Research on flame-retardant paper prepared by the method of in-pulp addition of ammonium polyphosphate, TAPPI Journal May 2023
ABSTRACT: At present, the production of flame-retardant paper usually uses the impregnation method of phosphorus-nitrogen flame retardants in paper. There are few reports on the application of an in-pulp addition method. In this paper, the solubility of ammonium polyphosphate (APP) and its effect on flame-retardant paper were investigated for use in an in-pulp addition method. It was found that APP particles were square, with an average particle size of 21.88 µm. The particle size decreased significantly after immersion in water at 25°C for 24 h. Furthermore, most of the APPs were dissolved after immersion in water at 90°C for 0.5 h, and the residuals agglomerated and their shape turned into an amorphous form. The APP possessed strong electronegativity and could partially ionize in water. The solubility of APP was 0.18 g/100 mL water at 25°C and increased quickly when the temperature was higher than 30°C. Therefore, APP should be added to the pulp at temperatures below 30°C. The tensile strength of the paper initially increased with the addition of APP, and it reached the maximum value when the APP content was 10% and then gradually decreased. The limiting oxygen index (LOI) value of the paper was 28.7% when the added amount of APP was 30% and cationic polyacrylamide (CPAM) was 0.08%, reaching the flame-retardant level.
Journal articles
Magazine articles
A case study review of wood ash land application programs in North America, TAPPI Journal February 2021
ABSTRACT: Several regulatory agencies and universities have published guidelines addressing the use of wood ash as liming material for agricultural land and as a soil amendment and fertilizer. This paper summarizes the experiences collected from several forest products facility-sponsored agricultural application programs across North America. These case studies are characterized in terms of the quality of the wood ash involved in the agricultural application, approval requirements, recommended management practices, agricultural benefits of wood ash, and challenges confronted by ash generators and farmers during storage, handling, and land application of wood ash.Reported benefits associated with land-applying wood ash include increasing the pH of acidic soils, improving soil quality, and increasing crop yields. Farmers apply wood ash on their land because in addition to its liming value, it has been shown to effectively fertilize the soil while maintaining soil pH at a level that is optimal for plant growth. Given the content of calcium, potassium, and magnesium that wood ash supplies to the soil, wood ash also improves soil tilth. Wood ash has also proven to be a cost-effective alternative to agricultural lime, especially in rural areas where access to commercial agricultural lime is limited. Some of the challenges identified in the review of case studies include lengthy application approvals in some jurisdictions; weather-related issues associated with delivery, storage, and application of wood ash; maintaining consistent ash quality; inaccurate assessment of required ash testing; potential increased equipment maintenance; and misconceptions on the part of some farmers and government agencies regarding the effect and efficacy of wood ash on soil quality and crop productivity.
Journal articles
Magazine articles
Print quality of flexographic printed paperboard related to coating composition and structure, TAPPI Journal January 2018
Print quality of flexographic printed paperboard related to coating composition and structure, TAPPI Journal January 2018
Journal articles
Magazine articles
Three-dimensional visualization and characterization of paper machine felts and their relationship to their properties and dewatering performance, TAPPI Journal July 2021
ABSTRACT: Polymeric felts are commonly used in the papermaking process on the paper machine wet end, in the press section, and in the dryer section. They provide an important function during paper manufacturing, including as a carrier or support; as a filter media assisting with water removal on the paper machine; in retention of fibers, fines, and fillers; and in some applications, such as tissue and towel, to impart key structural features to the web. These felts can have highly interwoven complex internal structures comprised of machine direction and cross-machine direction yarns of varying sizes and chemical compositions. Here, we present a non-intrusive three-dimensional (3D) image visualization method using advanced X-ray computed tomography (XRCT). This method was used to characterize the complex 3D felt structure and determine the water removal characteristics of some commonly used paper machine felts. The structural features analyzed include porosity; specific pore-yarn interfacial surface area; 3D pore size distribution; 3D fiber or yarn-size distribution; and their variations through the thickness direction. The top, middle, and bottom layers of the felt have very different structures to assist with water removal and impart paper properties. The size distribution of the yarns, as well as the pores in the different layers of the felt, are also inherently different. These structural features were non-intrusively quantified. In addition, variation in the structural characteristics through the thickness of the felts and its potential role in papermaking is explored. In addition to the 3D structural characteristics, permeability characteristics and water removal characteristics, including rewetting of select felt samples, have also been experimentally determined. It is interesting to observe the relationship between key structural features and permeability and water removal characteristics. These relationships can provide additional insights into press felt design, as well as ways to improve product properties and the dewatering efficiency and productivity of the paper machine.
