Effects of phosphogypsum whiskers modification with calcium stearate and their impacts on properties of bleached softwood paper sheets, TAPPI Journal September 2021
ABSTRACT: By combining the structural properties and characteristics of phosphogypsum whiskers, a preliminary study on the modification of phosphogypsum whiskers and their application in papermaking was carried out. The effects of reaction temperature, reaction time, and reaction concentration on the solubility and retention of modified phosphogypsum whiskers and the effects of phosphogypsum whiskers on the physical properties of paper under different modified conditions were explored. The research results show that, after the phosphogypsum whiskers are modified with calcium stearate, a coating layer will be formed on the surface of the whiskers, which effectively reduces the solubility of the phosphogypsum whiskers. The best modification conditions are: the amount of calcium stearate relative to the absolute dry mass of the phosphogypsum whisker is 2.00%; the modification time is 30 min, and the modification temperature is 60°C. The use of modified phosphogypsum whiskers for paper filling will slightly reduce the whiteness, folding resistance, burst resistance, and tensile strength of the paper, but the tearing degree and retention of the filler will be increased to some extent.
Journal articles
Magazine articles
Discrete element method to predict coating failure mechanisms, TAPPI JOURNAL January 2018
Discrete element method to predict coating failure mechanisms, TAPPI JOURNAL January 2018
Journal articles
Magazine articles
Quantification of vegetable oil in recycled paper, TAPPI JOURNAL September 2020
ABSTRACT: Vegetable soybean oil is commonly used in cooking foods that are packaged in takeaway paper-board containers. Vegetable oil is hydrophobic, and in sufficiently high concentration, could interfere with interfiber bonding and result in paper strength loss. In order to quantify the effect of oil on the resulting paperboard strength, it is necessary to quantify the oil content in paper. A lab method was evaluated to determine the soybean oil content in paper. Handsheets were made with pulps previously treated with different proportions of vegetable oil. Pyrolysis gas chromatography-mass spectrometry (pyGCMS) was used to quantify the amount of oil left in the handsheets. The results revealed a strong correlation between the amount of oil applied to the initial pulp and the amount of oil left in the handsheets.In addition, the effect of vegetable oils on paper strength may be affected by the cooking process. Vegetable oil is known to degrade over time in the presence of oxygen, light, and temperature. The vegetable oil was put in an oven to imitate the oil lifecycle during a typical pizza cooking process. The cooked oil was then left at room temperature and not protected from air (oxygen) or from normal daylight. The heated, then cooled, oil was stored over a period of 13 weeks. During this time, samples of the aged oil were tested as part of a time-based degradation study of the cooked and cooled oil.
Journal articles
Magazine articles
Chemical addition to wet webs using foam application, TAPPI Journal January 2023
ABSTRACT: In papermaking, the conventional way to add chemicals to the web is to dose them into the fiber stock and form the paper afterwards. However, in many cases, adding chemicals directly to the stock is challenging. For example, strength aids tend to increase flocculation in the stock, which limits the addition amounts of those aids. The need for better performance of paper (and paperboard) products has given rise to the need for functionalization of paper. Adding such functional chemicals to the stock is usually rather inefficient. Hence, novel methods are needed to add chemicals to the paper bulk. One such method is dosing chemicals to the wet web via foam application. In this study, we built a laboratory-scale sheetfed dynamic foam application device and utilized it to study addition of starch to wet bleached chemithermomechanical pulp (BCTMP) paper handsheets. The impact of parameters such as vacuum level, the amount of added chemical, and the viscosity of the foaming liquid on the penetration of starch into the wet web was explored. Starch penetration into wet webs was measured via iodine-potassium iodide staining, followed by image analysis. According to our results, controlling the viscosity of the foaming liquid gives the best possibility to control the penetration.
