A method to produce paperboard with a lightweight low-density coating, TAPPI Journal November 2025
ABSTRACT: In this work, a method is described in which a coating layer is produced that consists of a network of bubble-shaped air-filled voids within the coating. This is accomplished by instantaneously flash-drying all the water in the coating as it exits the application nip. The nip is formed between a polished chrome drum and a deformable press roll. The combination of the drum temperature, nip pressure, and nip width allow for sufficient energy to be transferred to the coating to completely flash-dry the coating material. The pressure within the nip is sufficient to allow the coating to superheat within the nip, then flash boil as it exits the nip. This boiling effect and resulting expansion are constrained by the roll surface, resulting in a coated surface that mirrors the polished chrome surface. The coating immobilizes while in the process of boiling, which preserves the bubble structure. With a coat weight of 5 g/m2, a flat, smooth surface is produced. This process was scaled up to a mill production machine layout and run at speeds as high as 450 m/min.
Journal articles
Pre-damping effects on water absorption and drying dynamics in flexographic printing, TAPPI Journal November 2025
ABSTRACT: Optimizing flexographic printability can involve the ink and the substrate, as well as the printing process. It has been widely reported in the literature that controlling topography of the substrate and its porosity are vital for good flexographic printability, especially when using water-based inks. This study focuses on how pre-damping a surface impacts liquid absorption and improves wet trapping (ink on ink with no intermediate drying) in flexographic printing. A Prüfbau universal print tester was adapted to analyze flexographic wet-on-wet ink printing and trapping using yellow and magenta inks for contrast. Slow drying of the first ink layer (yellow) leads to mottle when the second layer (magenta) is applied. The study explores the “wet sponge” hypothesis: a pre-damped surface should absorb liquid faster. The Lucas- Washburn equation describes long-term absorption, but it does not capture short-term uptake, which instead follows a linear dependence on time.
Journal articles
AOX Content of Paper Manufactured with 'Chlorine Free' Pulps
AOX Content of Paper Manufactured with 'Chlorine Free' Pulps, 1995 Papermakers Conference Proceedings
Journal articles
Xylanase Treatment for the Bleaching of Softwood Kraft Pulps
Xylanase Treatment for the Bleaching of Softwood Kraft Pulps: The Effect of Chlorine Dioxide Substitution, 1992 Pulping Conference Proceedings
Journal articles
Magazine articles
Comparative study of guar gum and its cationic derivatives as pre-flocculating polymers for PCC fillers in papermaking applications, TAPPI Journal April 2022
ABSTRACT: In this work, gums from guar seeds were evaluated as a potential precipitated calcium carbonate (PCC) filler pre-flocculant to induce functional filler in papermaking applications. In recent years, guar has been conidered one of the promising wet-end additives due to its abundance, rich source of hemicellulose content, and bio-degradability. However, application of guar gum in filler pretreatment methods for producing high ash paper has scarcely been reported. In this paper, the flocculating ability of three types of guar gum was established with charge analysis and turbidity (NTU) of the system at 1% and 5% for each gum: native gum (NG) having a degree of substitution (DS) of 0, and cationic gums having a DS value of 0.07 (CL) and 0.15 (CH). It was interesting to observe that even at a 5% dose of G, the charge density of PCC did not deviate much from the initial values. The system carried a weak negativeharge, resulting in an unstable colloidal suspension that led to PCC-PCC particle bridging. On the other hand, the operative mechanism of CL and CH during adsorption and PCC flocculation was predicted to be charge neutralization and electrostatic-patch formation, accompanied by particle bridging. Note that CL, with a maximum 47.5% eduction in residual turbidity of PCC at a 1% dose, was much more efficient in doing so than the other two gums; NG had a 40% maximum reduction in residual turbidity at a 5% dose and CH had a maximum 30% reduction at a 1% ose. Later on, floc formation and structure were correlated with optical and field emission scanning electron microscopy (FE-SEM) images. In the next set of trials, paper properties were determined by varying the different gum dosages from 0.2% to 5% at a constant dose of 20% filler. It is also noteworthy to mention that with 1% CL (low DS) dose, PCC retention increased by 39%, which also enhanced the tensile, tear, burst, and opacity properties by 11%, 19%, 5%, and 4.4%, respectively, without significantly affecting the bulk properties. Further, wide-angle X-ray diffraction (XRD) analysis nd Fourier transform infrared (FTIR) analysis revealed that pre-flocculating PCC with a 1% gum dose did not induce any change in crystalline transformation. Based on observation, it was found that cationic gums with low DS values re a better choice for maximizing the strength of paper while maintaining bulk and high opacity when pre-flocculaion is adopted to increase the filler retention in paper.