Journal articles
Magazine articles
Techno-economic analysis of hydrothermal carbonization of pulp mill biosludge, TAPPI Journal March 2023
ABSTRACT: For many mills, the biosludge from wastewater treatment is difficult to recycle or dispose of. This makes it a challenging side stream and an important issue for chemical pulping. It often ends up being burned in the recovery or biomass boiler, although the moisture and non-process element (NPE) contents make it a problematic fuel. Biosludge has proven resistant to attempts to reduce its moisture. When incinerated in the biomass boiler, the heat from dry matter combustion is often insufficient to yield positive net heat. Mixing the sludge with black liquor in the evaporator plant for incineration in the recovery boiler is more energy efficient, but is still an additional load on the evaporator plant, as well as introducing NPEs to the liquor. In this study, treating the biosludge by hydrother-mal carbonization (HTC), a mild thermochemical conversion technology, is investigated. The HTC process has some notable advantages for biosludge treatment; taking place in water, it is well suited for sludge, and the hydrochar product is much easier to dewater than untreated sludge. In this study, two HTC plant designs are simulated using IPSEpro process simulation software, followed by economic analysis. Low temperature levels are used to minimize investment costs and steam consumption. The results show that if the sludge is incinerated in a biomass boiler, payback periods could be short at likely electricity prices. The HTC treatment before mixing the sludge with black liquor in the evaporator plant is profitable only if the freed evaporator capacity can be used to increase the firing liquor dry solids content.
Journal articles
Reinforcing folding boxboard ply stock with refined pulp and its effect on dewatering potential, TAPPI Journal February 2025
ABSTRACT: The folding boxboard (FBB) filler ply typically contains a significant amount of mechanical pulp such as bleached thermomechanical pulp (BTMP), bleached chemi-thermomechanical pulp (BCTMP), and chemi-thermomechanical pulp (CTMP), etc. It is usually reinforced with either refined broke from the same paper machine line and converting process or by utilizing traditional bleached kraft pulp (BKP). In response to the drive for improved/increased ply bond (to avoid undesired delamination), increased bulk, reduced basis weight, and minimized energy consumption, papermakers have experimented with various options and strategies. In between the common approaches, choices have been made between reducing the refining of the mechanical pulp, increasing the broke refining (more frequently practiced on the production scale), or increasing the BKP refining (a potentially superior choice). This study focused on a simplified approach to assess the impact of three reinforcement pulps with different refining levels on the dewatering of the filler ply. The reinforcement pulp was added to the core stock for the FBB filler ply — a mechanical pulp, BCTMP, with a drainability of 25 °SR. The proportions of the reinforcement pulp, hardwood bleached kraft pulp (HWBKP), were 20% of 30-35 °SR, 10% of HWBKP 50-55 °SR, and 5% of HWBKP 70-75 °SR. The intention behind using varying percentages of reinforcement pulp was to attain a controlled internal bond while enhancing bulk through increased mechanical pulp content. The dewatering potential of the stock mixtures was assessed at three vacuum levels — 4, 10, and 25 kPa — that can be found in progressive stages within production- scale forming sections. Our goal was to find an optimal reinforcement strategy for filler ply that would minimize the use of the reinforcement pulp, give better strength, retain bulk, and lower basis weight. The success of this strategy was verified with an actual FBB machine.
Journal articles
Pilot-made, highly extensible paper for dry 3D forming, TAPPI Journal May 2025
Cellulose fiber-based packaging materials must perform well in demanding three dimensional (3D) forming process conditions. On the other hand, the development of manufacturing concepts is required for improved competitiveness of bio-based materials. This study covers some key factors that influence the extensibility of cellulose fiber-based structures and presents a pilot-scale development study of a 3D formable material concept. Bleached softwood kraft (BSK) pulp from a Nordic pulp mill was used in the pilot trials. Cellulose-based webs were formed using water-laid and foam-laid web forming using a pilot paper machine. For the water-laid forming, the BSK pulp was refined by applying a high consistency (HC) phase at over 40% consistency, followed by a low consistency (LC) refining at 4% consistency. The BSK pulp was refined for the foam-laid forming by only applying lowconsistency refining. In the foam-laid web forming, anionic sodium dodecyl sulfate (SDS), two foamable latexes, and polyvinyl alcohol (PVA) were used as foaming agents. The pilot rolls were dried at a separate steam cylinder dryer pilot and compacted in-plane in the machine direction (MD) at a separate pilot machine. Tensile properties of the treated paper webs were measured and evaluated with respect to achieved web shrinkage. The same dimensional contraction brought by shrinkage was almost strained out in tensile testing. The results indicated that the shrinkage that occurred by drying and in-plane compaction depended on the pulp furnish. The water-laid material achieved about 30% elongation, whereas the foam-laid material achieved significantly above 50% elongation. The 3D forming performance of the dry materials was tested using fixed and sliding blank methods. The dry paper sheets performed well enough in 3D forming for application to many consumer package applications according to their extensibility.
