Effects of hydrodynamic shear during formation of paper sheets with the addition of nanofibrillated cellulose, cationic starch, and cationic retention aid, TAPPI Journal September 2024
ABSTRACT: Laboratory tests were conducted to evaluate effects of hydrodynamic shear levels on papermaking process variables and paper handsheet properties. The furnish was from 100% recycled copy paper, to which was added nanofibrillated cellulose (NFC) at the 5% level following its optional pretreatment with cationic starch. A cationic copolymer of acrylamide (cPAM) was used as the retention aid. Different levels of hydrodynamic shear were applied both after mixing the NFC with the cationic starch (pre-shearing) or after all the furnish components had been combined (final shearing). The presence or absence of pre-shearing was found to have little effect on the measured outcomes. By contrast, increasing final shear hurt filler retention and made the resulting paper more uniform. However, the final shear level did not have a significant effect on the tensile strength of the resulting handsheets. Medium-charge density cationic starch, used in pretreating the NFC, consistently gave greater strength in comparison to a high-charge cationic starch. The significance of these findings is that though the relatively high hydrodynamic shear levels associated with modern paper machines can have some beneficial effects, they do not necessarily overcome all challenges associated with wet-end addition of nanocellulose in combination with other additives.
Journal articles
Magazine articles
Flocculation of fiber suspensions studied by Rheo-OCT, TAPPI Journal September 2024
ABSTRACT: When dealing with papermaking fiber suspensions, particle flocculation takes place even before the paper web is formed. The particle flocculation depends on several aspects, including particle mass concentration (consistency), particle collisions, electrochemical interactions promoted by chemical additives, etc. Due to its importance, fiber suspension flocculation has been studied for a long time in papermaking, and several methods have been developed for this purpose. The traditional techniques include, for example, focused beam reflectance microscopy (FBRM) and high-speed video imaging (HSVI). Recently, a new optical method, optical coherence tomography (OCT), has emerged for flocculation analysis. The advantages of OCT are the possibility to study opaque suspensions, its micron-llevel resolution, and its high data acquisition speed. The OCT measurements can be combined with rheological (Rheo) measurements, allowing simultaneous measurement of both the time evolution of the floc size and the suspension viscosity. In this work, we used this approach, Rheo-OCT, to study the flocculation of suspensions of various papermaking furnishes. We analyzed the time evolution of the floc size and the fiber suspension viscosity when the studied papermaking suspensions were treated with highly refined furnish (HRF) — a furnish that contained a significant amount of micofibrillated cellulose (MFC)-type fibrils — and/or chemical additives. Such studies can lead to a better understanding of the impact of flocculation on the produced paper web in terms of qualities like formation, drainage potential, and strength behavior.
Journal articles
Magazine articles
Dynamic compression characteristics of fiber-reinforced shoe press belts, TAPPI Journal April 2025
ABSTRACT: Shoe press belts contribute significantly to the overall dewatering performance in the press section of a paper machine. Within the shoe press nip, the press belt faces a dynamic and multidimensional load that mainly leads to a compression of the structure. As this will cause a loss in void volume, knowledge of the dynamic compression characteristics of shoe press belts is crucial for optimized dewatering. A novel method was developed to examine the dynamic compression characteristics of grooved polyurethane press belts. Therefore, an experimental setup allowing realistic boundary conditions to test specimens was placed in a servo-hydraulic testing machine. Press belt specimens with different matrix material formulations and groove patterns were tested under varying load rates equivalent to different paper machine operational speeds. The results showed an evident sensitivity of the dynamic compression stiffness to the operational speed of the paper machine. This behavior was seen to be more sensitive to changes in the matrix material formulation than to adaptions of the groove pattern. As a result, the compression of the press belt within a shoe press nip is not only influenced by the peak pressure within the shoe press nip but also depends on the operational speed of the paper machine.
