Measurement and control of extensional viscosity in barrier coating dispersions, TAPPI Journal November 2023

ABSTRACT: This study aimed to understand the effect of various rheological additives on the extensional viscosity of barrier coating dispersions, as well as to understand the role extensional viscosity plays in stabilizing a liquid curtain. The apparent extensional viscosity was measured using two devices that create accelerating flows: a capillary viscometer and an orifice rheometer. Additives tested include several polyvinyl alcohols, a high molecular weight polyethylene oxide, and carboxymethylcellulose. Extensional viscosity plays a significant role in stabilizing a liquid curtain, as it slows down hole expansion and prevents impurities and disturbances from causing holes in the first place. Some of the additives could substantially increase the extensional viscosity of the dispersions without increasing the shear viscosity outside the typical range of processability for a curtain coater. Some of the additives exhibited coil-stretch transition, meaning they start increasing extensional viscosity above a certain extension rate. Polymers with low chain lengths exhibited finite extensibility, which indicates the polymer chain has fully extended and cannot provide further extensional viscosity, even though the extending force is increased. Polymeric additives with stiff or branched chains significantly raised shear viscosity without increasing extensional viscosity. Both methods could reliably measure extensional viscosity in curtain coating barrier dispersions.

Multifunctional barrier coating systems created by multilayer curtain coating, TAPPI Journal November 2023

ABSTRACT: Functional coatings are applied to paper and paperboard substrates to provide resistance, or a barrier, against media such as oil and grease, water, water vapor, and oxygen, for applications such as food packaging, food service, and other non-food packaging. Today, there is increasing interest in developing recyclable and more sustainable approaches for producing these types of packages. This paper focuses on water-based barrier coatings (WBBC) for oil and grease resistance (OGR), water, moisture vapor transmission rate (MVTR), and oxygen barrier performance. The main goal is to create coated systems that can achieve more than one barrier property using multilayer curtain coating (MLCC) in a single application step. One advantage is in optimizing coating material cost with the use of functional chemistry in confined layers where performance is balanced within the coating layered structure. This allows simultaneous application of layers of different polymer types in one step to achieve the appropriate performance needs for a given barrier application. This paper provides working examples of using MLCC to create coating structures with multiple barrier properties in a single application pass. Barrier polymers studied include styrene butadiene, styrene acrylate, starch-containing emulsions, and polyvinyl alcohol. The paper also shows the effect of increasing the pigment volume concentration with platy clay or fine ground calcium carbonate on MVTR and OGR barrier properties.

Surface energy considerations for offset printing of coated paper and paperboard, TAPPI Journal November 2023

ABSTRACT: Offset printing of coated paper involves the complex interactions of ink with a surface that is characterized by three major properties: roughness, porosity, and related pore network structure and surface chemistry (related to surface free energy [SFE]). The effects of porosity and roughness are relatively well understood and are documented in the literature, whereas the influence of surface chemistry is much less studied and therefore the focus of this paper. The key results shown include: i) Coating porosity has a negligible effect on SFE determination by contact angle using two fluids. ii) The chemistry of the latex polymer in the coating formulation dominates the influence on SFE compared to pigment, with any surface energy differences present in the pigment being almost completely masked by latex. iii) Wetting agent and corona treatment can impact water absorption rate and surface spreading of water, resulting in small differences in printability. Increasing the concentration of the surfactant on a coated surface indicates switching orientation of the surfactant molecules, giving a “step wise” printing result. When looking to improve offset printability by selection of different pigments, the variation in SFE is less important than variation in either surface roughness or porosity.

Paper Chemistry for New Markets: An Overview, November/December 2023 Paper360º

Paper Chemistry for New Markets: Vendor Perspective, November/December 2023 Paper360º

Want to be Successful? Implement Systems and Seize Opportunities, November/December 2023 Paper360º

Over the Wire, Paper360º September/October 2023

TAPPI Journal Summaries, Paper360º September/October 2023

TAPPI Journal Summaries, Paper360º September/October 2023

Characterizing rheological behavior and fluidization of highly refined furnishes, TAPPI Journal April 2024

ABSTRACT: In this work, highly refined softwood bleached kraft pulp (SWBKP) furnishes, referred to here as XFC, were studied from the perspective of fiber suspension handling in processing. The rheology of the furnishes was studied with a rotational rheometer using a non-standard flow geometry to understand the viscosity development at different consistencies and the impact of temperature. For fluidization analysis during pipe flow, two optical methods were implemented; namely, optical coherence tomography (OCT) and high-speed video (HSV) imaging. The OCT was used to determine the small-scale floc structures near the pipe wall where the shear stress is highest, and the HSV imaging was applied for observing flow instabilities and XFC suspension uniformity at the pipe scale. All these issues can be significant in deciding the minimum flow rate required for a process pipe to get sufficient fluidization of XFC suspensions.

Effect of pressure and time on water absorption of coated paperboard based on a modified Cobb test method, TAPPI Journal April 2024

ABSTRACT: This manuscript presents the study of water absorption by paperboard subjected to water at high hydrostatic pressure based on a modified Cobb tester. The new tester is based on TAPPI Standard Test Method T 441; however, the water column can reach up to 550 mm. The evaluation consisted of measurements of water absorption for coated and uncoated paperboard at different exposure times from 5 s to 45 s and water column heights from 10 mm to 500 mm (corresponding to hydrostatic pressures 98 Pa and 4.9 kPa, respectively). The coatings were formulated as a combination of styrene acrylate (SA; two binder levels) and two types of ground calcium carbonates (differing particle sizes) to form the two pre-coating structures: open and closed. The coating weight was 6 g/m2 applied on 210 g/m2 solid bleached board (SBB). In addition, 210 g/m2 uncoated boards were studied. Characterization of the coatings was performed with scanning electron microscopy (SEM), mercury intrusion, and roughness. It was found that the new device properly mimics the conditions of the current Cobb tester. The characterization of the coating also confirmed the presence of more open/larger pores of open coatings, confirming the desired coating structure. The absorption of boards was mainly driven by exposure pressure by comparing with exposure time. This was already evident after shorter periods of exposure time at 5 s and also 15 s exposure time. Paperboards with open coatings showed slightly higher absorption than other boards.