Mill experience of calcium carbonate scale formation in green liquor pipelines, TAPPI Journal August 2020
ABSTRACT: Experience of hard calcite (CaCO3) scale formation in green liquor pipelines at four kraft pulp mills was systematically investigated to determine if there is any correlation between the severity of the scaling problem at each mill and the design and operating conditions of its causticizing plant. The results show that the high degree of supersaturation of calcium ions (Ca2+) in the liquor is the main contributing factor. Mills that operate at a lower green liquor total titratable alkali (TTA), higher causticity, and a larger liquor temperature drop are more likely to produce a green liquor that is supersaturated with Ca2+, and thus experience more severe scaling problems. In order to minimize CaCO3 scaling, the green liquor handling equipment should be operated as steady as possible to avoid conditions that allow Ca2+ to be supersaturated. The strategies include minimizing variations in liquor TTA, insulating the green liquor pipelines to reduce temperature gradients, and adding lime mud to weak wash to provide seeds for precipitation to occur on mud particles instead of on metal substrate.
Magazine articles
A visit to mount st. helens; meta lake illustrates natural recovery following volcanic eruption, TAPPI JOURNAL, April 1994, Vol. 77(4)
A visit to mount st. helens; meta lake illustrates natural recovery following volcanic eruption, TAPPI JOURNAL, April 1994, Vol. 77(4)
Magazine articles
Beauty or the beast: life after iso 9000, TAPPI JOURNAL, October 1994, Vol. 77(10)
Beauty or the beast: life after iso 9000, TAPPI JOURNAL, October 1994, Vol. 77(10)
Journal articles
Magazine articles
Boiler retrofit improves efficiency and increases biomass firing rates, TAPPI Journal March 2021
ABSTRACT: Domtar’s fluff pulp mill in Plymouth, NC, USA, operates two biomass/hog fuel fired boilers (HFBs). For energy consolidation and reliability improvement, Domtar wanted to decommission the No. 1 HFB and refurbish/retrofit the No. 2 HFB. The No. 2 HFB was designed to burn pulverized coal and/or biomass on a traveling grate. The steaming capacity was 500,000 lb/h from coal and 400,000 lb/h from biomass. However, it had never sustained this design biomass steaming rate. As the sole power boiler, the No. 2 HFB would need to sustain 400,000 lb/h of biomass steam during peak loads. An extensive evaluation by a combustion and boiler technologies supplier was undertaken. The evaluation involved field testing, analysis, and computational fluid dynamics (CFD) modeling, and it identified several bottle-necks and deficiencies to achieving the No. 2 HFB’s biomass steam goal. These bottlenecks included an inadequate combustion system; insufficient heat capture; excessive combustion air temperature; inadequate sweetwater con-denser (SWC) capacity; and limited induced draft fan capacity.To address the identified deficiencies, various upgrades were engineered and implemented. These upgrades included modern pneumatic fuel distributors; a modern sidewall, interlaced overfire air (OFA) system; a new, larger economizer; modified feedwater piping to increase SWC capacity; replacement of the scrubber with a dry electrostatic precipitator; and upgraded boiler controls.With the deployment of these upgrades, the No. 2 HFB achieved the targeted biomass steaming rate of 400,000 lb/h, along with lowered stack gas and combustion air temperatures. All mandated emissions limit tests at 500,000 lb/h of steam with 400,000 lb/h of biomass steam were passed, and Domtar reports a 10% reduction in fuel firing rates, which represents significant fuel savings. In addition, the mill was able to decommission the No. 1 HFB, which has substantially lowered operating and maintenance costs.
Journal articles
Magazine articles
Tetraethyl orthosilicate-containing dispersion coating — water vapor and liquid water barrier properties, TAPPI Journal September 2021
ABSTRACT: An aqueous styrene-butadiene latex dispersion coating containing in-situ processed tetraethyl orthosilicate (TEOS) applied on paperboard demonstrated improved water barrier performance. Coatings containing TEOS equivalent to 0.8% silicon dioxide (SiO2; dry basis) exhibited water vapor performance of < 25 g/m2/day (23°C, 50% relative humidity [RH]) and liquid water barrier performance Cobb 1800 s of < 6 g/m2, when applied as a single-layer 18 g/m2 coating. Cobb 1800 s barrier performance was still good (< 11 g/m2) at coat weights of 7•10 g/m2. The use of filler materials such as kaolin improved the vapor barrier properties of the coating, but this was not critical to the liquid water barrier properties.