Journal articles
Magazine articles
Study on the effect of aluminum diethyl phosphinate in synergy with ammonium polyphosphate on the flame retardancy of cellulose paper, TAPPI Journal April 2025
ABSTRACT: This paper involved the synergistic incorporation of ammonium polyphosphate (APP) and diethyl aluminum phosphinate (AlPi) as flame-retardant fillers for producing flame-retardant paper. The research revealed that APPs were square particles with a smooth surface, and their solubility was 0.29 g/100 mL at 20°C, which increased to 4.12 g/100 mL at 60°C. The surfaces of AlPis were rough and irregular. The solubility of AlPi was 0.023 g/100 mL at 20°C, and the solubility remained stable when the temperature increased. The addition of AlPi had a minor influence on the pulp beating degree. The tensile strength of kraft/APP/AlPi decreased with the increase of the AlPi addition. For a paper with 20 wt% APP and 0 wt% AlPi, the limiting oxygen index (LOI) value was 27.2%, and it burned completely at the eighth second during vertical combustion. When the AlPi additive content increased to 20 wt%, its LOI value increased to 32.2%, and the vertical combustion self-extinguished as soon as the flame was removed. Scanning electron microscopy (SEM) showed that the char residue of the kraft/APP/AlPi had a more complete fiber network structure than that of kraft/APP. The Raman spectroscopy indicated that the area ratio of the D (amorphous phase; disordered graphite vibration) band to the G (crystal phase; graphite carbon vibration) band (ID/ IG) ratio of kraft/APP/AlPi was lower than that of kraft/APP, meaning that the graphitization degree of the char residue of kraft/APP/AlPi was higher than that of kraft/APP, which indicated the kraft/APP/AlPi had better flame retardancy.
Journal articles
Magazine articles
Multifunctional barrier coating systems created by multilayer curtain coating, TAPPI Journal November 2020
ABSTRACT: Functional coatings are applied to paper and paperboard substrates to provide resistance, or a barrier, against media such as oil and grease (OGR), water, water vapor as measured by moisture vapor transmission rate (MVTR), and oxygen, for applications such as food packaging, food service, and other non-food packaging. Typical functional barrier coatings can be created by applying a solid coating or extruded film, a solvent based-coating, or a water-based coating to the paper substrate using various means of coating applicators.This paper focuses on water-based barrier coatings (WBBC) for OGR, water, MVTR, and oxygen barriers. The main goal was to create coated systems that can achieve more than one barrier property using multilayer curtain coating (MLCC). Curtain coating has emerged as the premier low-impact application me thod for coated paper and paperboard. This paper provides examples using MLCC to create coating structures that provide multiple barrier properties in a single coating step. Barrier polymer systems studied include styrene butadiene, styrene acrylate, vinyl acrylic, and natural materials, as well as proprietary additives where required to give desired performance. The paper also shows how the specific coating layers can be optimized to produce the desired property profile, without concern for blocking, as the addition of a non-blocking top layer can be applied in the MLCC structure as well. Experiments on base sheet types also shows the importance of applying the multilayer structure on a pre-coated surface in order to improve coating thickness consistency and potentially allow for the reduction of more expensive layer components.
Journal articles
Magazine articles
Numerical analysis of slot die coating of nanocellulosic materials, TAPPI Journal November 2020
ABSTRACT: Nanocellulosic coatings as a food packaging material are of commercial interest due to their nontoxic nature, renewability, and excellent barrier properties. Complex shear-thinning rheology poses challenges in designing and sizing equipment to pump, mix, and process the suspension and actual coating process. This study aims to determine the effectiveness of computational fluid dynamics (CFD) in predicting nanocellulosic suspension flow in light of existing rheological data. We employ and compare three distinct rheological models to characterize the rheology and flow of nanocellulose suspensions through a slot die coater, where the model parame-ters are established from existing slot rheometry measurements. A volume-of-fluid (VoF) based finite volume meth-od is employed to simulate the flow in a slot die operated in an unconventional metering mode. Results with the Casson model predict the presence of unyielded regions in the flow, which was not captured using the power law model. These stagnation regions will incur coatability issues stemming from flow intermittencies and lead to poten-tial defects in the coating layer, including fracture. The results suggest that a rheological model that includes yield stress should be considered while modeling such flows. A need for better rheological data to model nanocellulosic flows, especially at high consistencies and shear rates, is also highlighted.