Journal articles
Magazine articles
The Creep Properties of Paper, TAPPI Journal August 2022
ABSTRACT: The creep proprties of alpha-pup handshetts were determined at various constant tensile loads and relative humidities for the purpose of clarifying the prerupture mechanical behavior of paper.
Journal articles
Magazine articles
Web lateral instability caused by nonuniform paper properties, TAPPI Journal January 2022
ABSTRACT: Lateral or cross-machine direction (CD) web movement in printing or converting can cause problems such as misregistration, wrinkles, breaks, and folder issues. The role of paper properties in this problem was studied by measuring lateral web positions on commercial printing presses and on a pilot-scale roll testing facility (RTF). The findings clearly showed that CD profiles of machine direction (MD) tension were a key factor in web stability. Uneven tension profiles cause the web to move towards the low-tension side. Although extremely nonuniform tension profiles are visible as bagginess, more often, tension profiles must be detected by precision devices such as the RTF. Once detected, the profiles may be analyzed to determine the cause of web offset and weaving problems.Causes of tension profiles can originate from nonuniform paper properties. For example, by means of case studies, we show that an uneven moisture profile entering the dryer section can lead to a nonuniform tension profile and lateral web movement. Time-varying changes in basis weight or stiffness may also lead to oscillations in the web’s lateral position. These problems were corrected by identifying the root cause and making appropriate changes. In addition, we developed a mathematical model of lateral stability that explains the underlying mechanisms and can be used to understand and correct causes of lateral web instability.
Journal articles
Magazine articles
Application of ATR-IR measurements to predict the deinking efficiency of UV-cured inks, TAPPI Journal January 2022
ABSTRACT: In recent years, ultraviolet (UV)-curable ink has been developed and widely used in various printing applications. However, using UV-printed products (UV prints) in recovered paper recycling causes end-product dirt specks and quality issues. A new method was developed that can distinguish UV prints from other prints by means of attenuated total reflectance infrared (ATR-IR) spectroscopy. Application of this method could allow more efficient use of UV prints as raw materials for paper recycling.First, a mill trial was performed using UV prints alone as raw materials in a deinked pulp (DIP) process. Second, test prints were made with four types of UV inks: a conventional UV ink and three different highly-sensitive UV inks. Each print sample had four levels of four-color ink coverage patterns (100%, 75%, 50%, and 25%). Next, deinkability of all prints was evaluated by laboratory experiments. Finally, each print was measured using the ATR-IR method, and the relationship between the IR spectra and deinkability was investigated. Mill trial results showed that UV prints caused more than 20 times as many dirt specks as those printed with conventional oil-based ink. There were variations in recycling performance among UV prints taken from bales used for the mill trial. Lab tests clearly revealed that not all UV-printed products lead to dirt specks. In order to clarify the factors that affected deinkability of UV prints, the print samples were investigated by lab experiments. Key findings from lab experiments include: œ The number of dirt specks larger than 250 µm in diameter increased as the ink coverage increased. œ Higher ink coverage area showed stronger intensity of ATR-IR spectral bands associated with inks. These results indicate that deinkability of UV prints could be predicted by analysis of ATR-IR spectra. œ Finally, the method was applied for assessment of recovered paper from commercial printing presses. It was confirmed that this method made it possible to distinguish easily deinkable UV prints from other UV prints. Based on these findings, we concluded that the ATR-IR method is applicable for inspection of incoming recovered paper.
Journal articles
Magazine articles
Investigation of the Cellulose-Water Relationship by the Pressure Plate Method, TAPPI Journal July 2022
ABSTRACT: The swelling and water retention properties of pulp fibers are of basic importance in papermaking.
Journal articles
Magazine articles
Web instability in the open draw and the impact on paper machine efficiency, TAPPI Journal May 2022
ABSTRACT: Paper is most likely to break in the first open draw on a paper machine where it is unsupported, wettest, and weakest. Tension is applied to peel the web from the roll surface, as well as minimize web flutter in the open draw. The average tension is well below the breaking point and is often set by adjusting the speed difference between the press and the next machine element by visually observing the behavior of the web. However, machine direction variations caused by instabilities in the paper machine can cause tension swings that exceed the strength of the web. Measurement of the web’s release point from press rolls on pilot and commercial paper machines was used to identify the cause of tension instabilities. Variations in the speed of the paper machine drives and the work of adhesion from the press roll surface were identified as key factors. Fluctuations of paper moisture, which affects the elastic modulus and strength of the web, appear to be less important.