermal stability.
Journal articles
Magazine articles
On increasing wet-web strength with adhesive polymers, TAPPI JOURNAL February 2020
ABSTRACT: Fiber-fiber adhesion, called “bonding” in the old paper physics literature, is a critical component of the overall strength of dry paper. With freshly formed very wet pulp fiber webs, all evidence suggests there are no fiber-fiber crossings with significant adhesive joint strength. With water removal, a point will be reached where fiber-fiber adhesion starts to contribute to the overall wet-web strength.The literature reveals very few examples of polymers that increase fiber-fiber joint strength in freshly formed webs. Here, we summarize the literature and explain why it is so difficult to promote fiber-fiber wet adhesion with polymers. Nevertheless, ongoing research in areas as diverse as tissue engineering scaffolds and biomimetic adhesives gives clues to future developments. Advances in paper machine engineering have lessened the importance of wet-web strength. By contrast, a critical issue in many of the evolving nanocellulose technologies is the strength of objects first formed by aqueous processing, the green strength—the strength of wet bodies before drying. For exam-ple, 3-D printed nanocellulose objects and ultralow density cellulosic aerogels can be destroyed by capillary forces during drying. There is a need for adhesives that strengthen freshly formed, wet lignocellulosic joints.
Journal articles
Magazine articles
Effects of different ammonium lignosulfonate contents on the crystallization, rheological behaviors, and thermal and mechanical properties of ethylene propylene diene monomer/polypropylene/ammonium lignosulfonate composites, TAPPI Journal January 2020
ABSTRACT: Thermoplastic elastomer (TPE), made from ethylene propylene diene monomer (EPDM) and polypropylene (PP) based on reactive blending, has an excellent processing performance and characteristics and a wide range of applications. However, there are currently no reports in the literature regarding the usage of TPE in making composite boards. In this paper, EPDM, PP, and ammonium lignosulfonate (AL) were used as the raw materials, polyethylene wax was used as the plasticizer, and a dicumyl peroxide vulcanization system with dynamic vulcanization was used to make a new kind of composite material. This research studied the influences of the AL contents on the crystallization behaviors, rheological properties, thermal properties, and mechanical properties of the composites. The results showed that the AL content had a noticeable impact on the performance of the composite board. Accordingly, this kind of composite material can be used as an elastomer material for the core layer of laminated flooring.
Journal articles
Magazine articles
Synthesis of filtrate reducer from biogas residue and its application in drilling fluid, TAPPI Journal March 2020
ABSTRACT: Biogas residues (BR) containing cellulose and lignin are produced with the rapid development of biogas engineering. BR can be used to prepare the filtrate reducer of water-based drilling fluid in oilfields by chemical modification. BR from anaerobically fermenting grain stillage was alkalized and etherified by caustic soda and chloroacetic acid to prepare filtrate reducer, which was named as FBR. The long-chain crystalline polysaccharides were selected as dispersing agents (DA), and the water-soluble silicate was used as the cross-linking agent. After the hot rolling of FBR in saturated saltwater base mud for 16 h at 120°C, the filtration loss was increased from 7.20 mL/30 min before aging to 8.80 mL/30 min after aging. Compared with the commercial filtrate reducers, FBR had better tolerance to high temperature and salt, and lower cost.
Journal articles
Magazine articles
Fundamental understanding of removal of liquid thin film trapped between fibers in the paper drying process: A microscopic approach, TAPPI Journal May 2020
ABSTRACT: In the fabrication of paper, a slurry with cellulose fibers and other matter is drained, pressed, and dried. The latter step requires considerable energy consumption. In the structure of wet paper, there are two different types of water: free water and bound water. Free water can be removed most effectively. However, removing bound water consumes a large portion of energy during the process. The focus of this paper is on the intermediate stage of the drying process, from free water toward bound water where the remaining free water is present on the surfaces of the fibers in the form of a liquid film. For simplicity, the drying process considered in this study corresponds to pure convective drying through the paper sheet. The physics of removing a thin liquid film trapped between fibers in the paper drying process is explored. The film is assumed to be incompressible, viscous, and subject to evaporation, thermocapillarity, and surface tension. By using a volume of fluid (VOF) model, the effect of the previously mentioned parameters on drying behavior of the thin film is investigated.
Journal articles
Magazine articles
Pigmented aqueous barrier coatings, TAPPI Journal November 2020
ABSTRACT: The desire for more sustainable packaging has led to the development of new packaging materials that are fiber based. Aqueous coatings are a pathway to improve the recyclability of these materials. Pigments used in these coatings can improve the performance of the coating and reduce cost while further improving the recyclability. Mineral pigments are also considered to be compost neutral. In this paper, we provide the reader a better fundamental understanding of the mechanisms by which pigments work in barrier coatings. A pigment’s mineralogy and physical characteristics are important to how it will perform, and there have been recent pigment developments that improve coating performance. This paper shows that some pigments are better than others in particular barrier applications. Also, pigmented base or pre-coats can be used to prepare the surface for more highly functional coatings that go on top, improving the barrier function of packaging material and reducing overall cost. Finally, the converting operation is of major importance in driving formulation choices for barrier applications.