Journal articles
Magazine articles
The use of hollow sphere pigments as strength additives in paper and paperboard coatings—Part 1: The predictive nature of packing models on coating properties, TAPPI Journal November 2020
ABSTRACT: Hollow sphere pigments (HSPs) are widely used at low levels in coated paper to increase coating bulk and to provide gloss to the final sheet. However, HSPs also provide an ideal system through which one can examine the effect of pigment size and particle packing within a coating due to their unimodal and tunable particle sizes. The work presented in Part 1 and Part 2 of this study will discuss the use of blends of traditional inorganic pigments and HSPs in coating formulations across a variety of applications for improved coating strength. Part 1 of this study focuses on the theory of bimodal spherical packing and demonstrates the predictive nature of packing models on the properties of coating systems containing HSPs of two different sizes. This study also examines conditions where the model fails by examining the effect of particle size on coating strength in sytems like thermal paper basecoats where the non-HSP component has a broad particle size distribution, and how these surprising trends can be used to generate better-than-expected thermal printing performance in systems with low HSP/clay ratios. Part 2 of this study focuses on the incorporation of HSPs of different particle sizes into paperboard formulations to affect coating strength and opacity.
Journal articles
Magazine articles
The use of hollow sphere pigments as strength additives in paper and paperboard coatings—Part 2: Optimization in paperboard formulations for opacity and strength, TAPPI Journal November 2020
ABSTRACT: This report aims to summarize the efforts in testing the properties of coatings for paperboard utilizing hollow sphere pigments (HSPs). HSPs are known to effectively scatter light and replace titanium dioxide (TiO2) in architectural coating formulations. The effect of the particle size and void fraction was evaluated, along with many coating parameters, including level of addition, binder chemistry, and blends of two HSPs. The small HSPs that have optimized voids for scattering light showed equivalent strength to the TiO2-containing control. The strength data was surprising, particularly the improvement in strength for coatings containing large particle size HSPs. Because of this increase in strength, four parts of binder could be removed, which allowed for higher brightness while not compromising other properties, including hot melt glueability. These trends held true using different binder chemistries (styrene acrylic, vinyl acrylic, and styrene butadiene). Upon refining the formulations further, blends of two HSPs showed further benefit.
Journal articles
Magazine articles
Improving paper wet strength via increased lignin content and hot-pressing temperature, TAPPI JOURNAL October 2020
ABSTRACT: It is known that the strength properties of wood-based paper materials can be enhanced via hot-pressing techniques. Today, there is a desire not only for a change from fossil-based packaging materials to new sustainable bio-based materials, but also for more effective and eco-friendly solutions for improving the dry and wet strength of paper and board. Against this background, hot pressing of paper made from high yield pulp (HYP), rich in lignin, becomes highly interesting. This study investigated the influence of pressing temperature and native lignin content on the properties of paper produced by means of hot pressing. Kraft pulps of varied lignin content (kappa numbers: 25, 50, 80) were produced at pilot scale from the same batch by varying the cooking time. We then studied the effect of lignin content by evaluating the physical properties of Rapid Köthen sheets after hot pressing in the temperature range of 20°C•200°C with a constant nip pressure of 7 MPa. The pilot-scale cooked pulps were compared with reference samples of mill-produced northern bleached soft-wood kraft (NBSK) pulp and mill-produced chemithermomechanical pulp (CTMP).Generally, the results demonstrated that lignin content had a significant effect on both dry and wet tensile index. All of the pilot cooked pulps with increased lignin content had a higher tensile index than the reference NBSK pulp. To obtain high tensile index, both dry and wet, the pressing temperature should be set high, preferably at least 200°C; that is, well above the glass transition temperature (Tg) for lignin. Moreover, the lignin content should prefera-bly also be high. All kraft pulps investigated in this study showed a linear relationship between wet strength and lignin content.
Magazine articles
Recycling 'low value' post-consumer fibers to improve quality and reduce costs, TAPPI JOURNAL, September 1997, Vol. 80(9)
Recycling 'low value' post-consumer fibers to improve quality and reduce costs, TAPPI JOURNAL, September 1997, Vol. 80(9)