Journal articles
Magazine articles
Cationic emulsions of maleic anhydride derivatives of oleic and abietic acid for hydrophobic sizing of paper, TAPPI Journal 2020
ABSTRACT: Ordinary rosin sizing agents are mixtures of resin acids that include abietic acid and related compounds obtained from softwoods such as pine. Fatty acids, which are another byproduct of the kraft pulping of soft-wood species, also may have hydrophobic effects, but their use as sizing agents has seldom been considered. In the current study, abietic acid and oleic acid, in the absence of other components, were first modified by reaction with maleic acid anhydride. Then, the maleated derivatives (maleated oleic acid [MOA] and maleated abietic acid [MAA]), which were emulsified with cationic starch at the 1:1 and 3:2 ratio, respectively, were added to fiber furnish containing aluminum sulfate (papermaker’s alum). The prepared sheets were dried with a rotating drum on one side at 100°C at low pressure to cure the sizing agents. The chemical, optical strength, and absorption properties were measured. The presence of the sizing material was confirmed using time of flight secondary ion mass spectrometry (ToF-SIMS), and the retention of the sizing agent on fibers was supported by evidence of hydrocarbons on the paper surface. In addition to achieving sufficient water resistance features with MAA, a lesser hydrophobic character was obtained when using MOA. Compared to commercial applications, relatively large amounts of sizing agent were used to obtain a sufficient sizing degree. The MOA required 5% addition to achieve a similar sizing degree as MAA at the 2% level. The sizing treatments also resulted in substantial increases in tensile index value. Since cationic starch was used in the formulation of the sizing agents, the increase in tensile index may have been due to the influence of cationic starch. Contributions to paper strength from a combination of ionic complexation and mutual association of hydrophobic groups is also proposed. Depending on the amount of sizing agent, the yellowness increased, especially when sizing with MOA.
Journal articles
Allocation of carbon dioxide emissions from key production steps in high-grade paper mills, TAPPI JOURNAL August 2013
Allocation of carbon dioxide emissions from key production steps in high-grade paper mills, TAPPI JOURNAL August 2013
Journal articles
Characterization of printed offset ink layers on printing papers using fractal analysis, TAPPI JOURNAL May 2012
Characterization of printed offset ink layers on printing papers using fractal analysis, TAPPI JOURNAL May 2012
Journal articles
Optical and photocatalytic properties of photoactive paper with polycrystalline TiO2 nanopigment for optimal product design, TAPPI JOURNAL May 2012
Optical and photocatalytic properties of photoactive paper with polycrystalline TiO2 nanopigment for optimal product design, TAPPI JOURNAL May 2012
Journal articles
AOX Content of Paper Manufactured with 'Chlorine Free' Pulps
AOX Content of Paper Manufactured with 'Chlorine Free' Pulps, 1995 Papermakers Conference Proceedings
Journal articles
A method to produce paperboard with a lightweight low-density coating, TAPPI Journal November 2025
ABSTRACT: In this work, a method is described in which a coating layer is produced that consists of a network of bubble-shaped air-filled voids within the coating. This is accomplished by instantaneously flash-drying all the water in the coating as it exits the application nip. The nip is formed between a polished chrome drum and a deformable press roll. The combination of the drum temperature, nip pressure, and nip width allow for sufficient energy to be transferred to the coating to completely flash-dry the coating material. The pressure within the nip is sufficient to allow the coating to superheat within the nip, then flash boil as it exits the nip. This boiling effect and resulting expansion are constrained by the roll surface, resulting in a coated surface that mirrors the polished chrome surface. The coating immobilizes while in the process of boiling, which preserves the bubble structure. With a coat weight of 5 g/m2, a flat, smooth surface is produced. This process was scaled up to a mill production machine layout and run at speeds as high as 450 m/min.
Journal articles
Pre-damping effects on water absorption and drying dynamics in flexographic printing, TAPPI Journal November 2025
ABSTRACT: Optimizing flexographic printability can involve the ink and the substrate, as well as the printing process. It has been widely reported in the literature that controlling topography of the substrate and its porosity are vital for good flexographic printability, especially when using water-based inks. This study focuses on how pre-damping a surface impacts liquid absorption and improves wet trapping (ink on ink with no intermediate drying) in flexographic printing. A Prüfbau universal print tester was adapted to analyze flexographic wet-on-wet ink printing and trapping using yellow and magenta inks for contrast. Slow drying of the first ink layer (yellow) leads to mottle when the second layer (magenta) is applied. The study explores the “wet sponge” hypothesis: a pre-damped surface should absorb liquid faster. The Lucas- Washburn equation describes long-term absorption, but it does not capture short-term uptake, which instead follows a linear dependence on time.
