Research on flame-retardant paper prepared by the method of in-pulp addition of ammonium polyphosphate, TAPPI Journal May 2023

ABSTRACT: At present, the production of flame-retardant paper usually uses the impregnation method of phosphorus-nitrogen flame retardants in paper. There are few reports on the application of an in-pulp addition method. In this paper, the solubility of ammonium polyphosphate (APP) and its effect on flame-retardant paper were investigated for use in an in-pulp addition method. It was found that APP particles were square, with an average particle size of 21.88 µm. The particle size decreased significantly after immersion in water at 25°C for 24 h. Furthermore, most of the APPs were dissolved after immersion in water at 90°C for 0.5 h, and the residuals agglomerated and their shape turned into an amorphous form. The APP possessed strong electronegativity and could partially ionize in water. The solubility of APP was 0.18 g/100 mL water at 25°C and increased quickly when the temperature was higher than 30°C. Therefore, APP should be added to the pulp at temperatures below 30°C. The tensile strength of the paper initially increased with the addition of APP, and it reached the maximum value when the APP content was 10% and then gradually decreased. The limiting oxygen index (LOI) value of the paper was 28.7% when the added amount of APP was 30% and cationic polyacrylamide (CPAM) was 0.08%, reaching the flame-retardant level.

Over the Wire, Paper360º May/June 2023

Paper Mill Saves 30 Percent on Maintenance with LTSA, Paper360º May/June 2023

TAPPI Journal Summaries, Paper360º May/June 2023

TAPPI Journal Summaries, Paper360º May/June 2023

A method to produce paperboard with a lightweight low-density coating, TAPPI Journal November 2025

ABSTRACT: In this work, a method is described in which a coating layer is produced that consists of a network of bubble-shaped air-filled voids within the coating. This is accomplished by instantaneously flash-drying all the water in the coating as it exits the application nip. The nip is formed between a polished chrome drum and a deformable press roll. The combination of the drum temperature, nip pressure, and nip width allow for sufficient energy to be transferred to the coating to completely flash-dry the coating material. The pressure within the nip is sufficient to allow the coating to superheat within the nip, then flash boil as it exits the nip. This boiling effect and resulting expansion are constrained by the roll surface, resulting in a coated surface that mirrors the polished chrome surface. The coating immobilizes while in the process of boiling, which preserves the bubble structure. With a coat weight of 5 g/m2, a flat, smooth surface is produced. This process was scaled up to a mill production machine layout and run at speeds as high as 450 m/min.

Pre-damping effects on water absorption and drying dynamics in flexographic printing, TAPPI Journal November 2025

ABSTRACT: Optimizing flexographic printability can involve the ink and the substrate, as well as the printing process. It has been widely reported in the literature that controlling topography of the substrate and its porosity are vital for good flexographic printability, especially when using water-based inks. This study focuses on how pre-damping a surface impacts liquid absorption and improves wet trapping (ink on ink with no intermediate drying) in flexographic printing. A Prüfbau universal print tester was adapted to analyze flexographic wet-on-wet ink printing and trapping using yellow and magenta inks for contrast. Slow drying of the first ink layer (yellow) leads to mottle when the second layer (magenta) is applied. The study explores the “wet sponge” hypothesis: a pre-damped surface should absorb liquid faster. The Lucas- Washburn equation describes long-term absorption, but it does not capture short-term uptake, which instead follows a linear dependence on time.