Colloid chemical aspects of paper formation in the presence of nanofibrillated cellulose and cationic starch, TAPPI Journal September 2024
ABSTRACT: A series of experimental tests were carried out to examine colloidal-scale consequences of optionally treating nanofibrillated cellulose (NFC) with cationic starches of different charge density and dosage (0.5% or 2.0% by weight), adding that material to a furnish prepared from 100% recycled copy paper, and then subjecting the mixture to very different levels of hydrodynamic shear. Tests included optical microscopy, sediment volume tests, sediment velocity tests, and “percent fines” assessment by means of a fiber quality analyzer (FQA). In addition, the zeta potential and charge demand of the studied materials were evaluated. Optical imaging revealed that cationic starch treatment of the NFC tended to agglomerate it into multiparticle clusters, which sometimes could be mostly redispersed by hydrodynamic shear. Subsequent addition of the starch-treated NFC to the default furnish resulted in much of the colloidal material becoming attached to fibers. Subsequent shearing of the mixtures was at least partly effective in separating the clusters of NFC from the fiber surface, resulting in essentially a two-component mixture. Multiparticle NFC clusters coexisted with the fiber suspension, sometimes attached and sometimes not, depending on the details of treatments. Sediment volume tests showed that systems containing cationic starch-treated NFC tended to have a higher density after settling in comparison to untreated NFC; these findings are consistent with the cationic starch acting as a stabilizer on the solid surfaces, allowing them to slide past each other during the settling process. Application of intense hydrodynamic shear tended to result in denser sediment. Results of tests with the sediment velocity messurement and the FQA percent fines assessment did not correlate well with changes in test conditions considered in this study.
Journal articles
Magazine articles
Stiffness and strength properties of five paperboards and their moisture dependency, TAPPI Journal February 2020
ABSTRACT: Five commercial multiply folding boxboards made on the same paperboard machine have been analyzed. The paperboards were from the same product series but had different grammage (235, 255, 270, 315, 340 g/m2) and different bending stiffness. The paperboards are normally used to make packages, and because the bending stiffness and grammage varies, the performance of the packages will differ. Finite element simulations can be used to predict these differences, but for this to occur, the stiffness and strength properties need to be deter-mined. For efficient determination of the three-dimensional properties in the machine direction (MD), cross direction (CD), and Z direction (ZD), it is proposed that the paperboard should be characterized using in-plane tension, ZD-tension, shear strength profiles, and two-point bending. The proposed setups have been used to determine stiff-ness and strength properties at different relative humidity (20,% 50%, 70%, and 90% RH), and the mechanical proper-ties have been evaluated as a function of moisture ratio.There was a linear relation between mechanical properties and moisture ratio for each paperboard. When the data was normalized with respect to the standard climate (50% RH) and plotted as a function of moisture ratio, it was shown that the normalized mechanical properties for all paperboards coincided along one single line and could therefore be expressed as a linear function of moisture ratio and two constants.Consequently, it is possible to obtain the mechanical properties of a paperboard by knowing the structural properties for the preferred level of RH and the mechanical property for the standard climate (50% RH and 23°C).
Journal articles
Magazine articles
Numerical investigation of the effect of ultrasound on paper drying, TAPPI Journal March 2022
ABSTRACT: The paper drying process is very energy inefficient. More than two-thirds of the total energy used in a paper machine is for drying paper. Novel drying technologies, such as ultrasound (US) drying, can be assessed numerically for developing next-generation drying technologies for the paper industry. This work numerically illustrates the impact on drying process energy efficiency of US transducers installed on a two-tiered dryer section of a paper machine. Piezoelectric transducers generate ultrasound waves, and liquid water mist can be ejected from the porous media. The drying rate of handsheet paper in the presence of direct-contact US is measured experimentally, and the resultant correlation is included in the theoretical model. The drying section of a paper machine is simulated by a theoretical drying model. In the model, three scenarios are considered. In the first scenario, the US modules are positioned in the dryer pockets, while in the second scenario, they are placed upstream of the drying section right after the press section. The third case is the combination of the first and second scenarios. The average moisture content and temperature during drying, enhancement of total mass flux leaving the paper by the US mechanism, total energy consumption, and thermal effect of heated US transducers are analyzed for all cases. Results show that the application of the US can decrease the total number of dryer drums for drying paper. This numerical study is based on the US correlation obtained with the US transducer direct-contact with the paper sample. Thus, future work should include US correlation based on a non-contact US transducer.
Journal articles
Magazine articles
Black liquor evaporators upgrade — How many effects?, TAPPI Journal April 2023
ABSTRACT: Black liquor evaporation is generally the most energy intensive unit operation in a pulp and paper manufacturing facility. The black liquor evaporators can represent a third or more of the total mill steam usage, followed by the paper machine and digester. When considering an evaporator rebuild or a new system, the key design question is how many effects to include in the system. The number of effects is the main design feature that deter-mines the economy of the system and the steam usage for a given evaporation capacity. A higher number of effects increases steam economy and reduces energy cost to a point, but additional effects also have higher initial capital cost and increased power costs. This research paper uses life-cycle cost analysis (LCCA) as a method to determine the optimum number of evaporator effects for a new evaporator system. The same basic principles and method can also apply to existing evaporator rebuild projects.
Journal articles
Magazine articles
Determining operating variables that impact internal fiber bonding using Wedge statistical analysis
ABSTRACT: In this study, Wedge statistical analysis tools were used to collect, collate, clean up, plot, and analyze several years of operational data from a commercial paper machine. The z-direction tensile (ZDT) and Scott Bond tests were chosen as representative of fiber bond strength. After analyzing thousands of operational parameters, the ones with the most significant impact upon ZDT involved starch application method, starch penetration, and the amount of starch applied. Scott bond was found to be significantly impacted by formation and refining. Final calendering of the paper web has also shown an impact on internal fiber bonding.