Journal articles
Magazine articles
Multifunctional barrier coating systems created by multilayer curtain coating, TAPPI Journal November 2020
ABSTRACT: Functional coatings are applied to paper and paperboard substrates to provide resistance, or a barrier, against media such as oil and grease (OGR), water, water vapor as measured by moisture vapor transmission rate (MVTR), and oxygen, for applications such as food packaging, food service, and other non-food packaging. Typical functional barrier coatings can be created by applying a solid coating or extruded film, a solvent based-coating, or a water-based coating to the paper substrate using various means of coating applicators.This paper focuses on water-based barrier coatings (WBBC) for OGR, water, MVTR, and oxygen barriers. The main goal was to create coated systems that can achieve more than one barrier property using multilayer curtain coating (MLCC). Curtain coating has emerged as the premier low-impact application me thod for coated paper and paperboard. This paper provides examples using MLCC to create coating structures that provide multiple barrier properties in a single coating step. Barrier polymer systems studied include styrene butadiene, styrene acrylate, vinyl acrylic, and natural materials, as well as proprietary additives where required to give desired performance. The paper also shows how the specific coating layers can be optimized to produce the desired property profile, without concern for blocking, as the addition of a non-blocking top layer can be applied in the MLCC structure as well. Experiments on base sheet types also shows the importance of applying the multilayer structure on a pre-coated surface in order to improve coating thickness consistency and potentially allow for the reduction of more expensive layer components.
Journal articles
Magazine articles
The use of hollow sphere pigments as strength additives in paper and paperboard coatings—Part 1: The predictive nature of packing models on coating properties, TAPPI Journal November 2020
ABSTRACT: Hollow sphere pigments (HSPs) are widely used at low levels in coated paper to increase coating bulk and to provide gloss to the final sheet. However, HSPs also provide an ideal system through which one can examine the effect of pigment size and particle packing within a coating due to their unimodal and tunable particle sizes. The work presented in Part 1 and Part 2 of this study will discuss the use of blends of traditional inorganic pigments and HSPs in coating formulations across a variety of applications for improved coating strength. Part 1 of this study focuses on the theory of bimodal spherical packing and demonstrates the predictive nature of packing models on the properties of coating systems containing HSPs of two different sizes. This study also examines conditions where the model fails by examining the effect of particle size on coating strength in sytems like thermal paper basecoats where the non-HSP component has a broad particle size distribution, and how these surprising trends can be used to generate better-than-expected thermal printing performance in systems with low HSP/clay ratios. Part 2 of this study focuses on the incorporation of HSPs of different particle sizes into paperboard formulations to affect coating strength and opacity.
Journal articles
Magazine articles
Z-directional testing of paperboard in combined tensile and compression loading, TAPPI Journal May 2024
ABSTRACT: The out-of-plane properties of paperboard are important in several converting applications such as printing, sealing, creasing, and calendering. A juxtaposed tensile and compression curve in the z direction (ZD) will, however, appear to have a kink or discontinuity at 0 stress. The purpose of the present work is to capture the continuous transition between tension and compression and to increase the understanding of the complex ZD properties of paperboard by cyclic testing. In this attempt to unify the ZD tensile and compressive behavior of paperboard, samples were laminated to the testing platens using heat seal laminate film. The method for adhering the samples was compared to samples that were laminated and glued to the testing platens. The edge effects of the cutting method were evaluated in compression testing with samples not attached to the testing platens. The flat slope seen in the initial part of the pure compression curve disappeared when the samples were laminated to the testing platens. The flat slope was instead replaced by a continuous response in the transition across 0 N. The stiffness in the transition region resembled the response in tensile testing. When the testing is cycled, the material exhibits a history dependence. Starting the cycle in either compression or tensile will show an effect on the stiffness at the transition, as well as the compressive stiffness. However, the ultimate tensile strength is unaffected.