Journal articles
Magazine articles
Commercially relevant water vapor barrier properties of high amylose starch acetates: Fact or fiction?, TAPPI Journal September 2021
ABSTRACT: Starches have recently regained attention as ecofriendly barrier materials due to the increased demand for sustainable packaging. They are easily processable by conventional plastics processing equipment and have been utilized for oil and grease barrier applications. While starches have excellent oxygen barrier properties and decent water barrier properties at low relative humidity (RH), they are moisture sensitive, as demonstrated by the deterioration of the barrier properties at higher RH values. Starch esters are chemically modified starches where the hydroxyl group of the starch has been substituted by other moieties such as acetates. This imparts hydrophobicity to starches and has been claimed as a good way of retaining water vapor barrier properties of starches, even at high RH conditions. We studied the water vapor barrier properties of one class of starch esters, i.e., high amylose starch acetates that were assumed to have good water vapor barrier properties. Our investigations found that with a high degree of substitution of hydroxyl groups, the modified starches did indeed show improvements in water vapor response as compared to pure high amylose starch films; however, the barrier properties were orders of magnitude lower than commercially used water vapor barriers like polyethylene. Even though these materials had improved water vapor barrier response, high amylose starch acetates are likely unsuitable as water vapor barriers by themselves, as implied by previous literature studies and patents.
Journal articles
Magazine articles
A new method of studying the fundamental mechanisms involved in pigment liberation from recycle papers, TAPPI Journal October 2022
ABSTRACT: Deinking flotation is the most efficient and widely used method of removing ink particles from printed papers to improve the recyclability. A prerequisite for successful deinking flotation is detachment of pigments from paper fibers, a subprocess known as liberation. The degree of liberation is usually determined via hyperwashing tests, which are costly and time consuming. Furthermore, they provide no information on the fundamental mechanisms controlling liberation. In the present work, we developed a new method in which ?-potentials of the particles in a pulp are measured and analyzed. If pigments are not liberated from paper fibers, a frequency distribution plot gives a single peak, while two peaks appear when they are liberated. One can readily determine the degrees of liberation from the peak positions and peak heights. In addition, the ?-potential data can be used to construct disjoining pressure isotherms using the DLVO theory that are useful to better understand the fundamental mechanisms involved and the roles of different reagents used to improve pigment liberation.
Journal articles
Magazine articles
Fate of phosphorus in the recovery cycle of the kraft pulping process, TAPPI Journal March 2020
ABSTRACT: The accumulation of nonprocess elements in the recovery cycle is a common problem for kraft pulp mills trying to reduce their water closure or to utilize biofuels in their lime kiln. Nonprocess elements such as magnesium (Mg), manganese (Mn), silicon (Si), aluminum (Al), and phosphorus (P) enter the recovery cycle via wood, make-up chemicals, lime rock, biofuels, and process water. The main purge point for these elements is green liquor dregs and lime mud. If not purged, these elements can cause operational problems for the mill. Phosphorus reacts with calcium oxide (CaO) in the lime during slaking; as a result, part of the lime is unavailable for slaking reactions. The first part of this project, through laboratory work, identified rhenanite (NaCa(PO4)) as the form of P in the lime cycle and showed the negative effect of P on the availability of the lime. The second part of this project involved field studies and performing a mass balance for P at a Canadian kraft pulp mill.
Journal articles
Magazine articles
How do mud balls form in lime kilns?, TAPPI Journal April 2023
ABSTRACT: Mud ball formation in lime kilns has been a persistent problem in many kraft mills, particularly for older kilns that are equipped with chains. A systematic laboratory study was conducted to examine how mud balls are formed and the key factors that affect ball formation. The results confirm the general mill experience that high moisture and high sodium contents in lime mud are the main contributing factors to ball formation. The high moisture content allows lime mud to agglomerate and grow to form balls, while the high sodium content helps make the balls hard and retain their shape. A ball formation mechanism is proposed to explain how mud balls form and grow near the kiln feed end.
Journal articles
Magazine articles
Advantages of lean duplex stainless steels in the pulp and paper industry, TAPPI Journal April 2023
ABSTRACT: The performance of lean duplex stainless steels has been utilized by the pulp and paper industry since their introduction to the market almost 20 years ago. Experience has shown that this group of stainless steels has exceptional performance in, for example, alkaline environments towards typical deterioration mechanisms, i.e., uniform corrosion and stress corrosion cracking. The chemistry of the “lean” duplex steels is designed so that the content of volatile and expensive elements like nickel and molybdenum can be reduced to an absolute minimum without sacrificing the technical performance. This reduces the raw material cost and most importantly provides predictability of the steel price, which is often challenging with conventional austenitic and duplex stainless steels.Thanks to a dual phase microstructure and high nitrogen content, lean duplex steels have at least two times higher strength compared to standard austenitic stainless steels. This is often a preferred feature in pulp and paper construction, as it enables lighter structures and less material to be utilized. Today, lean duplex steels are widely available in various dimensions, from thin cold rolled sheets up to thick hot rolled plates. Lean duplex steels are also fully recyclable after the decommissioning stage of the equipment, thereby contributing to the circular economy.