Journal articles
Magazine articles
Impact of different calendering strategies on barrier coating pickup, TAPPI Journal November 2023
ABSTRACT: Paper was pre-calendered in a pilot scale configuration with a traditional soft nip calender and a metal belt calender. All calendering strategies reduced surface roughness and permeability of the samples, but different strategies affected the surface roughness and permeability differently. The metal belt calender seemed to have a larger effect on the large-scale variations compared to the soft nip calender. Six test points from the pilot calendered papers were chosen for laboratory coating studies. Uncalendered paper was included as reference samples. The calendered samples and the reference were pre-coated with a regular pigmented coating consisting of a ground calcium carbonate (GCC) pigment and a styrene acrylate (SA) latex. Both uncoated and pre-coated substrates were barrier coated with a polyvinyl alcohol (PVOH) in one and two layers. The coating pickup was determined gravimetrically, and the barrier properties were evaluated with TAPPI Standard Test Method T 454 grease resistance test. All samples needed two PVOH coating layers to form a grease barrier. The uncalendered sheets showed the best results with one coating layer, but this was at the expense of a higher coating pickup compared to the calendered sheets. The barrier coating pickup could be reduced by a combination of high temperature metal belt calendering and pre-coating. The high temperature and long residence time in the nip enabled plasticization of the fibers. This led to an irreversible deformation, even after water application. This meant that the smoothness obtained during calendering would be less affected by water-induced roughening during the coating operation.
Journal articles
Magazine articles
Use of kaolin clay in aqueous barrier coating applications, TAPPI Journal November 2023
ABSTRACT: Paper-based packaging with barrier effect, as opposed to single use plastics, is gaining more prominence for sustainability reasons. At the same time, latex- or biopolymer-based aqueous barrier coating dispersions are increasingly being adopted as a better alternative to the traditional barrier coating materials, such as wax, surface active chemicals, and polyethylene. In this work, studies were performed to determine the influence of different kaolin clays in latex binder-based aqueous coatings on barrier properties, namely, oil and grease, water resistance, and water vapor transmission rate, by applying coatings to solid bleached sulfate (SBS) paperboard substrate in the laboratory. The aim was to explore potential benefits of using kaolin clay to replace some of the latex binder in coating and improve or maintain various types of barrier performance and blocking without negatively influencing the other performance attributes, including heat seal. The delaminated clay with the highest shape factor provided improved barrier properties over the clays of low shape factor. The ultrafine and non-delaminated clays required significantly higher coat weights to reach satisfactory barrier properties. Coatings with different latex levels indicated that a considerably high proportion of coarse delaminated clay can be incorporated to replace latex binder, while still achieving exceptional barrier properties. Furthermore, a change in binder system was found to significantly alter the barrier properties and the role that a mineral pigment can play. The results indicate that a proper selection of binder systems for each barrier property would be required while considering the clay/latex coating systems.
Journal articles
Magazine articles
Factors affecting the free shrinkage of handsheets: apparent density, fines content, water retention value, and grammage, TAPPI JOURNAL June 2018
Factors affecting the free shrinkage of handsheets: apparent density, fines content, water retention value, and grammage, TAPPI JOURNAL June 2018
Journal articles
Magazine articles
Understanding wet tear strength at varying moisture content in handsheets, TAPPI Journal January 2021
ABSTRACT: A laboratory study was conducted looking at the effects of moisture content on wet tear strength in handsheets. Three different wetting techniques were used to generate the wet tear (Elmendorf-type) data at varying moisture levels, from TAPPI standard conditions (dry) to over 60% moisture content (saturated). Unbleached hardwood and softwood fiber from full-scale kraft pulp production were used. The softwood fiber was refined using a Valley beater to reduce freeness. Handsheets were made with a blend of hardwood and softwood and with refined softwood, without the addition of wet-end chemistry. The resulting grams-force tear data obtained from the test was indexed with basis weight and plotted versus both moisture content and dryness. As moisture content levels in the handsheets increased, the wet tear strength also increased, reaching a critical maximum point. This marked a transition point on the graph where, beyond a critical moisture content level, the tear strength began to decline linearly as moisture increased. This pattern was repeated in handsheets made from a blend of hardwood and softwood and from 100% refined softwood.
Journal articles
Magazine articles
The effect of microfibrillated cellulose on the wet-web strength of paper, TAPPI Journal January 2021
ABSTRACT: The wet-web strength of paper immediately after the press section of a paper machine is a critical factor in determining machine runnability. However, it is difficult to determine at commercial scale, because the web has to be broken and production interrupted in order to obtain a sample for measurement. The use of microfibrillated cellulose (MFC) is believed to increase wet-web strength, as it has allowed filler level increases of 10% or more on many commercial paper machines. In this paper, we describe a laboratory method for estimating the effect of MFC on wet sheet strength after press-ing, as well as actual measurements of wet-web strength from a pilot paper machine trial. These experiments have demonstrated the positive effect of MFC. At solids contents in the range typically observed after pressing, sheets with MFC at fixed filler content are significantly stronger, but also wetter, than those without it. When the use of MFC is combined with a typical increase in filler content, the wet web remains slightly stronger, but also becomes drier than the reference condition. These results are compatible with the theory put forward by van de Ven that wet-web strength is mainly a result of friction between entangled fibers, and they also suggest that the presence of MFC increases this friction.