Journal articles
Magazine articles
Dielectric spectroscopic studies of biological material evolution and application to paper, TAPPI JOURNAL September 2018
Dielectric spectroscopic studies of biological material evolution and application to paper, TAPPI JOURNAL September 2018
Journal articles
Magazine articles
Progress in foam forming technology, TAPPI JOURNAL August 2019
ABSTRACT: This paper summarizes recent developments in foam forming that were mainly carried out in pilot scale. In addition to improving the efficiency of existing processes and allowing better uniformity in material, a wide variety of raw materials can be utilized in foam forming. The focus of this paper is thin webs—papers, boards and foam-laid nonwovens, along with the pilot scale results obtained at VTT in Finland. For paper and board grades, the most direct advantage of foam forming is the potential to produce very uniform webs from longer and coarser fibers and obtain material savings through that. Another main point is increased solids content after a wet press, which may lead to significant energy savings in thermal drying. Finally, the potential to introduce “difficult” raw materials like long synthetic or manmade fibers into a papermaking process enables the manufacturing of novel products in an existing production line. This paper also briefly discusses other interesting foam-based applications, including insulation and absorbing materials, foam-laid nonwovens, and materials for replacing plastics.
Journal articles
Magazine articles
Effects of different ammonium lignosulfonate contents on the crystallization, rheological behaviors, and thermal and mechanical properties of ethylene propylene diene monomer/polypropylene/ammonium lignosulfonate composites, TAPPI Journal January 2020
ABSTRACT: Thermoplastic elastomer (TPE), made from ethylene propylene diene monomer (EPDM) and polypropylene (PP) based on reactive blending, has an excellent processing performance and characteristics and a wide range of applications. However, there are currently no reports in the literature regarding the usage of TPE in making composite boards. In this paper, EPDM, PP, and ammonium lignosulfonate (AL) were used as the raw materials, polyethylene wax was used as the plasticizer, and a dicumyl peroxide vulcanization system with dynamic vulcanization was used to make a new kind of composite material. This research studied the influences of the AL contents on the crystallization behaviors, rheological properties, thermal properties, and mechanical properties of the composites. The results showed that the AL content had a noticeable impact on the performance of the composite board. Accordingly, this kind of composite material can be used as an elastomer material for the core layer of laminated flooring.
Journal articles
A laboratory-scale automated vacuum-assisted device for coating of cellulose nanofibrils onto paper, TAPPI Journal November 2025
ABSTRACT: An automated vacuum-assisted coating system was developed to deposit cellulose nanofibril (CNF) layers onto paper substrates, simulating potential industrial geometries while allowing precise control of web speed (10•20 m/min), vacuum time (up to 30 s), and applicator gap (0.5•0.9 mm). Vacuum assistance makes it possible to obtain coat weights over 5 g/m2 in a single pass and increases solids after coating from less than 10% to over 28%• 30%, reducing drying demand by more than 60%. Coat weights were tuned from 6 to over 11 g/m² by varying suspension solids (0.4•0.6 wt%), line speed, and filtration length (20•40 mm), with strong agreement between experimental data and model predictions. Barrier testing showed Kit test values for double folded samples of 9•12 and Gurley air resistances above 4 × 104 s once coat weights exceeded 7 g/m². Comparable performance was achieved with lower fines content CNF (60%) by increasing coat weight, providing technical flexibility and cost advantages for industrial scale-up.
Journal articles
Magazine articles
Editorial: New coating grades require new tests: Barrier performance inside the package, TAPPI Journal November 2024
The TAPPI Journal special Coating issue is an annual issue that focuses on paper coating and coated papers. It is drawn from presentations at TAPPICon and from other submissions on the topic of paper coating. The TAPPICon 2024 Coating track was rich in high-quality technical content. In fact, the papers were of such significance that Coating members of the TAPPI Journal Editorial Board, which include me, Gregg Reed, and Gregory Welsch, decided that a second paper coating-related special issue would be appropriate for the TAPPI Journal editorial calendar. In addition to the current issue on Barrier Coating Testing, there will be another issue on Coating Fundamentals in early 2025.
Journal articles
Magazine articles
Test method and coating composition impact on measured moisture vapor transmission rate for waterborne coatings on paper, TAPPI Journal November 2024
ABSTRACT: Moisture vapor barrier is one of the necessary performance attributes for paper packages. Two methods are typically employed to assess the moisture vapor transmission rate (MVTR): the gravimetric cup method (ASTM E96) and the MOCON method (ASTM F1249). While those tests have been compared for free standing polymeric films, less is understood about their application in coated paper. Our results show that, despite a general agreement between the two methods, discrepancies exist where test protocols and material properties of coated paper impact the MVTR measurement. The measurement discrepancies can be explained by differences in local moisture concentration. Our study provides new insights on moisture vapor barrier assessment of waterborne coatings on paper and implications for achieving paper packages with improved barrier performance.