Journal articles
Water and grease resistance of paperboard coated with long chain cellulose fatty acid esters using electrostatic powder coating, TAPPI Journal April 2026
ABSTRACT: Fiber-based materials used for foodservice, takeaway, and other packaging applications must typically provide water and grease resistance. Simultaneously, there is growing interest towards bio-based and renewable barrier coatings. In this study we applied thermoplastic long chain fatty acid cellulose esters onto paperboard using electrostatic powder coating to create barrier properties of interest. Electrostatic powder coating provides a water-free process to tackle moisture-induced quality issues and to provide an even coating layer. Cellulose octanoate and palmitate esters were produced in pilot scale. These were ground into fine particles using liquid nitrogen and applied onto paperboard sheets using an electrostatic powder gun. The loosely packed coatings were fixed and fused onto the paperboard by hot pressing. We characterized the coated sheets for coating thickness, contact angles with water, water absorption, grease resistance (KIT), and olive oil barrier. Two commercial polyethylene powders were used as references. Our results indicated that the long chain cellulose fatty acid ester coatings were thermoplastic and hydrophobic with contact angles above 100°. Water absorption was similar to the reference coatings. While grease resistance was lower than with the references, the cellulose ester coatings slowed down diffusion of olive oil through the paperboard. Cellulose octanoate ester with a lower melt viscosity already provided smooth coatings after the initial hot pressing step, while in most cases, the second post hot pressing step further improved the barrier properties.
Journal articles
Point load measurements on paperboard packages and bulging, TAPPI Journal March 2026
ABSTRACT: Paperboard packaging is made by processing board materials into sheets or rolls and shaping them through creasing, cutting, folding, and erecting. The conversion process generates residual moments at the folds that cause panel bulging. This study experimentally investigates how the bulging introduced during the converting processes influence the mechanical response of paperboard packages during point load testing within the elastic deformation range. The study shows that panel bulging may significantly affect packaging performance as-perceived strength and stiffness. Bulging, influenced by the board’s basis weight, can affect the package performance even more than packaging stiffness. Point load tests in the elastic region were performed on empty packages (78 mm × 50 mm × 110 mm) with force applied at specific points along their long sides. The packages evaluated in this study were made of two identically processed materials of different grammages. The heavier material showed more pronounced bulging than the lighter one, leading to overlapping force-displacement curves for the packages, and to that, a lower force and stiffness may be measured at a certain indentation depth for the package of heavier material. This complicates material choice according to functional requirements. The results show that a highly bulged package might resemble one with less bulging of another material. According to the results, it is not certain that a higher grammage package shows a higher indentation force and stiffness than a lower grammage package when measured at a certain indentation. This indicates that optimizing the creasing and folding processes can be a way to enhance performance rather than simply increasing board weight. The study underscores the importance of controlling converting parameters, especially creasing and folding behavior. Well-performed creasing and folding gives a low residual momentum, little bulging, and a high stiffness and compression strength at point loading in the elastic region. Proper optimization can improve packaging performance and manual handling user-friendliness.
Journal articles
Magazine articles
Flow rheology of light foams generated from aqueous solutions of polyvinyl alcohol, TAPPI Journal January 2023
ABSTRACT: Recent studies have shown that foam-assisted application of additives into a wet web has advantages over the conventional way of adding the chemicals into the pulp suspension before forming, e.g., increased mechanical retention as well as high dosage giving increased wet strength without impairing the sheet uniformity. To engineer processes utilizing this new technology, the complex flow behavior of applied foams must be quantified. At the minimum, the foam viscosity and the slip velocity at the solid surfaces need to be known to build practical models that can be used in analyzing and upscaling unit processes of the foam-assisted application.In this study, the rheological behavior was quantified for foams having polyvinyl alcohol (PVOH), a widely used strength additive chemical, as the surfactant. The foam density was varied between 100 g/L and 300 g/L, and the concentration of the PVOH solution was varied between 0.5% and 6.0% (w/w). The foams were generated with a commercial foam generator, and the rheological properties of the foams were measured by using a horizontal pipe bank. At the outlet from the generator, the volumetric flow rate, the absolute pressure, and the bubble size distribution of the foam were measured. In the measurement pipe section, the viscous pressure gradient and the slip velocity were measured, after which the foam was discharged to ambient air pressure. The viscosity and the dynamic surface tension of the PVOH solutions were quantified with commercial laboratory devices. In the viscosity analysis, the apparent shear rate was calculated from the volumetric flow rate, and the resulting apparent viscosity was translated to real material viscosity data by applying the Weissenberg-Rabinowitsch correction. The results indicated that PVOH foams can be described with high accuracy as shear-thinning power-law fluids where the detailed behavior depends on the foam density and the PVOH concentration. Slip flow, as usual, increased with increasing wall shear stress, but it was also dependent on the PVOH concentration, the air content, and the bubble size. For both the foam viscosity and the slip flow, a correlation was found that described the quantitative behavior of all the studied foams with good accuracy.